PRINTABLE HARD FERROUS METALLIC ALLOYS FOR ADDITIVE MANUFACTURING BY DIRECT ENERGY DEPOSITION PROCESSES
A printed metallic part is provided. The alloy has the composition of Fe at 69.2 wt. % to 89.1 wt. %; Cr at 7.25 wt. % to 16.0 wt. %; Nb at 0.01 wt. % to 10.0 wt. %; Mo at 0.5 wt. % to 4.0 wt. %. C at 0.03 wt. % to 0.4 wt. % and optionally one or more of Ni, Cu, Si, W, Mn, N and B. The printed metallic part has a tensile strength of at least 1300 MPa, a yield strength of at least 700 MPa, an elongation of at least 4.0%, and a hardness of at least 45 HRC.
1 . A method of layer-by-layer construction by direct energy deposition of a metallic part comprising:
supplying an alloy in particle form comprising the following elements: Fe at 69.2 wt. % to 89.1 wt. %; Cr at 7.25 wt. % to 16.0 wt. %; Nb at 0.01 wt. % to 10.0 wt. %; Mo at 0.5 wt. % to 4.0 wt. %. C at 0.03 wt. % to 0.4 wt. % and optionally one or more of Ni, Cu, Si, W, Mn, N and B;
supplying a substrate; and
applying one or more layers of the alloy onto the substrate by melting the alloy into a molten state and cooling and solidifying;
wherein the metallic part has the following properties: tensile strength of at least 1300 MPa, yield strength of at least 700 MPa, elongation of at least 4.0%, and hardness of at least 45 HRC.
2 . The method of claim 1 , wherein the layers have a thickness of 20 microns to 1000 microns.
3 . The method of claim 1 , wherein the alloy comprises Fe at 82.0 wt. % to 87.0 wt. %; Cr at 10.5 wt. % to 12.0 wt. %; Ni at 1.5 wt. % to 2.5 wt. %; Nb at 0.02 wt. % to 0.05 wt. %; Cu at 0.1 wt. % to 0.6 wt. %; Mo at 1.2 wt. % to 1.8 wt. %; Si 0.1 wt. % to 0.5 wt. %; C at 0.15 wt. % to 0.22 wt. %; and N at 0.03 wt. % to 0.08 wt. %.
4 . The method of claim 1 , wherein the alloy comprises Fe at 82.0 wt. % to 87.0 wt. %; Cr at 11.0 wt. % to 13.5 wt. %; Ni at 1.5 wt. % to 2.5 wt. %; Nb at 0.02 wt. % to 0.05 wt. %; Cu at 0.1 wt. % to 0.4 wt. %; Mo at 1.5 wt. % to 2.1 wt. %; Si 0.1 wt. % to 0.5 wt. %; C at 0.17 wt. % to 0.25 wt. %; and N at 0.02 wt. % to 0.06 wt. %.
5 . The method of claim 1 , wherein the alloy comprises Fe at 79.0 wt. % to 83.0 wt. %; Cr at 10.5 wt. % to 12.0 wt. %; Ni at 2.8 wt. % to 3.8 wt. %; Nb at 0.04 wt. % to 0.08 wt. %; Cu at 0.1 wt. % to 0.6 wt. %; Mo at 2.5 wt. % to 3.5 wt. %; Si at 0.1 wt. % to 0.5 wt. %; W at 0.1 wt. % to 1.0 wt. %; C at 0.20 wt. % to 0.25 wt. %; and N at 0.05 wt. % to 0.13 wt. %.
6 . The method of claim 1 , wherein the alloy comprises Fe 79.0 wt. % to 83.0 wt. %; Cr at 7.7 wt. % to 9.0 wt. %; Ni at 1.5 wt. % to 2.5 wt. %; Nb at 0.04 wt. % to 0.08 wt. %; Mo at 1.2 wt. % to 1.8 wt. %; W at 4.1 wt. % to 5.5 wt. %; Mn at 0.4 wt. % to 1.1 wt. %; C at 0.15 wt. % to 0.22 wt. %; N at 0.05 wt. % to 0.13 wt. %; and B at 0.01 wt. % to 0.05 wt. %.
7 . The method of claim 1 , wherein the substrate is heated to a temperature of less than or equal to 800° C.
