Process for preparing zeolite material having an AFX framework structure and zeolite material as prepared
Disclosed herein is a process for preparing a zeolite material having an AFX framework structure including X2O3 and YO2 via interzeolite conversion, the process including (1) providing a mixture including a first zeolite material having a non-FAU framework structure including X2O3 and YO2 and an organic structure directing agent selected from the group consisting of diquaternary ammonium cation containing compounds, and (2) heating the mixture from (1) to form a second zeolite material having an AFX framework structure including X2O3 and YO2, wherein X is a trivalent element and Y is a tetravalent element, and where the organic structure directing agent is not 1,4-bis(1,4-diazabicyclo[2.2.2]octane)butyl dihydroxide when the first material zeolite has a CHA framework structure. Further disclosed herein is the zeolite material having an AFX framework structure as obtainable or obtained from the process, and a method of using the same as a catalytically active material.
1 . A process for preparing a zeolite material having an AFX framework structure comprising X 2 O 3 and YO 2 via interzeolite conversion, the process comprising
(1) providing a mixture comprising a first zeolite material having a non-FAU framework structure comprising X 2 O 3 and YO 2 and an organic structure directing agent selected from the group consisting of diquaternary ammonium cation containing compounds, wherein the first zeolite material acts as sources for X 2 O 3 and YO 2 , and
(2) heating the mixture from (1) to form a second zeolite material having an AFX framework structure comprising X 2 O 3 and YO 2 ,
wherein X is a trivalent element and Y is a tetravalent element, and
wherein when the first zeolite material is a zeolite having a CHA framework structure, the organic structure directing agent is not 1,4-bis(1,4-diazabicyclo[2.2.2]octane)butyl dihydroxide.
2 . The process according to claim 1 , wherein X is selected from the group consisting of Al, B, In and Ga and any combinations thereof.
3 . The process according to claim 1 , wherein Y is selected from the group consisting of Si, Sn, Ti, Zr, Ge and any combinations thereof.
4 . The process according to claim 1 , wherein the first zeolite material is a zeolite having a CHA framework structure or a zeolite having an MFI framework structure.
5 . The process according to claim 1 , wherein the first zeolite material is an aluminosilicate zeolite.
6 . The process according to claim 1 , wherein the organic structure directing agent is selected from the group consisting of the compounds containing a diquaternary ammonium cation of formula (I)
(R 1 R 2 R 3 )N + (CH 2 ) n N + (R 4 R 5 R 6 ) (I)
in which
R 1 , R 2 , R 3 , R 4 , R 5 and R 6 , independently from each other, are selected from the group consisting of C 1 -C 10 alkyl, and
n is an integer of 3 to 10,
or in which
one of R 1 , R 2 and R 3 is selected from the group consisting of C 1 -C 10 alkyl and the other two are linked together to form a C 4 -C 6 alkylene,
one of R 4 , R 5 and R 6 is selected from the group consisting of C 1 -C 10 alkyl and the other two are linked together to form a C 4 -C 6 alkylene, and
n is an integer of 3 to 10.
7 . The process according to claim 1 , wherein the organic structure directing agent is selected from the group consisting of the compounds containing a diquaternary ammonium cation of formula (I),
(R 1 R 2 R 3 )N + (CH 2 ) n N + (R 4 R 5 R 6 ) (I)
in which R 1 , R 2 , R 3 , R 4 , R 5 and R 6 , independently from each other, are selected from the group consisting of C 1 -C 6 alkyl, and n is an integer of 4 to 7.
8 . The process according to claim 1 , wherein the organic structure directing agent is selected from the group consisting of the compounds containing a diquaternary ammonium cation of formula (I),
(R 1 R 2 R 3 )N + (CH 2 ) n N + (R 4 R 5 R 6 ) (I)
in which R 1 , R 2 , R 3 , R 4 , R 5 and R 6 are the same and selected from the group consisting of C 1 -C 6 alkyl, and n is 5, 6 or 7.
9 . The process according to claim 1 , wherein the organic structure directing agent is selected from the group consisting of the compounds containing a diquaternary ammonium cation of formula (I),
(R 1 R 2 R 3 )N + (CH 2 ) n N + (R 4 R 5 R 6 ) (I)
in which each of R 1 , R 2 , R 3 , R 4 , R 5 and R 6 is methyl, ethyl or propyl, and n is 5, 6 or 7.
10 . The process according to claim 1 , wherein the organic structure directing agent is N,N,N,N′,N′,N′-hexaethyl-1,5-pentanediammonium.
11 . The process according to claim 1 , wherein the mixture in step (1) further comprises at least one source for alkali metal and/or alkaline earth metal cation.
12 . The process according to claim 11 , wherein the mixture provided in step (1) comprises at least one source for alkali metal and has an AM:YO 2 molar ratio of the at least one alkali metal to the source(s) for YO 2 calculated as YO 2 in the range of from 0.01 to 1.0.
13 . The process according to claim 12 , wherein the first zeolite material is a zeolite having an MFI framework structure, and the AM:YO 2 molar ratio of the at least one alkali metal to the source(s) for YO 2 calculated as YO 2 is in the range of 0.51 to 0.65.
14 . The process according to claim 12 , wherein the first zeolite material is zeolite having a CHA framework structure, and the AM:YO 2 molar ratio of the at least one alkali metal to the source(s) for YO 2 calculated as YO 2 is in the range of 0.56 to 0.64.
15 . The process according to claim 1 , further comprising (3) calcining the second zeolite material having an AFX framework structure.
16 . The process according to claim 1 , further comprising (4) exchanging one or more of ionic non-framework elements contained in the zeolite material obtained in step (2) or (3) to H + and/or NH 4 + .
17 . The process according to claim 1 , further comprising (5) loading a promoter metal cation on and/or in the zeolite material obtained in step (3) or (4).
18 . A process for preparing a zeolite material having an AFX framework structure comprising X 2 O 3 and YO 2 via interzeolite conversion, the process comprising
(1) providing a mixture comprising a first zeolite material having a non-FAU framework structure comprising X 2 O 3 and YO 2 and an organic structure directing agent selected from the group consisting of diquaternary ammonium cation containing compounds, wherein the first zeolite material acts as sources for X 2 O 3 and YO 2 , and
(2) heating the mixture from (1) to form a second zeolite material having an AFX framework structure comprising X 2 O 3 and YO 2 ,
wherein X is a trivalent element and Y is a tetravalent element,
wherein when the first zeolite material is a zeolite having a CHA framework structure, the organic structure directing agent is not 1,4-bis(1,4-diazabicyclo[2.2.2]octane)butyl dihydroxide, and
wherein the organic structure directing agent is N,N,N,N′,N′,N′-hexaethyl-1,5-pentanediammonium.
19 . A process for preparing a zeolite material having an AFX framework structure comprising X 2 O 3 and YO 2 via interzeolite conversion, the process comprising
(1) providing a mixture comprising a first zeolite material having a non-FAU framework structure comprising X 2 O 3 and YO 2 and an organic structure directing agent selected from the group consisting of diquaternary ammonium cation containing compounds, wherein the first zeolite material acts as sources for X 2 O 3 and YO 2 , and
(2) heating the mixture from (1) to form a second zeolite material having an AFX framework structure comprising X 2 O 3 and YO 2 ,
wherein X is a trivalent element and Y is a tetravalent element, and
wherein the organic structure directing agent is N,N,N,N′,N′,N′-hexaethyl-1,5-pentanediammonium.