MOLDING COMPOSITIONS BASED ON POLYAMIDE, ON CARBON FIBERS AND ON HOLLOW GLASS BEADS AND USE THEREOF
Molding composition, including by weight: (A) from 38 to 79.5% of at least one semi-crystalline aliphatic polyamide with the exclusion of PA6 and PA66, (B) from 10 to 20% of carbon fibres, (C) from 10 to 20% of hollow glass beads, (D) from 5.5 to 10% of at least one impact modifier having a flexural modulus of less than 200 MPa, in particular less than 100 MPa, as measured according to standard ISO 178: 2010, at 23° C., and (E) from 0.1 to 1% by weight of at least one additive, the sum of the proportions of each constituent (A)+(B)+(C)+(D)+(E) of the composition being equal to 100%.
1 . A molding composition, comprising by weight:
(A) from 38 to 79.5% of at least one semi-crystalline aliphatic polyamide,
(B) from 10 to 20% of carbon fibers,
(C) from 10 to 20% of hollow glass beads,
(D) from 5.5% to 20% of at least one impact modifier having a flexural modulus of less than 200 MPa, as measured according to standard ISO 178:2010 at 23° C., and
(E) from 0.1 to 1% by weight of at least one additive selected from the fillers selected from silica, graphite, expanded graphite, carbon black, kaolin, magnesia, slag, talc, wollastonite, nanofillers (carbon nanotubes), pigments, metal oxides (titanium oxide), metals, dyes, stabilizers, plasticizers, surfactants, nucleating agents, pigments, brighteners, antioxidants, lubricants, flame retardants, natural waxes and mixtures thereof, the sum of the proportions of each constituent (A)+(B)+(C)+(D)+(E) of said composition being equal to 100%,
excluding PA6 and PA66.
2 . The composition according to claim 1 , wherein said impact modifier is selected from a polyether block amide (PEBA), a functionalized or non-functionalized polyolefin and mixtures thereof.
3 . The composition according to claim 1 , wherein the impact modifier is selected from a polyether block amide (PEBA) having a flexural modulus less than 100 MPa as measured according to standard ISO 178:2010 at 23° C., and a mixture of polyether block amide (PEBA) having a flexural modulus less than 100 MPa as measured according to standard ISO 178:2010 at 23° C. with a functionalized or non-functionalized polyolefin.
4 . The composition according to claim 3 , wherein the PEBA has a density greater than or equal to 1, as determined according to ISO 1183-3: 1999.
5 . The composition according to claim 1 , wherein the impact modifier is selected from a functionalized polyolefin, a non-functionalized polyolefin and mixtures thereof, said impact modifier being present from 7 to 20.0% relative to the total weight of the composition.
6 . The composition according to claim 3 , wherein the functionalized polyolefin has a function selected from the maleic anhydride, carboxylic acid, carboxylic anhydride and epoxide functions.
7 . The composition according to claim 1 , wherein the carbon fibers are short carbon fibers having a fiber length comprised from 100 to 600 μm, said length being measured after compounding in the composition to be molded.
8 . The composition according to claim 1 , wherein the hollow glass beads have a mean volume diameter d 50 from 10 to 80 μm, as measured by laser diffraction according to ASTM B 822-17.
9 . The composition according to claim 1 , wherein the hollow glass beads have a real density of 0.10 to 0.65 g/cm 3 , measured according to ASTM D 2840-69 (1976) with a gas pycnometer and helium as the measuring gas.
10 . The composition according to claim 1 , wherein the hollow glass beads have a compression resistance, as measured according to ASTM D 3102-72 (1982) in glycerol of at least 50 MPa.
11 . The composition according to claim 1 , wherein the semi-crystalline polyamide is obtained by polycondensation:
of at least one C 6 to C 18 amino acid, or
of at least one C 6 to C 18 lactam, or
of at least one C 4 -C 36 aliphatic diamine Ca with at least one C 4 -C 36 aliphatic dicarboxylic acid Cb, or
a mixture thereof.
12 . The composition according to claim 1 , wherein the semi-crystalline polyamide is obtained by polycondensation:
of at least one C 6 to C 18 amino acid, or
of at least one C 6 to C 18 lactam.
13 . The composition according to claim 1 , wherein said semi-crystalline polyamide is selected from is selected from PA610, PA612, PA1010, PA1012, PA1212, PA11 and PA 12.
14 . The composition according to claim 1 , wherein said semi-crystalline polyamide is selected from PA11 and PA12.
15 . (canceled)
16 . A use of a composition as defined in claim 1 , for the manufacture of an article for electronics, sports, motor vehicles or industry.
17 . The use according to claim 16 , wherein the article is manufactured by injection molding.
18 . An article obtained by injection molding with a composition as defined in claim 1 .
19 . A molding composition, comprising by weight:
(A) from 38 to 79.5% of at least one semi-crystalline aliphatic polyamide,
(B) from 10 to 20% of carbon fibers,
(C) from 10 to 20% of hollow glass beads,
(D) from 5.5% to 20% of at least one impact modifier having a flexural modulus of less than 200 MPa, as measured according to standard ISO 178:2010 at 23° C., and
(E) from 0.1 to 1% by weight of at least one additive selected from the fillers selected from silica, graphite, expanded graphite, carbon black, kaolin, magnesia, slag, talc, wollastonite, nanofillers (carbon nanotubes), pigments, metal oxides (titanium oxide), metals, dyes, stabilizers, plasticizers, surfactants, nucleating agents, pigments, brighteners, antioxidants, lubricants, flame retardants, natural waxes and mixtures thereof,
the sum of the proportions of each constituent (A)+(B)+(C)+(D)+(E) of said composition being equal to 100%,
excluding PA6 and PA66, and
wherein the impact modifier is selected from a polyether block amide (PEBA) having a flexural modulus less than 100 MPa as measured according to standard ISO 178:2010 at 23° C., and a mixture of polyether block amide (PEBA) having a flexural modulus less than 100 MPa as measured according to standard ISO 178:2010 at 23° C. with a functionalized or non-functionalized polyolefin.
20 . A molding composition, comprising by weight:
(A) from 38 to 79.5% of at least one semi-crystalline aliphatic polyamide,
(B) from 10 to 20% of carbon fibers,
(C) from 10 to 20% of hollow glass beads,
(D) from 5.5% to 20% of at least one impact modifier having a flexural modulus of less than 200 MPa, as measured according to standard ISO 178:2010 at 23° C., and
(E) from 0.1 to 1% by weight of at least one additive selected from the fillers selected from silica, graphite, expanded graphite, carbon black, kaolin, magnesia, slag, talc, wollastonite, nanofillers (carbon nanotubes), pigments, metal oxides (titanium oxide), metals, dyes, stabilizers, plasticizers, surfactants, nucleating agents, pigments, brighteners, antioxidants, lubricants, flame retardants, natural waxes and mixtures thereof,
the sum of the proportions of each constituent (A)+(B)+(C)+(D)+(E) of said composition being equal to 100%,
excluding PA6 and PA66, and
excluding nano alumina.