Thin aerogel materials
The present invention provides a fiber-reinforced aerogel material which can be used as insulation in thermal battery applications. The fiber-reinforced aerogel material is highly durable, flexible, and has a thermal performance that exceeds the insulation materials currently used in thermal battery applications. The fiber-reinforced aerogel insulation material can be as thin as 1 mm less, and can have a thickness variation as low as 2% or less. Also provided is a method for improving the performance of a thermal battery by incorporating a reinforced aerogel material into the thermal battery. Further provided is a casting method for producing thin fiber-reinforced aerogel materials.
1. A reinforced aerogel composition comprising:
an aerogel framework and a reinforcement material, the reinforced aerogel composition having a thickness of from 0.75 mm to 2 mm and a thickness variation of less than 15%.
2. The reinforced aerogel composition of claim 1 , wherein the reinforcement material comprises an open-cell foam reinforcement material, and a fiber reinforcement material.
3. The reinforced aerogel composition of claim 1 , wherein the reinforcement material comprises a fibrous reinforcement material comprising discrete fibers, a woven material, a non-woven material, a batting, a web, a mat, a felt, or a combination thereof.
4. The reinforced aerogel composition of claim 3 , wherein the fibrous reinforcement material comprises glass-based fibers.
5. The reinforced aerogel composition of claim 3 , wherein the fibrous reinforcement material comprises silica-based fibers.
6. The reinforced aerogel composition of claim 5 , wherein the reinforced aerogel composition has a thermal conductivity in a range of about 12 mW/mK and about 20 mW/mK.
7. The reinforced aerogel composition of claim 3 , wherein the fibrous reinforcement material comprises ceramic fibers.
8. The reinforced aerogel composition of claim 1 , wherein the thickness variation is less than 6%.
9. The reinforced aerogel composition of claim 1 , wherein the thickness variation is from 2% to less than 15%.
10. The reinforced aerogel composition of claim 1 , wherein the reinforced aerogel composition has a thermal conductivity of about 25 mW/mK or less.
11. The reinforced aerogel composition of claim 1 , wherein the reinforced aerogel composition has a thermal conductivity of about 50 mW/mK or less.
12. The reinforced aerogel composition of claim 11 , wherein the reinforced aerogel composition has a thermal conductivity of between about 12 mW/mK and about 50 mW/mK.
13. The reinforced aerogel composition of claim 1 , wherein the reinforced aerogel composition includes a silica-based framework.
14. The reinforced aerogel composition of claim 1 , wherein the reinforced aerogel composition includes an organic aerogel.
15. The reinforced aerogel composition of claim 1 , wherein the reinforced aerogel composition has a density in a range of about 0.60 g/cc and about 0.30 g/cc.
16. The reinforced aerogel composition of claim 1 , wherein the thickness is from 1 mm to 2 mm.
17. The reinforced aerogel composition of claim 1 , wherein the reinforced aerogel composition is a flexible aerogel blanket composition.
18. The reinforced aerogel composition of claim 1 , wherein the reinforced aerogel composition has a resilience of from 50% to 95%.
19. A battery comprising the aerogel reinforced composition of claim 1 .
20. A method of improving performance of a battery comprising incorporating the reinforced aerogel composition of claim 1 into the battery.