CHEMOENZYMATIC DEGRADATION OF EPOXY RESINS
Provided is a method for degrading epoxy resins by enzymatic route, in particular by adding an epoxy resin in a solvent followed by treatment with a glutathione S-transferase. A method for recycling a composite material comprising epoxy resin as well as the use of glutathione 5-transferase and eventually para-hydroxybenzoate hydroxylase for degrading epoxy resins are also provided.
1 . A method for degrading an epoxy resin comprising the following successive steps:
a) adding in a solvent an epoxy resin R based on:
at least one aromatic compound R1 bearing at least two epoxide groups per molecule and comprising at least one aromatic ring bearing at least one glycidyloxy group, and
at least one curing agent R2,
to obtain mixture MA,
b) treating enzymatically the mixture MA obtained after step a), the treatment comprising a step of contacting the mixture MA with a glutathione S-transferase to obtain a mixture MB.
2 . The method according to claim 1 , further comprising a step c) performed after step b) or concomitantly with step b), step c) consisting in an enzymatic treatment which comprises a step of contacting mixture MA or mixture MB with a para-hydroxybenzoate hydroxylase to obtain a mixture MC.
3 . The method according to claim 1 , wherein enzymatic treatment consisting in step b) or step b) and step c) is followed by a successive step d) which consists in treating chemically mixture MB or mixture MC, the chemical treatment comprising a step of contacting mixture MB or mixture MC with an aqueous solution of a strong Bronsted base to obtain a mixture MD.
4 . The method according to claim 1 , wherein step a) comprises swelling of the epoxy resin R in the solvent.
5 . The method according to claim 1 , wherein in step a) the solvent is chosen among the group consisting in an aqueous solution of disodium phosphate and an aqueous solution of phosphoric acid and phenol.
6 . The method according to claim 1 , wherein in step b) the glutathione S-transferase is issued from a N. aromaticivorans strain.
7 . The method according to claim 2 , wherein in step c) the para-hydroxybenzoate hydroxylase is a mutated enzyme.
8 . The method according to claim 3 , wherein the aqueous solution of a strong Bronsted base in step d) is a sodium hydroxide aqueous solution.
9 . The method according to claim 1 , wherein the aromatic compound R1 corresponds to a diglycidyl ether of bisphenol.
10 . The method according to claim 1 , wherein the curing agent R2 is an amine or an imidazole derivative.
11 . The method according to claim 3 , wherein mixture MD obtained after step d) is then further submitted to steps b) to d) as defined above.
12 . The method according to claim 3 , wherein mixture MD obtained after step d) is further submitted to steps a) to d) as defined above.
13 . (canceled)
14 . (canceled)
15 . A method for recycling a composite material CM comprising the following steps:
a′) providing a composite material comprising an epoxy resin R based on:
at least one aromatic compound R1 bearing at least two epoxide groups per molecule and comprising at least one aromatic ring bearing at least one glycidyloxy group, and
at least one curing agent R2,
b′) treating the composite material CM obtained after step a′), the treatment comprising a step of degrading the epoxy resin R with the method as defined in claim 1 , in which case the epoxy resin R in step a) is the composite material CM,
c′) obtaining after step b′) the composite material with a reduced content in epoxy resin.
16 . The method of claim 5 , wherein in step a) the solvent is an aqueous solution of disodium phosphate.
17 . The method of claim 2 , wherein in step c) the para-hydroxybenzoate hydroxylase is a mutated enzyme presenting at least two point mutations L199V or L200V and Y385F.
18 . The method of claim 9 , wherein the aromatic compound R1 corresponds to a bisphenol A diglycidyl ether.