Granted Patent B2

US 12,295,848 · App. 17/966,092 · Granted May 13, 2025

Inventors: Michele Christine McAllister (Freehold, NJ); David Wang (Rockville, MD); Michelle Bubear (Newton, NJ); Joed Canales (Harrison, NJ); Amy Chang (Kaneohe, HI); Roman Shikhanovich (Edison, NJ); Mark Spilker (Plainsboro, NJ); Eric Semler (Morganville, NJ)

A61F2/28A61L27/3604A61L27/3608A61L27/365A61L27/3683A61F2240/001A61L2400/18A61L2430/02A61L2430/38

Abstract

Claims (20)

1. A method for producing an implant from modified demineralized cortical bone fibers which is at least partially opaque, said method comprising the steps of:

contacting the demineralized cortical bone fibers with a salt solution prior to lyophilizing;

shaping a mass of the demineralized cortical bone fibers to form an implant having a desired shape;

forming one or more at least partially radio opaque portions of the implant, after the shaping step and before the lyophilizing step, by

at least partially remineralizing one or more regions of the implant by alternately contacting implant with an aqueous calcium chloride solution and an aqueous sodium phosphate solution, with agitation, to form one or more remineralized regions each of which is at least partially opaque,

and

lyophilizing the implant,

to produce a lyophilized implant that is at least partially radio opaque and has a residual moisture content of less than about 6% by weight, based on the total weight of the implant, and a complete rehydration time of less than about 30 minutes, and wherein said lyophilized implant remains cohesive and retains its shape upon complete hydration.

2. The method of claim 1 , wherein the at least one radio opaque material comprises at least partially remineralized cortical bone, at least partially remineralized cancellous bone, or combinations thereof.

3. The method of claim 1 , further comprising contacting the demineralized cortical bone fibers with a chemical solution, which may or may not be combined with the salt solution prior to shaping and is selected from: a biocompatible polar molecule, a buffer solution, and combinations thereof.

4. The method of claim 3 , wherein the chemical solution is a buffered saline solution.

5. The method of claim 1 , further comprising the step of curing the implant at a temperature of from about 20° C. to about 50° C. for a period of up to about 48 hours by one or more techniques selected from air drying, heat drying and applying energy to the implant, said curing step being performed prior to said lyophilizing step.

6. The method of claim 1 , further comprising the step of crosslinking at least a portion of the implant by one or more techniques selected from: exposing the implant to energy, chemical crosslinking and heating, said crosslinking step being performed prior to said lyophilizing step.

7. The method of claim 6 , wherein said crosslinking step is performed by exposing the implant to energy and the energy is selected from ultraviolet light or microwave energy.

8. The method of claim 1 , wherein the step of shaping comprises:

providing to an implant forming container a solution comprising demineralized cortical bone fibers and a liquid;

separating the liquid from the demineralized cortical bone fibers; and

removing the liquid from the container.

9. The method of claim 8 , wherein the step of shaping further comprises agitating the solution in the implant forming container to homogenously distribute the demineralized cortical bone fibers in the liquid.

10. The method of claim 8 , wherein the implant forming container is a press mold comprising a reservoir for holding the solution therein and a plunger which is reciprocatingly movable in and out of the reservoir, wherein the step of separating is performed by pressing the plunger into the reservoir, thereby compressing the demineralized cortical bone fibers and causing the liquid to separate from the demineralized cortical bone fibers by either flowing through a filter at an end of the reservoir that is opposite the plunger, or by flowing through a plurality of perforations provided in the plunger.