Device and method for manufacturing optical fiber ribbon
An optical fiber ribbon manufacturing device comprising: a tape die 20 for coating a plurality of single-core coated optical fibers 2 with a photocurable resin; a split die 30 for forming a split portion in the photocurable resin present between the single-core coated optical fibers; and a light irradiation device 40 for irradiating the photocurable resin with light to cure the photocurable resin, wherein both the tape die 20 and the split die 30 are temperature-controlled or only the split die 30 is temperature-controlled, a temperature of the tape die 20 is higher than a temperature of the split die 20 , and the temperature of the split die 20 is lower than the temperature of the tape die 30.
1. An optical fiber ribbon manufacturing method comprising:
a first step of coating a plurality of single-core coated optical fibers with a photocurable resin;
a second step of forming a split portion in the photocurable resin present between all of the single-core coated optical fibers; and
a third step of irradiating the photocurable resin with light to cure the photocurable resin,
wherein, in the first step and the second step, both a tape die used in the first step and a split die used in the second step are temperature-controlled a temperature of the tape die used in the first step is set higher than a temperature of the split die used in the second step, and the temperature of the split die used in the second step is set lower than the temperature of the tape die used in the first step,
wherein the photocurable resin has a 4.7-8.8 Pa·s viscosity at 25° C., and
wherein a temperature difference between the tape die and the split die is set to 2-25° C.
2. The optical fiber ribbon manufacturing method according to claim 1 ,
wherein the temperature of the tape die used in the first step is set to 30-50° C., and
wherein the temperature of the split die used in the second step is set to 25-45° C.
3. The optical fiber ribbon manufacturing method according to claim 1 ,
wherein the photocurable resin is an epoxy acrylate-based photocurable resin or a urethane acrylate-based photocurable resin.