Method for manufacturing a fused metal sight window with a high flow temperature optical material
A method for manufacturing a fused metal sight window that melts the metal of the frame around the window, instead of the traditional method of melting the window into the frame. Since most of the superior optical transparent materials (such as fused silica, sapphire, YAG, ALON, diamond, fused quartz and magnesium fluoride) have a melting point higher than most metals, it was not previously possible to create fused metal sight windows with these materials. By melting the frame onto the window, many new combinations of metals and optical materials may be used while retaining the strength of the sight window that results from fusing the metal and the window.
1. A method for manufacturing a fused metal sight window with a high flow temperature optical material, comprising:
obtaining a window, wherein
said window comprises an optical material that can be heated to a threshold temperature at or below which said optical material does not flow and is not damaged; and
said window comprises an outer window edge;
obtaining a frame, wherein
said frame comprises a metal having a melting temperature below said threshold temperature; and
said frame comprises an inner frame edge and an outer frame edge, wherein said outer window edge fits inside said inner frame edge;
placing said window inside said frame;
heating said window and said frame to a temperature greater than or equal to said melting temperature of said metal of said frame and less than or equal to said threshold temperature, maintaining said window and said frame heating temperature for a period of time until said inner frame edge flows onto said outer window edge and said metal of said frame at said inner frame edge fuses with said optical material of said window at said outer window edge, and wherein the optical material of the window will not flow and will not be damaged; and,
cooling said window and said frame to compress the window as the metal contracts around the window and applies compressive force to strengthen the window and to form a fused metal sight window.
2. The method for manufacturing the fused metal sight window with the high flow temperature optical material of claim 1 , wherein said frame is a ring.
3. The method for manufacturing the fused metal sight window with the high flow temperature optical material of claim 1 , wherein said frame is a geometrical shape other than a ring.
4. The method for manufacturing the fused metal sight window with the high flow temperature optical material of claim 1 , wherein said optical material comprises a crystalline optical material.
5. The method for manufacturing the fused metal sight window with the high flow temperature optical material of claim 1 , wherein said optical material comprises one or more of fused silica, aluminosilicate, borosilicate glass, YAG, ALON, sapphire, zinc selenide, zinc sulfide, quartz crystal, fused quartz, diamond, and magnesium fluoride.
6. The method for manufacturing the fused metal sight window with the high flow temperature optical material of claim 1 , wherein
said optical material comprises sapphire; and,
said metal comprises one or more of stainless steel, a nickel-based alloy, copper, brass, gold, titanium, platinum, and rhodium.
7. The method for manufacturing the fused metal sight window with the high flow temperature optical material of claim 1 , further comprising wherein said metal of said frame is a first metal and said melting temperature is a first melting temperature, obtaining an outer housing, wherein
said outer housing comprises a second metal having a second melting temperature greater than said first melting temperature;
said outer housing comprises an inner housing edge wherein said outer frame edge fits inside said inner housing edge; and,
placing said frame and said window inside said outer housing, such that said frame is sandwiched between the window and the outer housing; and,
wherein said heating said window and said frame, and further comprises heating said outer housing to said temperature greater than or equal to said first melting temperature of said first metal of said frame, less than or equal to said threshold temperature, and less than said second melting temperature of the outer housing, and wherein said maintaining said window and said frame heating temperature further comprises maintaining said outer housing heating temperature which occurs until
said outer frame edge flows onto said inner housing edge and said first metal of said frame fuses with said second metal of said outer housing;
wherein said cooling further comprising cooling said outer housing to form said fused metal sight window.
8. The method for manufacturing the fused metal sight window with the high flow temperature optical material of claim 7 , wherein
said optical material comprises zinc selenide;
said second metal comprises stainless steel; and,
said metal comprises a transition metal.
9. The method for manufacturing the fused metal sight window with the high flow temperature optical material of claim 7 , wherein
said inner frame edge flows onto said outer window edge without using capillary action; and,
said outer frame edge flows onto said inner housing edge without using capillary action.
10. The method for manufacturing the fused metal sight window with the high flow temperature optical material of claim 7 , wherein joining said window, said frame, and said outer housing to form said fused metal sight window does not comprise brazing and does not comprise soldering.
11. A method for manufacturing a fused metal sight window with a high flow temperature optical material, comprising:
obtaining a window, wherein
said window comprises an optical material that can be heated to a threshold temperature at or below which said optical material does not flow and is not damaged;
said optical material comprises one or more of fused silica, aluminosilicate, borosilicate glass, YAG, ALON, sapphire, zinc selenide, zinc sulfide, quartz crystal, fused quartz, diamond, magnesium fluoride;
said window comprises an outer window edge; and,
said outer window edge comprises a circular shape;
obtaining a frame, wherein
said frame comprises a metal having a melting temperature below said threshold temperature;
said metal comprises one or more of stainless steel, a nickel-based alloy, copper, brass, gold, titanium, platinum, and rhodium;
said frame comprises an inner frame edge and an outer frame edge, wherein said outer window edge fits inside said inner frame edge; and,
said inner frame edge comprises a circular shape;
placing said window inside said frame;
heating said window and said frame to a temperature greater than or equal to said melting temperature of said metal of said frame and less than or equal to said threshold temperature, maintaining said window and said frame heating temperature for a period of time until said inner frame edge flows onto said outer window edge and said metal of said frame at said inner frame edge fuses with said optical material of said window at said outer window edge, and wherein the optical material of the window will not flow and will not be damaged; and,
cooling said window and said frame to compress the window as the metal contracts around the window and applies compressive force to strengthen the window and to form a fused metal sight window.
12. A method for manufacturing a fused metal sight window with a high flow temperature optical material, comprising:
obtaining a window, wherein
said window comprises an optical material that can be heated to a threshold temperature at or below which said optical material does not flow and is not damaged; and
said window comprises an outer window edge;
obtaining a frame, wherein
said frame comprises a first metal having a first melting temperature below said threshold temperature; and
said frame comprises an inner frame edge and an outer frame edge, wherein said outer window edge fits inside said inner frame edge;
obtaining an outer housing wherein
said outer housing comprises a second metal having a second melting temperature greater than said first melting temperature;
said outer housing comprises an inner housing edge wherein said outer frame edge fits inside said inner housing edge;
placing said window inside said frame and placing said frame and said window inside said outer housing, such that said frame is sandwiched between the window and the outer housing;
heating said window, said frame and said outer housing to a temperature greater than or equal to said first melting temperature of said first metal, less than or equal to said threshold temperature, and less than said second melting temperature of the outer housing,
maintaining said window, said frame and said outer housing heating temperature for a period of time until
said inner frame edge flows onto said outer window edge and said first metal of said frame at said inner frame edge fuses with said optical material of said window at said outer window edge, and wherein the optical material of the window will not flow and will not be damaged such that a state of the window is unchanged; and
said outer frame edge flows onto said inner housing edge and said first metal of said frame fuses with said second metal of said outer housing;
thereby joining the window to the outer housing and joining said window, said frame and said outer housing;
cooling said window said frame and said outer housing to compress the window as the first metal contracts around the window and applies compressive force to strengthen the window and to form a fused metal sight window;
wherein said joining said window, said frame and said outer housing to form said fused metal sight window does not comprise brazing and does not comprise soldering.