NON-ASPHALT BASED SEALANT WITH HIGH ADHESION
A non-asphaltic sealant composition, and methods of producing and using the sealant composition, wherein the non-asphaltic sealant composition includes a sufficient amount of one or more polar, non-asphaltic base resins having functional groups for hydrogen bonding to provide high adhesion for sealing cracks and joints in polar concrete pavements and other polar substrates.
1 . A non-asphalt-based sealant composition having high adhesion for sealing cracks and joints in polar concrete pavements and other polar substrates, the non-asphalt-based sealant composition comprising:
A polar non-asphaltic sealant base blend comprising
one or more polar non-asphaltic base resins having functional groups for hydrogen bonding,
one or more processing oils,
one or more plasticizing materials, and
the one or more polar non-asphaltic base resins being present in the polar non-asphaltic sealant base blend in a total amount which both (i) is equivalent to an amount of at least 30% by weight of a total final weight of the non-asphalt-based sealant composition and (ii) causes the non-asphalt-based sealant composition to undergo hydrogen bonding when applied to polar substrates and
one or more elastomeric polymer materials.
2 . The non-asphalt-based sealant composition of claim 1 further comprising the functional groups for hydrogen bonding of the one or more polar non-asphaltic base resins being ester functional groups, hydroxyl functional groups, carboxylic acid functional groups, and/or amine functional groups.
3 . The non-asphalt-based sealant composition of claim 1 further comprising the total amount of the one or more polar non-asphaltic base resins in the polar non-asphaltic sealant base blend being an amount equivalent to an amount of from 35% to 65% by weight based upon the total final weight of the non-asphalt-based sealant composition.
4 . The non-asphalt-based sealant composition of claim 1 further comprising the one or more polar non-asphaltic base resins comprising one or more polar rosin esters.
5 . The non-asphalt-based sealant composition of claim 4 further comprising the one or more polar rosin esters being (i) one or more pine-based pentaerythritol ester resins, (ii) one or more pine-based glycerol ester resins, and/or (iii) one or more other pine-based ester resins esterified using glycols bearing hydroxyl functionality.
6 . The non-asphalt-based sealant composition of claim 4 further comprising the one or more polar rosin esters being one or more pine-based pentaerythritol ester resins.
7 . The non-asphalt-based sealant composition of claim 1 further comprising the one or more polar non-asphaltic base resins comprising (i) one or more polyurethane resins derived from a reaction of one or more isocyanate compounds with a flexible chain extender; (ii) one or more epoxy resins based on a diglycidyl ether of Bisphenol-A (DGEBA); (iii) one or more polyurethane resins derived from DGEBA that is modified with flexible diamines or flexible diols; and/or (iv) one or more silane-based resins having silanol functionality.
8 . The non-asphalt-based sealant composition of claim 1 further comprising:
the one or more processing oils being present in the polar non-asphaltic sealant base blend in a total amount which is equivalent to an amount of from 35% to 65% by weight based upon the total final weight of the non-asphalt-based sealant composition and
the one or more plasticizing materials being present in the polar non-asphaltic sealant base blend in a total amount which is equivalent to an amount of from 0.5% to 6% by weight based upon the total final weight of the non-asphalt-based sealant composition.
9 . The non-asphalt-based sealant composition of claim 8 further comprising the one or more processing oils comprising one or more aromatic, naphthenic, paraffinic, and/or vegetable oils, the one or more processing oils having a total aromatic content of at least 40% by weight based on a total weight of the one or more processing oils.
10 . The non-asphalt-based sealant composition of claim 8 further comprising the one or more plasticizing materials comprising one or more epoxidized esters of one or more vegetable oils.
11 . The non-asphalt-based sealant composition of claim 8 further comprising the one or more plasticizing materials comprising an epoxy functionalized methyl ester of soybean oil.
12 . The non-asphalt-based sealant composition of claim 8 further comprising the one or more plasticizing materials being selected from: esters derived from vegetable oil fatty acids; esters and diesters derived from esterification of fatty alcohols and carboxylic acids, or from esterification of alcohols with fatty acids; hydrogenated and non-hydrogenated aromatic oils and distillates; hydrogenated and non-hydrogenated naphthenic oils and distillates; and paraffinic oils and distillates.
13 . The non-asphalt-based sealant composition of claim 1 further comprising the one or more elastomeric polymer materials being present in the non-asphalt-based sealant composition in a total amount of from 2% to 20% by weight based upon the total final weight of the non-asphalt-based sealant composition.
14 . The non-asphalt-based sealant composition of claim 13 further comprising the one elastomeric polymer materials being selected from: radial and/or linear styrene butadiene styrene (SBS) block copolymers; styrene butadiene copolymers; styrene isoprene copolymers; styrene isoprene styrene (SIS) block copolymers; ethylene vinyl acetate (EVA); ethylene-propylene-diene monomer rubber (EPDM) formed by copolymerization of ethylene and propylene with monomers which disrupt crystallinity; butyl acrylate; glycidyl methacrylate; other polymers derived from copolymerization of ethylene with acrylic monomers; and combinations thereof.
15 . The non-asphalt-based sealant composition of claim 13 further comprising the one elastomeric polymer materials being a SBS polymer and/or a SIS polymer.
16 . The non-asphalt-based sealant composition of claim 1 further comprising one or more color-neutralizing materials which at least partially neutralize a non-white shade or color of the polar non-asphaltic sealant base blend, the one or more color-neutralizing materials comprising titanium dioxide in an amount which is from 3% to 20% by weight based upon the total final weight of the non-asphalt-based sealant composition.
17 . The non-asphalt-based sealant composition of claim 1 further comprising one or more pigment materials which impart a desired end color to the polar non-asphaltic sealant base blend in a total amount of from 0.1% to about 6% by weight based upon the total final weight of the non-asphalt-based sealant composition.
18 . The non-asphalt-based sealant composition of claim 17 further comprising the one or more pigment materials comprising Gilsonite powder.
19 . The non-asphalt-based sealant composition of claim 1 further comprising one or more inorganic filler materials in a total amount of from 6.5% to 24% by weight based upon the total final weight of the non-asphalt-based sealant composition.