Use of polyamide 6
The invention relates to the use of polyamide 6 for reduction of the melt viscosity, to be determined at 260° C. to ISO 11443, and/or of the fill pressure, to be determined according to EN ISO 294-1, of compositions and moulding compounds in which there are 10 to 115 parts by mass of glass fibres per 100 parts by mass of poly-C 1 -C 6 -alkylene terephthalate.
1 . A method for reduction of the melt viscosity to be determined at 260° C. to ISO 11443, and/or of the fill pressure to be determined according to EN ISO 294-1, of compositions and moulding compounds having 10 to 115 parts by mass of glass fibers per 100 parts by mass of poly-C 1 -C 6 -alkylene terephthalate, comprising including polyamide 6 in the compositions and moulding compounds.
2 . A method according to claim 1 , wherein the poly-C 1 -C 6 -alkylene terephthalate is polyethylene terephthalate.
3 . A method according to claim 1 , wherein the poly-C 1 -C 6 -alkylene terephthalate is polybutylene terephthalate.
4 . A method according to claim 1 , wherein in addition to the glass fibers 0.5 to 30 parts by mass of at least one copolymer of at least one α-olefin and at least one methacrylic ester or acrylic ester of an aliphatic alcohol are applied.
5 . A method according to claim 4 , wherein the copolymer of at least one α-olefin and at least one acrylic ester used is a copolymer of ethene and 2-ethylhexyl acrylate.
6 . A method according to claim 4 , wherein the copolymer of at least one α-olefin and at least one acrylic ester used is a copolymer of ethene and butyl acrylate.
7 . A method according to claim 1 , wherein the amount of polyamide 6 used is 0.5 to 15 parts by mass.
8 . A method according to claim 1 , wherein the compositions and moulding compounds are the basis for components to be used in the electrical or electronics industry.
9 . A method according to claim 1 , wherein the compositions and moulding compounds are the basis for components to be used in the electromobility.
10 . Compositions, moulding compounds and articles of manufacture comprising, per
A) 100 parts by mass of poly-C1-C6-alkylene terephthalate,
B) 10 to 115 parts by mass of glass fibres,
C) 0.5 to 15 parts by mass of polyamide 6, and
D) 0.5 to 30 parts by mass of at least one copolymer of at least one α-olefin and at least one methacrylic ester or acrylic ester of an aliphatic alcohol.
11 . Compositions, moulding compounds and articles of manufacture according to claim 10 , wherein the poly-C 1 -C 6 -alkylene terephthalate is polyethylene terephthalate.
12 . Compositions, moulding compounds and articles of manufacture according to claim 10 , wherein the poly-C 1 -C 6 -alkylene terephthalate is polybutylene terephthalate.
13 . Compositions, moulding compounds and articles of manufacture according to claim 10 , wherein the copolymer of at least one α-olefin and at least one acrylic ester used is a copolymer of ethene and 2-ethylhexyl acrylate.
14 . Compositions, moulding compounds and articles of manufacture according to claim 10 , wherein the copolymer of at least one α-olefin and at least one acrylic ester used is a copolymer of ethene and butyl acrylate.