IP Library Granted Patent US 12,559,827
Granted Patent B2
US 12,559,827 · App. 18/157,539 · Granted Feb 24, 2026

Processes for making metal rings formed from beryllium-copper alloys

Inventors: Jeffrey M. Schirm (Perrysburg, OH); Christopher W. Damschroder (Elmore, OH); Edward B. Longenberger (Perrysburg, OH); Jeffrey A. McBride (Luckey, OH)
Assignee: MATERION CORPORATION
C22F1/08B21K1/761C22C9/00C22F1/002
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,559,827
App. No.
18/157,539
Granted
Feb 24, 2026
Kind
B2
Abstract

Processes are disclosed for forming beryllium-copper metal rings having a fine and uniform grain structure. A raw BeCu casting is pre-forged and turned to form a BeCu billet. The BeCu billet is subjected to various heat treatment and cooling cycles to obtain/maintain combinations of advantageous material properties. Generally, the BeCu billet is preheated, hot worked via forging, heated again, hot worked again via ring rolling followed by air cooling, solution annealed followed by quenching, and heated a final time followed by air cooling.

Claims (47)

1 . A process for making a metal ring from a BeCu alloy, comprising:

preheating a BeCu alloy billet at a temperature of about 800° C. to about 850° C., wherein the BeCu alloy comprises about 1.6 wt % to about 2.0 wt % beryllium;

forging the billet into a ring-shaped preform at a temperature of about 750° C. to about 850° C.;

soaking the preform at a temperature of about 815° C. to about 835° C.;

ring rolling the preform at a temperature of about 750° C. to about 850° C. to form a ring having a wall thickness, wherein the ring rolling reduces the wall thickness by at least 50%;

solution annealing the ring at a temperature of about 780° C. to about 800° C., immediately followed by quenching the ring, wherein the solution annealing is performed for a period of about 30 minutes for approximately every 25 mm of wall thickness of the ring; and

heat treating the ring at a temperature of about 385° C. to about 400° C.

2 . The process of claim 1 , wherein the preheating occurs for a period of at least 8 hours.

3 . The process of claim 1 , wherein the soaking occurs for a minimum period of 2 hours.

4 . The process of claim 3 , wherein the soaking is performed for a period of at least 8 hours if the preform has cooled to a temperature of about 600° C. or less.

5 . The process of claim 1 , wherein the solution annealing occurs for a period of at least 1.5 hours.

6 . The process of claim 1 , wherein the heat treating occurs for a period of about 3 hours.

7 . The process of claim 6 , further comprising starting the about 3 hour period at a temperature of about 393° C., raising the temperature to about 400° C., and heat treating the ring at the about 400° C. temperature for the remaining period of time.

8 . The process of claim 1 , wherein the preheating and soaking are each performed at a temperature of about 820° C.

9 . The process of claim 1 , wherein the ring rolling reduces the wall thickness by at least 70%.

10 . The process of claim 1 , further comprising air cooling the ring after both the ring rolling and the heat treating.

11 . A process for making a metal ring comprising:

providing a billet made from a BeCu alloy comprising about 1.6 wt % to about 2.0 wt % beryllium;

preheating the billet at a temperature of about 800° C. to about 850° C. for a period of at least 8 hours;

forming a ring-shaped preform from the billet at a temperature of about 750° C. to about 850° C.;

soaking the preform at a temperature of about 815° C. to about 835° C. for a period of about 2 hours to about 8 hours;

ring rolling the preform at a temperature of about 750° C. to about 850° C. until the preform has a substantially uniform wall thickness, followed by air cooling;

solution annealing the preform at a temperature of about 780° C. to about 800° C. for a period of at least 1.5 hours, immediately followed by quenching in a quench medium, wherein the solution annealing is performed for a period of about 30 minutes for approximately every 25 mm of wall thickness of the ring;

heat treating the preform at a temperature of about 385° C. to about 400° C. for a period of about 3 hours, followed by air cooling; and,

mechanically machining the preform to form the metal ring having a desired shape.

12 . The process of claim 11 , wherein the BeCu alloy billet comprises from about 1.8 wt % to about 2.0 wt % beryllium.

13 . The process of claim 11 , wherein the BeCu alloy billet further comprises from about 0.2 wt % to about 0.3 wt % cobalt.

14 . The process of claim 11 , wherein the BeCu alloy billet comprises:

about 1.8 wt % to about 2.0 wt % beryllium;

an amount of nickel, cobalt, and optionally iron such that the sum of (nickel+cobalt) is about 0.2 wt % or higher, and the sum of (nickel+cobalt+iron) is about 0.6 wt % or less;

about 0.2 wt % to about 0.6 wt % lead; and

balance copper.

15 . The process of claim 1 , wherein the BeCu alloy billet comprises from about 1.8 wt % to about 2.0 wt % beryllium.

