Blade made of composite material with at least partially ceramic matrix
A blade made of composite material includes a fibrous reinforcement and an at least partially ceramic matrix, wherein the fibrous reinforcement includes a first structural portion formed by three-dimensional or multilayer weaving, and a second functional portion, distinct from the first portion, including short fibers.
1. A method for manufacturing a blade made of composite material, the blade comprising a fibrous reinforcement that is densified by a matrix that is at least partially ceramic, wherein the fibrous reinforcement comprises a first structural portion formed by three-dimensional weaving densified by said matrix, and a second functional portion consisting essentially of short fibers densified by said matrix and wherein the second functional portion forms a platform of the blade and spoilers of the platform and/or spoilers of a root of the blade, wherein the short fibers have an average length less than or equal to 5000 μm, and wherein the first structural portion and the second functional portion are co-densified with said matrix, wherein the method comprises:
depositing a mixture of the short fibers and a binder on the first structural portion of the fibrous reinforcement,
removing the binder, and
forming the matrix, which includes a ceramic matrix phase common to the short fibers and to the first structural portion of the fibrous reinforcement.
2. The method according to claim 1 , wherein the first structural portion is consolidated before depositing the mixture.
3. The method according to claim 1 , wherein the mixture of the short fibers and the binder is deposited by additive manufacturing.
4. The method according to claim 1 , wherein the common ceramic matrix phase is formed by melt infiltration.
5. The method according to claim 1 , wherein the first structural portion forms the fibrous reinforcement of the root, of a stilt and of an airfoil of the blade.
6. The method according to claim 1 , wherein the short fibers have an average length less than or equal to 1000 μm.
7. The method according to claim 1 , wherein the blade is a turbine blade or a compressor blade.