DRY AND COLD PERFORMANCE OF POLYAMIDES VIA INCORPORATION OF POLYETHER DIAMINES
A polyamide composition comprising a base polyamide and an elastomer concentrate comprising: 20-80 wt % of an elastomeric aliphatic polyether having a molecular weight ranging from 400-4000 g/mol; and 80-20 wt % of a concentrate polyamide. The polyamide composition has particular uses as a cable tie and demonstrates improved cold-temperature applications while maintaining high strength, good flammability rating, and excellent processability.
1 . A polyamide composition comprising:
a base polyamide, and
an elastomer concentrate comprising:
a. 20-80 wt % of an elastomeric aliphatic polyether having a molecular weight ranging from 400-4000 g/mol; and
b. 80-20 wt % of a concentrate polyamide.
2 . The polyamide composition of claim 1 , wherein the elastomeric aliphatic polyether comprises a compound of the formula:
wherein:
each n ranges from 1-5;
each x ranges from 1-50; and
y ranges from 0-2.
3 . The polyamide composition of claim 1 , wherein the elastomeric aliphatic polyether is a polytetramethylether diamine.
4 . The polyamide composition of claim 1 , wherein the elastomeric aliphatic polyether is a polyethylene oxide diamine.
5 . The polyamide composition of claim 2 , wherein n is 3 and the elastomeric aliphatic polyether has a molecular weight of 500-1500 g/mol.
6 . The polyamide composition of claim 2 , wherein n is 1 and the elastomeric aliphatic polyether has a molecular weight of 1500-2500 g/mol.
7 . The polyamide composition of claim 2 , wherein y is 0 and the elastomeric aliphatic polyether is a diamine.
8 . The polyamide composition of claim 1 , wherein the concentrate polyamide comprises PA6,6; PA6; PA610; PA611, PA612; PA10; PA11; or PA12; or combinations thereof.
9 . The polyamide composition of claim 1 , wherein the elastomer concentrate comprises a copolymer/terpolymer comprising elastomer repeat units and polyamide repeat units comprising PA6,6; PA6; PA610; PA611, PA612; PA10; PA11; or PA12; or combinations thereof.
10 . The polyamide composition of claim 4 , wherein the elastomer concentrate comprises a terpolymer of PA6,6, PA6, and the elastomeric aliphatic polyether.
11 . The polyamide composition of claim 3 , wherein the elastomer concentrate comprises a terpolymer of PA6,6, PA6,10, and the elastomeric aliphatic polyether.
12 . The polyamide composition of claim 1 , wherein the polyamide composition comprises 5-20 wt % of the elastomer concentrate and 80-95 wt % of the base polyamide.
13 . The polyamide composition of claim 1 , wherein the base polyamide comprises a PA6,6 homopolymer.
14 . The polyamide composition of claim 1 , further comprising one or more lubricants.
15 . The polyamide composition of claim 14 , wherein the lubricant is selected from the group consisting of ethylene bis(stearamdie) (EBS), stearyl erucamide, montan waxes, polyethylene waxes, polypropylene waxes, and combinations thereof.
16 . The polyamide composition of claim 1 , further comprising one or more heat stabilizers.
17 . The polyamide composition of claim 1 , further comprising colorants, carbon black, and/or nigrosine.
18 . The polyamide composition of claim 1 , further comprising one or more nucleating agents.
19 . The polyamide composition of claim 18 , wherein the nucleating agents are selected from the group consisting of calcium fluoride, calcium carbonate, talc, PA 2,2, and combinations thereof.
20 . An article for use in cold-temperature applications, wherein the article is formed from the polyamide composition of claim 1 , wherein the article is used for fasteners, circuit breakers, terminal blocks, connectors, automotive parts, furniture parts, appliance parts, cable ties, sports equipment, gun stocks, window thermal breaks, aerosol valves, food film packaging, automotive/vehicle parts, textiles, industrial fibers, carpeting, or electrical/electronic parts.
21 . The article of claim 20 , wherein the article is a cable tie.
22 . The article of claim 20 , wherein the article demonstrates a tensile strength greater than 60 MPa, and a flame rating of V-2 or higher.
23 . The article of claim 20 , wherein the article demonstrates a cold-weather cable-tie-installation-performance fail rate of less than 10%.
24 . A process for improving cold-temperature performance in a polyamide composition, comprising the step of adding to a base polymer an elastomer concentrate comprising:
an elastomer concentrate comprising:
a. 20-80 wt % of an elastomeric aliphatic polyether having a molecular weight ranging from 400-4000 g/mol; and
b. 80-20 wt % of a concentrate polyamide,
to produce a modified polyamide composition having improved cold-temperature performance.
25 . The process of claim 24 , wherein the polyamide composition is a cable tie, and the improved cold-temperature performance demonstrated by a cold-weather cable-tie-installation-performance fail rate of less than 10%.
26 . The process of claim 24 , wherein the polyamide composition has a tensile strength of 60 MPa or greater, and a flame rating of V-2 or higher.