Method for manufacturing renewable film and products
A method of manufacturing a film includes forming a blend containing a renewable content starch, a renewable content mineral, and polyethylene, operating a mass flow hopper to maintain a consistent mass flow rate of the blend to a feed throat of an extruder, and operating the extruder with a screw speed and melt temperature based on the amount by weight of the starch and mineral within the blend. The melt is passed through a screen pack with a mesh rating based on the amount by weight of the starch and mineral within the blend, is passed through a die, and is cooled into a film. The film is nipped to a gauge such that the film can be formed into a bag.
1. A method of manufacturing a film comprising:
forming a blend, wherein the blend comprises: (i) a renewable content starch, (ii) a renewable content mineral comprising oolitic aragonite, and (iii) polyethylene;
operating a mass flow hopper to maintain a consistent mass flow rate of the blend to a feed throat of an extruder;
operating a screw of the extruder at a speed, wherein the speed is based on the amount by weight of (i) the renewable content starch and (ii) the renewable content mineral within the blend;
operating the extruder at a melt temperature, wherein the melt temperature is based on the amount by weight of (i) the renewable content starch and (ii) the renewable content mineral within the blend;
causing a melt of the blend to pass through a screen pack and a die, wherein the mesh rating of the screen pack is based on the amount by weight of (i) the renewable content starch and (ii) the renewable content mineral within the blend;
cooling the melt into a film after the melt passes through the die; and
nipping the film to a gauge such that the film can be formed into a bag.
2. The method of claim 1 , wherein a bag formed from the manufactured film comprises at least twenty percent renewable material content.
3. The method of claim 1 , wherein the blend comprises at least fifteen percent by weight the renewable content starch.
4. The method of claim 1 , wherein the blend comprises an odor absorber.
5. The method of claim 1 , wherein the renewable content mineral absorbs odor given off by the renewable content starch during the manufacturing process.
6. The method of claim 1 , wherein the gauge of the manufactured film is suitable for at least one of a sandwich bag, a storage bag, a freezer bag, and a waste bag.
7. The method of claim 1 , wherein the mesh rating of the screen pack is at least 80 mesh.
8. The method of claim 1 , further comprising:
forming the film into the bag;
coupling a reclosable closure element to a top portion of the bag.
9. The method of claim 1 , wherein the blend comprises glycerin, the method further comprising:
operating a vent near a die of the extruder to remove at least a portion of the glycerin that is volatilized during extrusion.
10. The method of claim 1 , wherein the gauge of the nipped film is between 0.5 and 5 mils.
11. The method of claim 1 , further comprising:
adjusting, based on a desired gauge of the film, the amount by weight of the renewable content starch within the blend.
12. The method of claim 1 , further comprising:
adjusting, based on a desired use of the film, the amount by weight of the renewable content starch within the blend.
13. The method of claim 12 , wherein the desired use of the film is at least one of a sandwich bag, a storage bag, a freezer bag, and a waste bag.
14. The method of claim 1 , further comprising:
determining, based on at least one of a desired use of the film and a desired gauge of the film, an amount by weight of the renewable content starch to be formed into the blend.
15. The method of claim 1 , wherein an amount by weight of the renewable content starch formed into the blend is greater than an amount by weight of the renewable content mineral formed into the blend.
16. The method of claim 15 , wherein a ratio of the amount of the renewable content starch to the amount of the renewable content mineral within the blend is about two to one.
17. The method of claim 1 , further comprising determining, based on at least one of a desired gauge or desired use for the manufactured film, a desired blend ratio of (i) the renewable content starch, (ii) the renewable content mineral comprising oolitic aragonite, and (iii) polyethylene.
18. The method of claim 1 , wherein the polyethylene is not renewable.
19. A method of manufacturing a film comprising:
determining a use for a manufactured film;
determining, based on the use for the manufactured film, a desired gauge for the manufactured film;
determining, based on at least one of the desired gauge and desired use for the manufactured film, a desired ratio of (i) a renewable content starch, (ii) a renewable content mineral, and (iii) polyethylene;
mixing (i) the renewable content starch, (ii) the renewable content mineral, and (iii) the polyethylene at the desired ratio to create a blend;
operating film extrusion equipment to form the manufactured film from the blend.
20. The method of claim 19 , further comprising:
determining, based on the amount by weight of (i) the renewable content starch and (ii) the renewable content mineral within the blend, a melt temperature at which to operate an extruder of the film extrusion equipment.