ROLLER SURFACE HARDENING
The present disclosure relates to rollers such as nip rollers and calendering rollers with a coating and a method of applying the coating. More specifically, the present disclosure relates to a nip roller or a calender roller with a hardening layer applied to the surface to prevent damage from contaminants.
1 . A method of forming a dry electrode film, the method comprising:
contacting a surface hardened roller with a dry electrode or dry electrode precursor powder,
imparting at least one force on the dry electrode or the dry electrode precursor powder with the surface hardened roller in order to form the dry electrode film.
2 . The method of claim 1 , wherein the surface hardened roller includes a hardening layer of at least diamond like coating or tungsten carbide.
3 . The method of claim 2 , wherein the thickness of the hardening layer is about 1 μm to about 300 μm.
4 . The method of claim 1 , wherein the surface hardened roller includes at least one underlayer.
5 . The method of claim 4 , wherein the underlayer is comprised of one of tungsten carbide, a diamond like coating, copper, or chrome.
6 . The method of claim 4 , wherein the underlayer has a thickness of about 1 μm to about 50 μm.
7 . The method of claim 1 , wherein the surface hardened roller is at least one of a nip roller or a calendering roller.
8 . A system comprising:
a roller comprising:
a hardening layer positioned on the surface of the roller.
9 . The system of claim 8 , wherein the hardening layer is comprised of one of tungsten carbide, chrome, or a diamond like coating.
10 . The system of claim 8 , wherein the thickness of the hardening layer is about 1 μm to about 300 μm.
11 . The system of claim 8 , further comprising an underlayer positioned between the surface of the roller and the hardening layer, wherein:
the underlayer is comprised of one of tungsten carbide, a diamond like coating, copper, or chrome.
12 . The system of claim 11 , wherein the underlayer has a thickness of about 1 μm to about 300 μm