Dental material compositions for cleansing and removal of anionic contaminants from substrates and their methods of use
Compositions and methods useful for removing anionic contaminates and debris including phosphates from dental restorative substrates are disclosed.
1. A composition for removing anionic contaminants from dental restorative surfaces, comprising:
at least one metal trihalide salt;
at least one thickening agent;
at least colorant; and water
wherein the pH of the composition is between 2 and 4.
2. The composition of claim 1 , wherein the composition retains its chemical stability for more than 60 days without the formation of a visible precipitate.
3. The composition of claim 1 , wherein the at least one metal trihalide salt contains a metal element exhibiting an electronegativity value between 1.0 and 1.3.
4. The composition of claim 1 , wherein the at least one metal trihalide salt dissolves in water forming at least one metal cations, wherein the at least one metal cations has a high affinity for phosphate.
5. The composition of claim 1 , wherein the metal of the at least one metal trihalide salt has an atomic size between 125 pm and 215 pm.
6. The composition of claim 1 , wherein the at least one metal trihalide salt comprises a lanthanum salt.
7. The composition of claim 1 , wherein the at least one metal trihalide salt comprises lanthanum chloride hydrate.
8. The composition of claim 1 , wherein the at least one metal trihalide salt comprises lanthanum chloride hydrate at a concentration between 20% and 40%.
9. The composition of claim 1 , wherein the at least one thickening agent comprises polyvinyl alcohol.
10. The composition of claim 1 , wherein the at least one thickening agent comprises fumed silica.
11. The composition of claim 1 , further comprising a surfactant or blend of surfactants.
12. The composition of claim 1 , further comprising a humectant or humectants.
13. The composition of claim 1 , wherein the composition has a viscosity between 0.2 and 0.8 Pa·s.
14. The composition of claim 1 , wherein the colorant is added in sufficient quantity to provide visual contrast when applied to a dental restorative surface.
15. The composition of claim 1 , wherein the composition consists of: lanthanum chloride hydrate at a concentration of 28% (wt/wt), polyvinyl alcohol at a concentration of 3.2% (wt/wt), a blend of FD&C yellow #5-6 and red #40 at a concentration of 0.5% (wt/wt), and deionized water.
16. A method of cleaning a dental restorative surface, comprising:
applying a cleaning solution of claim 1 to a dental restoration surface;
allowing the cleaning solution to dwell on the dental restoration surface for a period of time; and
rinsing away the cleaning solution from the dental restoration surface,
wherein the pH of the cleaning solution is between 2 and 4.
17. The method of claim 16 , wherein, the cleaning solution does not require shaking prior to application to the dental restoration surface, wherein, the cleaning solution chemically removes substantially all phosphate contaminates from the dental restoration surface; and, wherein, the cleaning solution is chemically stable for at least 60 days without the formation of a visible precipitate.
18. The method of claim 16 , wherein the dwell time is between 10 and 30 seconds.
19. A dental restoration kit, comprising:
a cleaning composition of claim 1 ; and,
application tips or application brushes.
20. The kit of claim 19 further comprising a dental primer and a dental cement or a dental composite.