UHMWPE PASTE EXTRUDED TUBES
The disclosure generally relates to ultra high molecular weight poly(ethylene) (“UHMWPE”) tubes with an average wall thickness of 0.2 mm or less; a tensile stress at break greater than 40 MPa; and a storage modulus of greater than 500 MPa at 23° C. The disclosure further relates to preparing and using such tubes and to constructions (e.g., catheter constructions) and components thereof including such tubes.
1 . An Ultra High Molecular Weight Poly(ethylene) (UHMWPE) tube comprising:
a. an average wall thickness of 0.2 mm or less; and
b. a tensile stress at break greater than 40 MPa; and
c. a storage modulus of greater than 500 MPa at 23° C.
2 . The UHMWPE tube of claim 1 , wherein the UHMWPE tube is prepared via extrusion of a billet comprising lubricant and UHMWPE resin through an annular die.
3 . The UHMWPE tube of claim 2 , wherein the lubricant is selected from the group consisting of d-limonene, naphtha, Isopar G, Isopar M, or any combination thereof.
4 . The UHMWPE tube of claim 1 , wherein the UHMWPE tube is prepared via extrusion over a metallic or non-metallic wire or mandrel.
5 . The UHMWPE tube of claim 4 , wherein the metallic or non-metallic wire or mandrel and UHMWPE tube are both substantially cylindrical in shape.
6 . The UHMWPE tube of claim 1 , wherein the average wall thickness is 0.1 mm or less.
7 . The UHMWPE tube of claim 1 , wherein the average wall thickness of the tube is 0.005 mm to 0.1 mm.
8 . The UHMWPE tube of claim 1 , wherein the tube exhibits a change in the storage modulus between 23° C. and 40° C. of 70 MPa/° C. or less.
9 . The UHMWPE tube of claim 1 , comprising an inner surface with a coefficient of friction against stainless steel of less than 0.2.
10 . The UHMWPE tube of claim 9 , wherein a difference in the coefficient of friction between 23° C. and 40° C. is <0.1.
11 . The UHMWPE tube of claim 1 , comprising an inner surface with a coefficient of friction against stainless steel in saline of less than 0.1.
12 . The UHMWPE tube of claim 11 , wherein a difference in the coefficient of friction in saline between 23° C. and 40° C. is <0.1.
13 . The UHMWPE tube of claim 1 , consisting essentially of UHMWPE.
14 . The UHMWPE tube of claim 1 , comprising UHMWPE and a particulate filler, wherein the particulate filler is present in a concentration of less than 50% by weight, based on a weight of the UHMWPE tube.
15 . The UHMWPE tube of claim 1 , comprising UHMWPE and a particulate filler, wherein the particulate filler is present in a concentration of less than 20% by weight, based on a weight of the UHMWPE tube.
16 . The UHMWPE tube of claim 14 , wherein the particulate filler is a filler to impart radiopacity, strength, or hydrophilicity.
17 . The UHMWPE tube of claim 1 , further comprising one or more additives selected from the group consisting of antioxidants, antimicrobials, processing aids, sip aids, and colorants.
18 . The UHMWPE tube of claim 1 , wherein the UHMWPE tube comprises one or more additional polymeric materials other than UHMWPE, wherein the one or more additional polymer materials are present in a concentration of less than 50% by weight, based on a weight of the UHMWPE tube.
19 . The UHMWPE tube of claim 1 , wherein the UHMWPE tube comprises one or more additional polymeric materials other than UHMWPE, wherein the one or more additional polymer materials are present in a concentration of less than 20% by weight, based on a weight of the UHMWPE tube.
20 . The UHMWPE tube of claim 18 , wherein the one or more additional polymer materials are selected from modified polyethylene and ethylene vinyl acetate tie resins.