Nylon terpolymers
A terpolymer composition is described that contains a statistical amount of 50-98 wt % of a first repeating AA-BB comonomer unit; 1-25 wt % of a second repeating AA-BB comonomer unit; and 1-25 wt % of a repeating lactam comonomer unit or 1-25 wt % of a third repeating AA-BB comonomer unit, where the terpolymer composition exhibits a high melting point similar to that of PA66 while also exhibiting a significantly reduced crystallization rate and crystallization temperature.
1. A terpolymer comprising:
50-98 wt % of a first repeating AA-BB comonomer unit selected from PA6,6;
1-25 wt % of a second repeating AA-BB comonomer unit selected from PA6,9; PA6,10; and PA6,12; and
1-25 wt % of a third repeating AA-BB comonomer unit,
wherein the first, second, and third repeating AA-BB comonomer units are all different;
wherein the terpolymer has a relative viscosity according to ASTM D789 (9.34) of 45 to 350 and a melting point greater than 215° C. and the terpolymer is of Formula (2):
wherein:
a=50-98 wt %;
b=7, 8, or 10;
c=6;
d=1-25 wt %;
e=2-16; and
f=1-25 wt %.
2. The terpolymer according to claim 1 , wherein the terpolymer has a relative viscosity according to ASTM D789 (9.34) of 70 to 230.
3. The terpolymer according to claim 1 , wherein the second repeating AA-BB comonomer unit is PA6,9.
4. The terpolymer according to claim 1 , wherein the second repeating AA-BB comonomer unit is PA6,10.
5. The terpolymer according to claim 1 , wherein the second repeating AA-BB comonomer unit is PA6,12.
6. The terpolymer according to claim 1 , wherein the third repeating AA-BB comonomer unit is PA6,I.
7. The terpolymer according to claim 1 , wherein:
a=82-87 wt %,
d=5-8% wt %, and
f=8-10 wt %; and the terpolymer has a relative viscosity according to ASTM D789 (9.34) of 70 to 230.
8. A composition comprising the terpolymer according to claim 1 , further comprising greater than 60 ppm and less than 500 ppm copper.
9. A composition comprising the terpolymer according to claim 1 , further comprising a lubricant.
10. A composition comprising the terpolymer according to claim 1 , further comprising an anti-block agent.
11. A film comprising the terpolymer according to claim 1 .
12. The film according to claim 11 , where the film is a blown film.
13. The film according to claim 12 , where the blown film is a multilayer film.
14. The multilayer film according to claim 13 , where the film comprises 3 to 10 layers.
15. The multilayer film according to claim 14 , where at least two of the 3 to 10 layers comprise non-terpolymer layers selected from the group consisting of low density polyethylene (LDPE), ethylene acrylic acid copolymer (EAA), ethylene methacrylic acid copolymer (EMAA), ethylene vinyl acetate copolymer (EVA), ethylene methacrylate copolymer (EMA), anhydride modified polyethylene (AMP), nylon (PA) and ethylene vinyl alcohol copolymer (EVOH).
16. The film according to claim 11 , where the film is a cast film.
17. The film according to claim 11 , where the film is biaxially oriented.
18. The film according to claim 17 , where the biaxially oriented film is a multilayer film.
19. The multilayer film according to claim 18 , where the film comprises 3 to 10 layers.
20. The multilayer film according to claim 19 , where at least two of the 3 to 10 layers comprise non-terpolymer layers selected from the group consisting of low density polyethylene (LDPE), ethylene acrylic acid copolymer (EAA), ethylene methacrylic acid copolymer (EMAA), ethylene vinyl acetate copolymer (EVA), ethylene methacrylate copolymer (EMA), anhydride modified polyethylene (AMP), nylon (PA) and ethylene vinyl alcohol copolymer (EVOH).