Multi-Layer Insulator for Thermal Run-Away Containment in Lithium-Ion Batteries
A multi-layered composite insulation material includes a first and second outer layers having one or more of para-aramid, meta-aramid, flame-retarded modacrylic, or pre-oxidized polyacrylonitrile fibers; and an inner layer disposed between the first and second outer layers having one or more of polyacrylonitrile fibers or ceramic fibers. The inner and outer layers are bonded via needle punching, thermal bonding, or stitch bonding. The outer layers further include flame-retardant rayon fibers and a woven or knit fabric having continuous high-temperature glass, silica, or ceramic filaments.
1 . A multi-layered composite insulation material, comprising:
a first and second outer layers comprising one or more of:
para-aramid, meta-aramid, flame-retarded modacrylic, or pre-oxidized polyacrylonitrile fibers; and
an inner layer disposed between the first and second outer layers comprising one or more of:
polyacrylonitrile fibers or ceramic fibers,
wherein
the inner and outer layers are bonded.
2 . The material of claim 1 , wherein
one or more of the outer layers further comprises:
flame-retardant rayon fibers.
3 . The material of claim 1 , wherein
the dielectric strength of one or more of the outer layers is greater than 50 volts per mil.
4 . The material of claim 1 , wherein one or more of the outer layers further comprises:
a woven or knit fabric comprising continuous high-temperature filaments fibers.
5 . The material of claim 1 , wherein
the first or second outer layer includes para-aramid or meta-aramid fibers of about 1.2 to 3.0 denier.
6 . The material of claim 1 , wherein
the first or second outer layer includes modacrylic fibers of about 2 to 7 denier.
7 . The material of claim 1 , wherein
the first or second outer layer includes para-aramid fibers of about 10 to 30% of the first or second outer layer by weight.
8 . The material of claim 1 , wherein
the first or second outer layer includes flame-retardant modacrylic fibers of about 0 to 40% of the total first or second outer layer by weight.
9 . The material of claim 1 , wherein
the weight of the first or second outer layer is between about 50 grams per square meter (gsm) and 240 gsm.
10 . The material of claim 1 , wherein
the thickness of the first or second outer layer is about 0.1 mm to 3.5 mm.
11 . The material of claim 1 , wherein
the weight of the inner layer is between about 200 gsm and 1000 gsm.
12 . The material of claim 1 , wherein
the thickness of the inner layer is about 0.5 mm to 7.5 mm.
13 . The material of claim 1 , wherein
the material is free of flammable materials and does not ignite when tested using SAE J369 horizontal and/or UL94 vertical burn tests.
14 . The material of claim 1 , wherein
the material is free of intumescent coatings.
15 . The material of claim 1 , wherein
the inner layer exhibits stability when exposed to open-flame temperatures of about 1200° Celsius or greater for at least ten minutes in accordance with ISO 6469.
16 . The material of claim 1 , wherein
the outer and inner layers are bonded via needle punching.
17 . The material of claim 1 , wherein
the outer and inner layers are bonded via thermal bonding.
18 . The material of claim 1 , wherein
the outer and inner layers are bonded via, or stitch bonding.
19 . A multi-layered composite insulation material, comprising:
a first and second outer layers comprising one or more of:
para-aramid, meta-aramid, flame-retarded modacrylic, or pre-oxidized polyacrylonitrile fibers; and
an inner layer disposed between the first and second outer layers comprising one or more of:
polyacrylonitrile fibers or ceramic fibers,
wherein
the inner and outer layers are bonded via needle punching, thermal bonding, or stitch bonding, and
the outer layers further comprise:
flame-retardant rayon fibers; and
a woven or knit fabric comprising continuous high-temperature glass, silica, or ceramic filaments.
20 . A multi-layered composite insulation material, comprising:
a first layer comprising one or more of:
para-aramid, meta-aramid, flame-retarded modacrylic, or pre-oxidized polyacrylonitrile fibers; and
a second layer comprising one or more of:
polyacrylonitrile fibers or ceramic fibers,
wherein
the first and second layers are bonded via needle punching, thermal bonding, or stitch bonding.