A mixed acrylate-siloxane polymer can be used to create three-dimensional (3D) structures of arbitrary shape via nanolithography. Treatment of such structures with amine (such as diamine) makes them permissive for neuronal cell adhesion and growth without need of additional modification such as poly-lysine (D or L) nor laminin.
1. A method of preparing a structure for cell culture, the method comprising:
providing an acrylate polymer attached to a substrate,
optionally treating the polymer to remove residual solvent and/or monomer; and then
performing Michael addition of amine with free acrylate groups on the polymer,
thereby obtaining a structure for cell culture having free amine groups wherein at least a portion of the free amine groups are protected by photo-cleavable functionality.
2. The method of claim 1 , wherein said amine is a diamine.
3. The method of claim 2 , wherein said diamine is selected from the group consisting of 1,2-ethane diamine; 1,3-propane diamine; 1,4-butane diamine; and 1,6-hexane diamine.
4. The method of claim 1 , wherein said substrate is glass.
5. The method of claim 1 , further comprising an initial step of preparing the acrylic polymer by cross-linking via ultraviolet radiation.
6. The method of claim 1 , further comprising selectively applying light to remove protection from one or more desired areas.