8 . The method of claim 1 , wherein the metallic part undergoes solutionizing at a temperature of or greater than 900° C. followed by quenching.
9 . The method of claim 7 , wherein the metallic part is tempered at temperatures at or above room temperature.
10 . The method of claim 1 , wherein the metallic part undergoes a process to alter the surface structure and properties including carburizing, nitriding, carbonitriding, and deposition of coatings.
11 . A printed metallic part comprising:
Fe at 69.2 wt. % to 89.1 wt. %; Cr at 7.25 wt. % to 16.0 wt. %; Nb at 0.01 wt. % to 10.0 wt. %; Mo at 0.5 wt. % to 4.0 wt. %. C at 0.03 wt. % to 0.4 wt. % and optionally one or more of Ni, Cu, Si, W, Mn, N and B;
wherein the printed metallic part indicates a tensile strength of at least 1300 MPa, yield strength of at least 700 MPa, elongation of at least 4.0%, and hardness of at least 45 HRC.
12 . The printed metallic part of claim 11 , wherein the part comprises one or more layers having a thickness of 20 microns to 1000 microns.
13 . The printed metallic part of claim 11 , wherein the alloy comprises Fe at 82.0 wt. % to 87.0 wt. %; Cr at 10.5 wt. % to 12.0 wt. %; Ni at 1.5 wt. % to 2.5 wt. %; Nb at 0.02 wt. % to 0.05 wt. %; Cu at 0.1 wt. % to 0.6 wt. %; Mo at 1.2 wt. % to 1.8 wt. %; Si 0.1 wt. % to 0.5 wt. %; C at 0.15 wt. % to 0.22 wt. %; and N at 0.03 wt. % to 0.08 wt. %.
14 . The printed metallic part of claim 13 , wherein the metallic part has tensile strength of at least 1400 MPa, yield strength of at least 1000 MPa, elongation of at least 10.0%.
15 . The printed metallic part of claim 11 , wherein the alloy comprises Fe at 82.0 wt. % to 87.0 wt. %; Cr at 11.0 wt. % to 13.5 wt. %; Ni at 1.5 wt. % to 2.5 wt. %; Nb at 0.02 wt. % to 0.05 wt. %; Cu at 0.1 wt. % to 0.4 wt. %; Mo at 1.5 wt. % to 2.1 wt. %; Si 0.1 wt. % to 0.5 wt. %; C at 0.17 wt. % to 0.25 wt. %; and N at 0.02 wt. % to 0.06 wt. %.
16 . The printed metallic part of claim 15 , wherein the metallic part has tensile strength of at least 1300 MPa, yield strength of at least 800 MPa and hardness of at least 46 HRC.
17 . The printed metallic part of claim 11 , wherein the alloy comprises Fe at 79.0 wt. % to 83.0 wt. %; Cr at 10.5 wt. % to 12.0 wt. %; Ni at 2.8 wt. % to 3.8 wt. %; Nb at 0.04 wt. % to 0.08 wt. %; Cu at 0.1 wt. % to 0.6 wt. %; Mo at 2.5 wt. % to 3.5 wt. %; Si at 0.1 wt. % to 0.5 wt. %; W at 0.1 wt. % to 1.0 wt. %; C at 0.20 wt. % to 0.25 wt. %; and N at 0.05 wt. % to 0.13 wt. %.
18 . The printed metallic part of claim 17 , wherein the metallic part has tensile strength of at least 1600 MPa, and hardness of at least 48 HRC.
19 . The printed metallic part of claim 11 , wherein the alloy comprises Fe 79.0 wt. % to 83.0 wt. %; Cr at 7.7 wt. % to 9.0 wt. %; Ni at 1.5 wt. % to 2.5 wt. %; Nb at 0.04 wt. % to 0.08 wt. %; Mo at 1.2 wt. % to 1.8 wt. %; W at 4.1 wt. % to 5.5 wt. %; Mn at 0.4 wt. % to 1.1 wt. %; C at 0.15 wt. % to 0.22 wt. %; N at 0.05 wt. % to 0.13 wt. %; and B at 0.01 wt. % to 0.05 wt. %.
20 . The printed metallic part of claim 19 , wherein the metallic part has tensile strength of at least 1700 MPa, and hardness of at least 49 HRC.