Magnetic composition comprising a resin consisting of copolymers containing polyamide blocks and polyether blocks
A magnetic composition including a polyamide block- and polyether block-containing copolymer resin in which the magnetic particles are dispersed. Also, a process for preparing same and to the use of same for the manufacture of a magnet which can in particular be used for electronic or electrical applications (smartphone, tablet, etc.), for sports, automobiles or industry.
1 . A magnetic composition comprising:
from 92% to 97% by weight of at least one magnetic filler,
from 3% to 8% by weight of a polyamide block- and polyether block-containing (PEBA) copolymer resin having an instantaneous hardness of less than or equal to 55 Shore D, and,
from 0% to 1% by weight of at least one additive,
the total amounting to 100% by weight of the composition,
wherein the melt viscosity of the PEBA copolymer is less than 550 Pa·s.
2 . The composition as claimed in claim 1 , wherein the at least one magnetic filler is chosen from magnetic particles based on rare earths and/or based on alnico (aluminum, nickel, cobalt) and/or based on ferrite.
3 . The composition as claimed in claim 1 , wherein the PEBA copolymer is a polyetheresteramide resulting from the polycondensation of polyamide blocks bearing dicarboxylic chain ends with polyetherdiols.
4 . The composition as claimed in claim 1 , wherein the polyamide blocks of the PEBA copolymer comprise at least one block chosen from PA 11, PA 12, PA 1112, PA 1010, PA 1012, PA 6, PA 610, PA 612, copolyamides, and/or mixtures thereof, and the polyether blocks of the PEBA copolymer comprise at least one block chosen from PTMG (polytetrahydrofuran), PEG (polyethylene glycol), PPG (propylene glycol), and PO3G (polytrimethylene glycol) blocks, and/or mixtures thereof.
5 . The composition as claimed in claim 1 , wherein the PEBA copolymer comprises from 30% to 90% by weight of polyether blocks, and from 10% to 70% by weight of polyamide blocks, relative to the total weight of the copolymer.
6 . The composition as claimed in claim 1 , wherein the at least one additive is chosen from UV stabilizers, heat stabilizers, antioxidants, fillers, mold-release agents, pigments, coupling agents, reinforcing materials, and lubricant.
7 . The composition as claimed in claim 1 , having an elongation at break of greater than 2%.
8 . A process for preparing a composition as claimed in claim 1 , comprising the steps of:
(i) mixing a PEBA copolymer in the form of powder or granules with a magnetic filler, and optional additives;
(ii) extruding the mixture obtained in step (i) to give an extrudate in the form of granules.
9 . The process as claimed in claim 8 , comprising a step (iii) of shaping by grinding the extrudate obtained in step (ii) to give a powder composition; or by injection molding the extrudate obtained in step (ii) to give a molded object.
10 . The process as claimed in claim 9 , comprising a step of applying a magnetic field to impart a desired magnetic characteristic on the extrudate during step (ii) or on the powder composition during step (iii) or on the molded object during step (iii).
11 . A composition obtained by the process of claim 8 .
12 . A method comprising manufacturing a magnet usable in electrical or electronic parts that can be used in the field of sports, automobiles, or medicine, the method comprising manufacturing the magnet by injection molding the composition of claim 1 .
13 . An article consisting of or comprising at least one magnet as described in claim 12 , the article being a component of sports equipment, of a sports shoe, of a smartwatch, of glasses, of furniture, of audiovisual equipment, of a computer, of automotive or aeronautical equipment, a household electrical appliance, and computing, electronic and/or microelectronic equipment.