Carbon nano materials in crosslinked polyurethane and polyurea applications with optimized properties
Disclosed herein are novel methods to handling carbon nano materials and forming composite materials from carbon nano materials and polymers such as polyurethane and polyurea materials. Such novel methods provide a number of benefits to a polymer processor and end user of any resulting materials or products. As disclosed herein, methods of incorporating carbon nano materials into polymers can achieve benefits regarding electrical properties, modulus, and thermal stability as well as other benefits. However, enhancing and creating such improvements in material properties must be done with care because creating or enhancing one property does not always result in the creation or improvement in other properties. For example, thermal stability, electrical conductivity, and mechanical properties can be optimized in different ways, and at different loadings of differing carbon nano materials. Thus, it is necessary to carefully consider a number of factors when designing methods for incorporating carbon nano materials into polymers.
1. A method of making a crosslinked aliphatic polyurea polymer with rheological and conducting properties, the method comprising:
providing a carbon nanotube masterbatch dispersion comprising from 0.1% to 15% (weight/weight) of carbon nanotubes;
blending an amount of the carbon nanotube masterbatch and a polyol resin to obtain a carbon nanotube polyol resin blend, to afford a concentration of carbon nanotubes in the polyol resin of from 60 ppm to 11000 ppm, and the polyol viscosity is below 4000 cP at a shear rate of 100 s −1 , 25° C.;
mixing the carbon nanotube polyol blend and polyisocyanate in a 1:1 polyol: polyisocyanate stoichiometry to form a polymer mixture; and
curing the polymer mixture in a form;
wherein the resulting polymer has electrical resistivity of 10 4 Ω*cm −1 or more.
2. The method of claim 1 , wherein the concentration of the carbon nanotube in the polyol resin does not exceed 600 ppm.
3. The method of claim 1 , wherein the concentration of the carbon nanotubes in the polyol resin is 150 ppm.
4. The method of claim 3 , wherein the polyol viscosity is about 1400 cP at 20 s −1 .
5. The method of claim 1 , wherein the carbon nanotubes are single wall carbon nanotubes.
6. A crosslinked aliphatic polyurea polymer comprising:
a carbon nanotube polyol resin blend, wherein the concentration of carbon nanotubes in the polyol resin blend is from 60 ppm to 11000 ppm, and the polyol viscosity is below 4000 cP at a shear rate of 100 s −1 , 25° C.; and
blending polyisocyanate in a 1:1 stoichiometry with the polyol resin
wherein upon curing the polyol carbon nanotube and polyisocyanate mixture to form a polymer, wherein the polymer has electrical resistivity of 10 4 Ω*cm −1 or more.
7. The crosslinked aliphatic polyurea polymer of claim 6 , wherein the concentration of carbon nanotubes in the polyol resin does not exceed 600 ppm.
8. The crosslinked aliphatic polyurea polymer of claim 6 , wherein the concentration of carbon nanotubes in the polyol resin is 150 ppm.
9. The crosslinked aliphatic polyurea polymer of claim 6 , wherein the polyol resin viscosity is about 1400 cP at 20 s −1 .
10. The crosslinked aliphatic polyurea polymer of claim 6 , wherein the carbon nanotubes are single wall carbon nanotubes.
11. A carbon nanotube polyol blend obtained by a method comprising:
providing a carbon nanotube masterbatch dispersion comprising from 0.1% to 15% (weight/weight) of carbon nanotubes;
blending an amount of the masterbatch and a polyol resin to obtain a carbon nanotube polyol resin blend, wherein the concentration of carbon nanotubes in the polyol resin blend is from 60 ppm to 11000 ppm, and the polyol viscosity is below 4000 cP at a shear rate of 100 s −1 , 25° C.; and
the carbon nanotubes in the polyol resin blend are characterized by an electrical resistivity of 10 4 Ω*cm −1 or more when the polyol resin in the carbon nanotube in the polyol resin blend is combined in a 1:1 stoichiometric ratio with a polyisocyanate and cured.
12. The carbon nanotube polyol blend of claim 11 , wherein the concentration of carbon nanotubes in the polyol resin does not exceed 600 ppm.
13. The carbon nanotube polyol blend of claim 11 , wherein the concentration of the carbon nanotube in the polyol resin is 150 ppm.
14. The carbon nanotube polyol blend of claim 11 , wherein the polyol resin viscosity is about 1400 cP at 20 s −1 .
15. The carbon nanotube polyol blend of claim 11 , wherein the carbon nanotubes are single wall carbon nanotubes.