MODIFIED SILICON MATERIAL AND PREPARATION METHOD THEREOF, NEGATIVE ELECTRODE MATERIAL
This application provides a modified silicon material with a core-shell structure, a method for preparing a modified silicon material, a negative electrode active material, a negative electrode plate, a secondary battery, a battery module, a battery pack, and an electric apparatus. The modified silicon material with a core-shell structure includes an inner core, a first coating layer that wraps the inner core, and a second coating layer that wraps the first coating layer, where the inner core is elemental silicon and/or a silicon alloy; the first coating layer includes a silicon-oxygen compound; the second coating layer includes lithium fluoride, lithium carbonate, and carbon; and a weight ratio of element lithium to element carbon in the modified silicon material is 6% to 52%. The modified silicon material of this application has high gram capacity and sound conductivity, so that a battery has high first-cycle coulombic efficiency and sound cycling performance.
1 . A modified silicon material with a core-shell structure, comprising an inner core, a first coating layer that wraps the inner core, and a second coating layer that wraps the first coating layer, wherein the inner core is elemental silicon and/or a silicon alloy; the first coating layer comprises a silicon-oxygen compound; the second coating layer comprises lithium fluoride, lithium carbonate, and carbon; and a weight ratio of element lithium to element carbon in the modified silicon material is 6% to 52%, and optionally, 6.5% to 50%.
2 . The modified silicon material according to claim 1 , wherein the second coating layer further comprises lithium hydroxide.
3 . The modified silicon material according to claim 1 , wherein the silicon-oxygen compound is SiO x , wherein 0<x<2, and optionally, 0.3≤x≤1.5.
4 . The modified silicon material according to claim 1 , wherein the second coating layer contains:
0.1% to 2.9% lithium fluoride;
0.005% to 3.8% lithium carbonate;
0.15% to 3% carbon; and
0% to 0.07% lithium hydroxide.
5 . The modified silicon material according to claim 1 , wherein a particle size D v 50 of the modified silicon material is 1 μm to 3.5 μm, and optionally, 1.1 μm to 3 μm.
6 . The modified silicon material according to claim 1 , wherein a specific surface area of the modified silicon material is 5.5 m 2 /g to 14 m 2 /g, and optionally, 6 m 2 /g to 13 m 2 /g.
7 . The modified silicon material according to claim 1 , wherein a quantity of pores in a single particle of the modified silicon material is less than 10, and a pore diameter of the pore is not less than 50 nm.
8 . The modified silicon material according to claim 1 , wherein the modified silicon material contains 0.1% to 3%, and optionally, 0.2% to 2% element fluorine by weight.
9 . The modified silicon material according to claim 1 , wherein the modified silicon material contains 0.2% to 3%, and optionally, 0.3% to 2.8% element carbon by weight.
10 . The modified silicon material according to claim 1 , wherein the silicon alloy is selected from at least one of a ferrosilicon alloy, a silicon aluminum alloy, a silicon manganese alloy, a silicon tin alloy, and a silicon germanium alloy.
11 . The modified silicon material according to claim 1 , wherein thickness of the first coating layer is 1 nm to 8 nm.
12 . The modified silicon material according to claim 1 , wherein thickness of the second coating layer is 5 nm to 45 nm.
13 . A method for preparing a modified silicon material, comprising the following steps:
(1) heat-treating an inner core in an oxygen-containing atmosphere to obtain a pretreatment, wherein the inner core is elemental silicon and/or a silicon alloy;
(2) mixing the pretreatment, PVDF, a lithium-containing compound, and a solvent, wherein the lithium-containing compound is lithium carbonate and/or lithium hydroxide; and
(3) subjecting the mixture to drying, roasting, cooling, crushing, and sieving in sequence to obtain a modified silicon material.
14 . The method according to claim 13 , wherein in step (1), the heat treating is performed at 200° C. to 400° C. for 0.5 to 3 hours.
15 . The method according to claim 13 , wherein in step (3), the roasting is performed in an inert atmosphere at a temperature of 800° C. to 1000° C., and optionally, for a duration of 3 to 5 hours.
16 . The method according to claim 13 , wherein in step (3), the dried material is preheated at 300° C. to 500° C. for 1 to 2 hours before the roasting.
17 . The method according to claim 13 , wherein in step (2), a weight ratio of the PVDF, the lithium-containing compound, and the pretreatment is 1:(0.1-2):(13-155).
18 . A negative electrode active material, which is the modified silicon material according to claim 1 .
19 . A negative electrode plate comprising the negative electrode active material according to claim 18 .
20 . A secondary battery comprising the negative electrode plate according to claim 19 .