METHOD FOR PRODUCING LITHIUM SULFIDE
A method is provided that can produce lithium sulfide with high purity. The method for producing lithium sulfide includes: a first step of reducing a raw material containing lithium (Li) and sulfur (S) elements, using a reductant containing a carbon (C) element, thereby obtaining an intermediate; and a second step of reducing the intermediate using a reducing gas, thereby obtaining lithium sulfide. It is preferable that the first step is performed in an inert gas atmosphere. It is also preferable that the first step is performed at a temperature of from 700° C. to 850° C. It is also preferable that the second step is performed at a temperature of from 830° C. to 930° C.
1 . A method for producing lithium sulfide, comprising:
a first step of reducing a raw material containing lithium (Li) and sulfur (S) elements, using a reductant containing a carbon (C) element, thereby obtaining an intermediate; and
a second step of reducing the intermediate using a reducing gas, thereby obtaining lithium sulfide.
2 . The method for producing lithium sulfide according to claim 1 , wherein the first step is performed in such a manner that a ratio of I A to I B (I A /I B ) is 0.10 or less, and a ratio of I C to I B (I C /I B ) is from 0.03 to 0.09, wherein
the I A represents an intensity of a peak observed at 2θ=25.6°±0.5° in an X-ray diffraction pattern of the intermediate,
the I B represents an intensity of a peak observed at 2θ=27.1°±0.5° in an X-ray diffraction pattern of the intermediate and
the I C represents an intensity of a peak observed at 2θ=21.2°±0.5° in an X-ray diffraction pattern of the intermediate,
the X-ray diffraction pattern of the intermediate being measured using an X-ray diffractometer.
3 . The method for producing lithium sulfide according to claim 1 , wherein the second step is performed in such a manner that a ratio of I C to I B (I C /I B ) is 0.02 or less, wherein
the I B represents an intensity of a peak observed at 2θ=27.1°±0.5° in an X-ray diffraction pattern of the lithium sulfide, and
the I C represents an intensity of a peak observed at 2θ=21.2°±0.5° in an X-ray diffraction pattern of the lithium sulfide,
the X-ray diffraction pattern of the lithium sulfide being measured using an X-ray diffractometer.
4 . The method for producing lithium sulfide according to claim 1 , wherein the first step is performed in an inert gas atmosphere.
5 . The method for producing lithium sulfide according to claim 1 , wherein the first step is performed at a temperature of from 700° C. to 850° C.
6 . The method for producing lithium sulfide according to claim 1 , wherein the second step is performed at a temperature of from 830° C. to 930° C.
7 . A method for producing lithium sulfide, comprising a step of reducing a raw material containing lithium (Li) and sulfur (S) elements, using a reductant containing a carbon (C) element and a reducing gas, thereby obtaining lithium sulfide.
8 . The method for producing lithium sulfide according to claim 7 , wherein the step is performed at a temperature of from 830° C. to 870° C.
9 . Lithium sulfide produced using the method according to claim 1 .
10 . A method for producing a solid electrolyte, comprising:
a step A of obtaining lithium sulfide;
a step B of mixing the lithium sulfide with phosphorus pentasulfide and lithium halide, thereby obtaining a raw material composition; and
a step C of firing the raw material composition,
wherein the step A includes a first step of reducing a raw material containing lithium (Li) and sulfur (S) elements, using a reductant containing a carbon (C) element, thereby obtaining an intermediate, and a second step of reducing the intermediate using a reducing gas, thereby obtaining lithium sulfide.
11 . The method for producing a solid electrolyte according to claim 10 , wherein the solid electrolyte contains a crystalline phase with an argyrodite-type crystal structure.