Interbody fusion device comprising textured surfaces
An expandable interbody fusion device and an associated instrument for inserting the device into an intervertebral disc space, expanding the device and for use in delivering graft material into the device once expanded in the disc space. The device is small enough to fit through Kambin's triangle yet is capable of expanding both in the vertical direction to accommodate spinal lordosis and in the lateral direction to provide sufficient structural support for opposing vertebral bodies laterally within the disc space. A process of forming textured top and bottom surfaces of the device by initially laser ablating each surface with a nano-second pulsed laser followed by laser ablating those surfaces with a femto-second pulsed laser.
1. A process of forming textured surfaces on an interbody fusion device that comprises a cage having a top surface and an opposite bottom surface, said textured surfaces being prepared by a process comprising the steps of:
initially laser ablating said top surface and said bottom surface of said cage with a nano- second pulsed laser to form a three-dimensional geometric pattern on each of said top surface and said bottom surface that comprises projections and recesses; and
then, laser ablating said initially ablated top surface and said bottom surface of said cage with an ultrafast pulsed laser to form nano-scale structures on said top surface and bottom surface, said nano-scale structures having a depth less than 1 μm.
2. An interbody fusion device comprising a cage with textured top and bottom surfaces prepared by the process of claim 1 .
3. The process of claim 1 , wherein said laser ablation of said initially ablated top and bottom surfaces with an ultrafast pulsed laser is conducted with a femtosecond pulsed laser such that said nano-scale structures have a depth not greater than 200 nm.
4. An interbody fusion device comprising a cage with textured top and bottom surfaces prepared by the process of claim 3 .
5. The interbody fusion device of claim 4 , wherein said cage is formed of titanium or titanium alloys.
6. A process of forming textured surfaces on an interbody fusion device that comprises a cage having a top surface and an opposite bottom surface, said textured surfaces being prepared by a process comprising the steps of:
initially forming a three-dimensional geometric pattern on each of said top surface and said bottom surface by laser ablating said respective top and bottom surfaces with a nano-second laser to form projections and recesses having a depth of up to at least 100 μm; and
then, laser ablating said three-dimensional geometric pattern surface on each of said top surface and said bottom surface of said cage with an ultrafast pulsed laser to form nano-scale structures on projections and within said recesses that have a depth less than 1 μm.
7. The process of claim 6 , wherein said nano-scale structures on each of said top surface and said bottom surface are formed with a picosecond pulsed laser.
8. The process of claim 6 , wherein said nano-scale structures on each of said top surface and said bottom surface are formed with a femtosecond pulsed laser.
9. The process of claim 8 , wherein said nano-scale structures on each of said top surface and said bottom surface are formed to have projections and recesses having a depth not greater than 200 nm.
10. An interbody fusion device comprising a cage with textured top and bottom surfaces prepared by the process of claim 9 .
11. The interbody fusion device of claim 10 , wherein said cage is formed of titanium or titanium alloys.
12. An interbody fusion device comprising a cage with textured top and bottom surfaces prepared by the process of claim 6 .
13. A process of forming textured surfaces on an interbody fusion device that comprises a cage having a top surface and an opposite bottom surface, said textured surfaces being prepared by a process comprising the steps of:
initially forming a three-dimensional geometric pattern on each of said top surface and said bottom surface by ablating each of said top surface and said bottom surface with a nanosecond laser to form a plurality of projections and recesses; and
then, further laser ablating said initially laser ablated top surface and bottom surface of said cage with a femtosecond pulsed laser to form nano-scale structures on said projections and within said recesses of said top surface and bottom surface.
14. The process of claim 13 , wherein said projections and recesses have a depth of up to at least 100 μm.
15. The process of claim 14 , wherein said nano-scale structures on said projections and within said recesses on said top surface and said bottom surface are formed to have a depth not greater than 200 nm.
16. An interbody fusion device comprising a cage with textured top and bottom surfaces prepared by the process of claim 15 .
17. An interbody fusion device of claim 16 , wherein said cage is formed of titanium or a titanium alloy.