The invention relates to plastic films and a silicone containing polymer blend composition that can be used in the production of the plastic films which is a polymer composition obtainable from, per 100 parts by weight of the composition, 99.99 to 90 parts by weight of a polyolefin polymer (P) and 0.01 to 10 parts by weight of a masterbatch (M).
1 . A plastic packaging film comprising a core layer and two opposite outer layers, wherein an outer layer is obtainable by:
(i) forming a masterbatch (M) by reactively mixing under shear an organopolysiloxane (B) containing on average at least 1 alkenyl functionality per molecule with a polyolefin polymer (A), at a temperature such that the organopolysiloxane (B) and the polyolefin polymer (A) are in liquid phase, so as to form a copolymer of (A) and (B) then cooling the formed copolymer to produce said masterbatch (M) in solid form containing organopolysiloxane (B), polyolefin polymer (A) and the copolymer of (A) and (B); then
(ii) introducing, per 100 parts by weight, 0.01 to 10 parts by weight of masterbatch (M) into 99.99 to 90 parts by weight of a polyolefin polymer (P) and blending to form a composition, and
(iii) making a film by processing the composition of step (ii).
2 . The plastic film according to claim 1 wherein the polyolefin polymer (A) and/or the polyolefin polymer (P) is a blend of polyolefins.
3 . The plastic film according to claim 1 , wherein the polyolefin polymer (A) and/or the polyolefin polymer (P) are functionalized, preferably with an alkyl acrylate function such as methyl acrylate, ethyl acrylate, butyl acrylate, or an acrylic function or maleic anhydride function.
4 . The plastic film according to claim 1 wherein the polyolefin polymer (P) comprises polypropylene and/or polyethylene.
5 . The plastic film according to claim 1 wherein the polyolefin polymer (A) comprises polypropylene and/or polyethylene.
6 . The plastic film according to claim 1 wherein the organopolysiloxane (B) has a number average molecular weight of 200,000 to 2.000,000 g/mole.
7 . The plastic film according to claim 1 wherein the alkenyl functionalities of the organopolysiloxane (B) comprise vinyl functionalities and wherein the vinyl functionalities are present in an amount comprised between 0.01% and 2.00% by weight of the organopolysiloxane (B).
8 . A method of making a plastic packaging film comprising a core layer and two opposite outer layers, wherein an outer layer is made by:
(i) forming a masterbatch (M) by reactively mixing under shear an organopolysiloxane (B) containing on average at least 1 alkenyl functionality per molecule with a polyolefin polymer (A), at a temperature such that the organopolysiloxane (B) and the polyolefin polymer (A) are in liquid phase, so as to form a copolymer of (A) and (B) then cooling the formed copolymer to produce said masterbatch (M) in solid form containing organopolysiloxane (B), polyolefin polymer (A) and the copolymer of (A) and (B); then
(ii) introducing, per 100 parts by weight, 0.01 to 10 parts by weight of masterbatch (M) into 99.99 to 90 parts by weight of a polyolefin polymer (P) and blending to form a composition and
(iii) making a film by processing the composition of step (ii).
9 . The method according to claim 8 , wherein the polyolefin polymer (A) and/or the polyolefin polymer (P) are functionalized, preferably with an alkyl acrylate function such as methyl acrylate, ethyl acrylate, butyl acrylate, or an acrylic function or maleic anhydride function.
10 . The method according to claim 8 wherein the polyolefin polymer (P) comprises polypropylene and/or polyethylene.
11 . The method according to claim 8 wherein the polyolefin polymer (A) comprises polypropylene and/or polyethylene.
12 . The method according to claim 8 wherein the organopolysiloxane (B) is linear.
13 . The method in accordance with claim 8 wherein step (iii) is selected from one or more of extrusion, co-extrusion, lamination, melt pressing, and coating methods or a combination thereof.
14 . The method in accordance with claim 8 wherein step (iii) involves one or more of cast co-extrusion or blown co-extrusion methods, adhesive lamination, extrusion lamination, thermal lamination, melt pressing and coating methods such as vapour deposition.
15 . A plastic film in accordance with claim 1 wherein the polymer composition additionally comprises one or more additives selected from antistatic additives, anti-blocking additives and/or anti-fogging additives.
16 . A plastic film in accordance with claim 1 wherein step (iii) is selected from one or more of extrusion, co-extrusion, lamination, melt pressing, and coating methods or a combination thereof.
17 . A plastic film in accordance with claim 1 wherein step (iii) involves one or more of cast co-extrusion or blown co-extrusion methods, adhesive lamination, extrusion lamination, thermal lamination, melt pressing and coating methods such as vapour deposition.
18 . The method according to claim 8 wherein the polyolefin polymer (A) and/or the polyolefin polymer (P) is a blend of polyolefins.