Co-based alloy material, co-based alloy product, and method for manufacturing said product
There is provided a Co-based alloy material, having a chemical composition including: Al of 0.1 to 10 mass %; W of 3 to 45 mass %, the total content of Al and W being 50 mass % or less; O of 0.007 to 0.05 mass %; and the balance being Co and impurities, wherein in γ phase crystal grains as a matrix phase of the Co-based alloy material, segregation cells within an average size of 0.15 to 1.5 μm are formed, wherein in the segregation cells, γ′ phase grains within a size of 0.01 to 0.5 μm including Co, Al and W are dispersively precipitated, and wherein on boundary regions of the segregation cells and grain boundaries of the γ phase crystal grains, μ phase grains within a size of 0.005 to 2 μm including Co and W are dispersively precipitated.
1. A Co-based alloy material, having a chemical composition comprising:
Al of 0.1 mass % or more and 10 mass % or less;
W of 3 mass % or more and 45 mass % or less, the total content of the Al and the W being 50 mass % or less;
O of 0.007 mass % or more and 0.05 mass % or less; and
the balance being Co and impurities,
wherein in γ phase crystal grains as a matrix phase of the Co-based alloy material, segregation cells within an average size of 0.15 μm or more and 1.5 μm or less are formed,
wherein in the segregation cells, γ′ phase grains within a size of 0.01 μm or more and 0.5 μm or less including Co, Al and W are dispersively precipitated, and
wherein on boundary regions of the segregation cells and grain boundaries of the γ phase crystal grains, μ phase grains within a size of 0.005 μm or more and 2 μm or less including Co and W are dispersively precipitated.
2. The Co-based alloy material according to claim 1 , wherein:
the material is a powder comprising particles;
the particles have a size of 0.3 μm or more and 90 μm or less; and
the γ phase crystal grains constituting the powder particles have an average size of 50 μm or less.
3. The Co-based alloy material according to claim 1 , wherein:
the material is a powder comprising particles;
the particles have a size of 0.3 μm or more and 90 μm or less in an amount of 90 mass % or more thereof; and
the γ phase crystal grains constituting the powder particles have an average size of 50 μm or less.
4. The Co-based alloy material according to claim 2 , wherein
when a hole flow testing is performed in accordance with JIS Z 2502: 2012 for 50 g of the powder classified into a size range of 15 μm or more and 45 μm or less, fluidity of the powder classified is 15 s or more and 30 s or less.
5. The Co-based alloy material according to claim 3 , wherein
when a hole flow testing is performed in accordance with JIS Z 2502: 2012 for 50 g of the powder classified into a size range of 15 μm or more and 45 μm or less, fluidity of the powder classified is 15 s or more and 30 s or less.
6. The Co-based alloy material according to claim 1 , wherein the chemical composition further comprises:
E1 component that is at least one selected from B, C, Y, La and mischmetal, the total content of the E1 component being 0.001 mass % or more and 2 mass % or less; and
E2 component that is at least one selected from Cr, Fe, Ni, Mo, Ru, Re, Ir, Ti, Zr, Hf, V, Nb and Ta, the total content of the E2 component being 0.1 mass % or more and 50 mass % or less.
7. The Co-based alloy material according to claim 6 , wherein the chemical composition consists of:
C of 0.05 mass % or more and 0.15 mass % or less;
O of 0.007 mass % or more and 0.05 mass % or less;
Al of 2 mass % or more and 5 mass % or less;
W of 7 mass % or more and 25 mass % or less;
Cr of 6 mass % or more and 10 mass % or less;
Ni of 20 mass % or more and 35 mass % or less;
Ta of 3 mass % or more and 8 mass % or less; and
the balance being Co and impurities.