Humidity and sag resistant building panel
Described herein is a stain and sag resistant acoustic building panel comprising a porous body formed from building material and latex binder, wherein the building material may include fibers and filler and at one of the building materials has been pre-treated with a charge-modifying component, thereby enhancing the sag-resistance of the building panel.
1. An acoustic ceiling panel comprising:
a porous body having an upper surface opposite a lower surface and at least one side surface extending between the upper surface and the lower surface, the porous body comprising a latex binder and a fibrous material;
a non-woven scrim having a first major surface opposite a second major surface, the second major surface of the non-woven scrim adjacent to the lower surface of the porous body; and
a coating in a dry state applied to the first major surface of the non-woven scrim in an amount ranging from about 5 g/m 2 to about 40 g/m 2 , the coating comprising:
a first hydrophobic component;
inorganic filler, and
binder,
wherein the hydrophobic component is present in an amount ranging from about 0.1 wt. % to about 10 wt. % based on a total dry weight of the coating, and wherein the hydrophobic component comprises at least one of a wax, a silicone, or a fluoro-containing additive.
2. The acoustic ceiling panel according to claim 1 , wherein the latex is present in a non-zero amount ranging up to about 15 wt. % based on the total dry weight of the porous body.
3. The acoustic ceiling panel according to claim 1 , wherein the first hydrophobic component comprises a siloxane emulsion.
4. The acoustic ceiling panel according to claim 1 , wherein the first hydrophobic component comprises an emulsion blend of silicon and siloxane.
5. The acoustic ceiling panel according to claim 1 , wherein the non-woven scrim is hydrophobic.
6. The acoustic ceiling panel according to claim 1 , wherein the coating is applied to the non-woven scrim in an amount ranging from about 5 g/m2 to about 40 g/m2.
7. The acoustic ceiling panel according to claim 1 , wherein the coating is discontinuous.
8. The acoustic ceiling panel according to claim 1 , wherein the fibrous material is pre-treated with a charge-modifying component.
9. The acoustic ceiling panel according to claim 1 , wherein the charge-modifying component is present in an amount ranging from about 0.1 wt. % to about 2.5 wt. % based on the total weight of the porous body.
10. The acoustic ceiling panel according to claim 9 , wherein the charge-modifying component is cationic.
11. The acoustic ceiling panel according to claim 9 , wherein the charge-modifying component is selected from the group consisting of aluminum sulfate, poly(diallyldimethylammonium chloride), and combinations thereof.
12. The acoustic ceiling panel according to claim 1 , wherein the fibrous material is an inorganic fiber selected from the group consisting of mineral wool, fiberglass, and combinations thereof.
13. An acoustic ceiling panel comprising
a porous body having an upper surface opposite a lower surface and at least one side surface extending between the upper surface and the lower surface, the porous body comprising a latex binder and a fibrous material;
a non-woven scrim having a first major surface opposite a second major surface, the second major surface of the non-woven scrim adjacent to the lower surface of the porous body;
a coating applied to the first major surface of the non-woven scrim, the coating comprising a first hydrophobic component; and
a back coating is applied to the upper surface of the body, the back coating comprising a hygroscopic component and a second hydrophobic component.
14. A coated non-woven scrim comprising:
a non-woven scrim comprising fiberglass, wherein the non-woven scrim is hydrophobic; and
a coating applied to the non-woven scrim, wherein the coating is present in a dry state in an amount ranging from about 5 g/m2 to about 40 g/m2, wherein the coating comprises
a hydrophobic component,
inorganic filler, and
binder,
wherein the hydrophobic component is present in an amount ranging from about 0.1 wt. % to about 10 wt. % based on a total dry weight of the coating, and wherein the hydrophobic component comprises at least one of a wax, a silicone, or a fluoro-containing additive.