Low melting temperature flux materials for brazing applications and methods of brazing using the same
Low melting temperature flux materials for brazing applications and methods of brazing using the same are provided. A low melting temperature flux material for brazing applications includes as a majority constituent, a Cs-containing flux material, as a first minority constituent, a eutectic blend composition, and, optionally, as a second minority constituent, a mediating compound. The second minority constituent is present in the low melting temperature flux material in a lesser amount with respect to the first minority constituent.
1. A flux composition for brazing applications comprising:
a cesium (Cs)-containing flux material in an amount of from 80 mol-% to 90 mol-% of the total flux composition; and
a eutectic blend composition including sodium tetrafluoroborate and sodium fluoride, wherein the eutectic blend composition is in an amount of 7 mol-% to 13 mol-% of the total flux composition; and wherein the molar ratio of sodium tetrafluoroborate to sodium fluoride is from 88:12 to 92:8.
2. The flux composition of claim 1 , further comprising a mediating compound, wherein the mediating compound is present in the flux composition in a lesser amount with respect to the eutectic blend composition.
3. The flux composition of claim 2 , wherein the mediating compound is zinc oxide.
4. The flux composition of claim 2 , wherein the mediating compound is present in an amount of 3 mol-% to 7 mol-% of the total flux composition.
5. The use flux composition of claim 3 , wherein the flux composition is in the form of a powder or a paste.
6. The flux composition of claim 4 , wherein the mediating compound is zinc oxide.
7. A method of brazing using the flux composition according to claim 1 comprising:
providing or obtaining two metallic substrates;
providing or obtaining a brazing material;
providing or obtaining the flux composition,
applying the brazing material and the flux composition to a joint area of one of the two metallic substrates; bringing together in contact at the joint area the two metallic substrates;
heating the joint area to a temperature above a melting temperature of the brazing material and above a melting temperature of the flux composition, but below a melting temperature of the two metallic substrates; and
allowing the joint area to cool below the melting temperature of the brazing material and below the melting temperature of the flux composition.
8. The method of claim 7 , wherein the brazing material comprises an aluminum-zinc material.
9. The method of claim 8 , wherein the aluminum zinc material comprises a 98Zn/2Al material.
10. The method of claim 7 , wherein the two metallic substrates comprise an aluminum material or an aluminum alloy material.
11. The method of claim 7 , wherein the flux composition is in the form of a powder or a paste.
12. The method of claim 7 , wherein the flux composition further comprises zinc oxide as a mediating compound in an amount of 3 mol-% to 7 mol-% of the total flux composition.
13. The method of claim 12 , wherein the Cs-containing flux material comprises a cesium-aluminum-fluorine flux material.