16 . The process of claim 1 , wherein the BeCu alloy billet further comprises from about 0.2 wt % to about 0.3 wt % cobalt.

17 . The process of claim 1 , wherein the BeCu alloy billet comprises:

about 1.8 wt % to about 2.0 wt % beryllium;

an amount of nickel, cobalt, and optionally iron such that the sum of (nickel+cobalt) is about 0.2 wt % or higher, and the sum of (nickel+cobalt+iron) is about 0.6 wt % or less;

about 0.2 wt % to about 0.6 wt % lead; and

balance copper.

18 . The process of claim 1 , wherein the BeCu alloy billet comprises:

about 1.6 wt % to about 2.0 wt % beryllium;

about 0.2 wt % to about 0.3 wt % cobalt; and

balance copper.

19 . The process of claim 1 , wherein the BeCu alloy billet comprises:

about 1.8 wt % to about 2.0 wt % beryllium;

an amount of nickel, cobalt, and optionally iron such that the sum of (nickel+cobalt) is about 0.2 wt % or higher, and the sum of (nickel+cobalt+iron) is about 0.6 wt % or less; and

balance copper.

Assignments (2)
CONFIRMATORY GRANT OF SECURITY INTEREST IN UNITED STATES PATENTS Recorded Jun 26, 2025
From: MATERION CORPORATION
To: JPMORGAN CHASE BANK, N.A., AS ADMINISTRATIVE AGENT
Reel/Frame 071751/0085 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jan 20, 2023
From: SCHIRM, JEFFREY M.; DAMSCHRODER, CHRISTOPHER W.; LONGENBERGER, EDWARD B.; MCBRIDE, JEFFREY A.
To: MATERION CORPORATION
Reel/Frame 062441/0768 →
Continuity (3)
Division 16762175
Provisional Application 62587533 · Nov 17, 2017
Related Publication 20230151474A1 · May 18, 2023
References Cited (29)
US 4179314A · Wikle · 1979 [cited by applicant]
US 4425168A · Goldstein et al. · 1984 [cited by applicant]
US 4579603A · Woodard et al. · 1986 [cited by applicant]
US 4792365A · Matsui et al. · 1988 [cited by applicant]
US 5354388A · Nojiri et al. · 1994 [cited by applicant]
US 5564490A · Liebermann et al. · 1996 [cited by applicant]
US 5651844A · Longenberger · 1997 [cited by examiner]
US 5842511A · Raybould · 1998 [cited by examiner]
US 7510615B2 · Rode et al. · 2009 [cited by applicant]
US 20040112566A1 · Myojin · 2004 [cited by examiner]
US 20040216817A1 · Harkness · 2004 [cited by applicant]
US 20100006191A1 · Wetzel et al. · 2010 [cited by applicant]
CN 1188436A · 1998 [cited by applicant]
CN 101981211A · 2011 [cited by applicant]
CN 102212712A · 2011 [cited by applicant]
CN 102383078A · 2012 [cited by applicant]
CN 102876918A · 2013 [cited by applicant]
CN 103100715A · 2013 [cited by applicant]
CN 103436829A · 2013 [cited by examiner]
CN 104769139A · 2015 [cited by applicant]
EP 0854200A1 · 1998 [cited by applicant]
RU 2168084C2 · 2001 [cited by applicant]
WO 2014069303A1 · 2014 [cited by applicant]
CN-103436829-A, machine translation. (Year: 2013). [cited by examiner]
Anonymous, “Guide to High Performance Alloys”, (Jan. 1, 2012), p. FP-82, Lamineries Matthey SA, Retrieved from the Internet: URL:www.matthey.ch/fileadmin/user_upload/brochure/Guide)_To_HP_Alloys.pdf XP055307616 [retriev… [cited by applicant]
Zheleznyak et al., “Nontraditional Technological Processes Mechanical Properties and Structure of Rolled Rings From Beryllium Bronze BrB2”, (Oct. 1, 1999), pp. 454-456 Retrieved from the Internet: URL:https:/link.spring… [cited by applicant]
Anonymous, “Characteristics for grade BrB2”, Database of Steel and Alloy (Marochnik) Retrieved from the Internet: URL:http://www.splav-kharkov.com/en/e_mat_start.php?name_id=1086#1 XP002790529 [retrieved on Apr. 11, 201… [cited by applicant]
Harness, et al., “Beryllium-Copper And Other Beryllium-Containing Alloys”, “Properties And Selection : Nonferrous Alloys and Special Purpose Materials”, pp. 403-423, (Jan. 1, 1990), ASM International, ASM, US, XP0020451… [cited by applicant]
Arthington, et al., Curvature control in radial-axial ring rolling, I FAC-PapersOn Line, vol. 49, Issue 20, 2016, pp. 244-249. (Year: 2016). [cited by applicant]