Method of making a microporous material
A method for producing a microporous material comprising the steps of: providing an ultrahigh molecular weight polyethylene (UHMWPE); providing a filler; providing a processing plasticizer; adding the filler to the UHMWPE in a mixture being in the range of from about 1:9 to about 15:1 filler to UHMWPE by weight; adding the processing plasticizer to the mixture; extruding the mixture to form a sheet from the mixture; calendering the sheet; extracting the processing plasticizer from the sheet to produce a matrix comprising UHMWPE and the filler distributed throughout the matrix; stretching the microporous material in at least one direction to a stretch ratio of at least about 1.5 to produce a stretched microporous matrix; and subsequently calendering the stretched microporous matrix to produce a microporous material which exhibits improved physical and dimensional stability properties over the stretched microporous matrix.
1. A battery separator microporous material made by a process comprising:
mixing ultra-high molecular weight polyethylene (UHMWPE), siliceous filler and processing plasticizer together to form a mixture, having a weight ratio of siliceous filler to UHMWPE of from 1:9 to 15:1 by weight and having the ratio of siliceous filler to processing plasticizer be 1:15 to 3:1 by weight;
extruding said mixture to form a sheet;
calendering said sheet;
extracting all or part of said processing plasticizer from said sheet to produce a matrix comprising UHMWPE and said particulate siliceous filler, the siliceous filler being distributed throughout said matrix, to produce a microporous matrix sheet;
stretching said microporous matrix sheet in at least one stretching direction to a stretch ratio of at least 1.5 to produce a stretched microporous matrix sheet; and
calendering said stretched microporous matrix sheet under conditions to form the battery separator microporous material having pores having a diameter from 0.01 micrometers to 0.1 micrometer, and wherein the siliceous filler constitutes from 5 percent to 95 percent by weight of the battery separator microporous material,
wherein the battery separator microporous material has an MD tensile strength from 40 to 65 N/mm 2 , and a TD tensile strength from 28 to 55 N/mm 2 .
2. The battery separator microporous material of claim 1 , wherein the siliceous filler constitutes from 45 percent to 95 percent by weight of the battery separator.
3. The battery separator microporous material of claim 1 , wherein the siliceous filler constitutes from 55 percent to 80 percent by weight of the battery separator.
4. The battery separator microporous material of claim 1 , wherein the siliceous filler constitutes from 61.1 percent to 80 percent by weight of the battery separator.
5. The battery separator microporous material of claim 1 , wherein the siliceous filler is selected from silica, precipitated silica, silica gel, or fumed silica.
6. The battery separator microporous material of claim 1 , wherein the siliceous filler is silica.
7. The battery separator microporous material of claim 1 , wherein in addition to the siliceous filler, a particulate water-insoluble filler is also present.
8. The battery separator microporous material of claim 7 , wherein the particulate water-insoluble filler is one or more selected from carbon black, activated carbon, carbon fibers, charcoal, graphite, titanium oxide, iron oxide, copper oxide, zinc oxide, lead oxide, tungsten, antimony oxide, zirconia, magnesia, alumina, molybdenum disulfide, zinc sulfide, barium sulfate, strontium sulfate, calcium carbonate, and magnesium carbonate.
9. The battery separator microporous material of claim 8 , wherein the particulate water-insoluble filler includes carbon material.
10. The battery separator microporous material of claim 9 , wherein the carbon material is at least one of carbon black, activated carbons, and carbon fibers.
11. The battery separator microporous material of claim 1 , having a wet out time less than 20 seconds.
12. The battery separator microporous material of claim 11 , having a wet out time less than 18 seconds.
13. The battery separator microporous material of claim 11 , having a wet out time less than 16 seconds.
14. The battery separator microporous material of claim 11 , having a wet out time less than 10 seconds.
15. The battery separator microporous material of claim 1 , having a tensile strength in the machine direction (MD) that is greater than 20 N/mm 2 .
16. The battery separator microporous material of claim 15 , having a tensile strength in the machine direction (MD) that is greater than 41 N/mm 2 .
17. The battery separator microporous material of claim 15 , having a tensile strength in the machine direction (MD) that is greater than 64 N/mm 2 .
18. The battery separator microporous material of claim 15 , having a tensile strength in the machine direction (MD) that is greater than 77 N/mm 2 .
19. The battery separator microporous material of claim 1 , having an electrical resistance of less than 130 mohm/mm 2 .
20. A battery comprising the battery separator microporous material of claim 1 .