POLYOXO NIOBATE COMPOUND DISPERSION AND METHOD FOR MANUFACTURING SAME
A polyoxo niobate compound dispersion is provided and includes a part or all of a polyoxo niobate compound dispersed or dissolved in a mixed solvent using a lower alcohol and water as a main solvent and containing a primary amine, a secondary amine, a tertiary amine, a quaternary ammonium compound, or two or more of them, wherein the content of water is 5.0% by mass or more, the content of the amine compound solvent is 0.50 or more in terms of a molar ratio relative to the content of niobium (Nb), and the lower alcohol accounts for 70% by mass or more of a contained component other than a component derived from the polyoxo niobate compound, a component derived from the amine compound solvent, and water.
1 . A polyoxo niobate compound dispersion comprising a part or all of a polyoxo niobate compound dispersed or dissolved in a mixed solvent using a lower alcohol and water as a main solvent and containing a primary amine, a secondary amine, a tertiary amine, a quaternary ammonium compound, or two or more of them (also referred to as “amine compound solvent”),
wherein the content of water is 5.0% by mass or more,
the content of the amine compound solvent is 0.50 or more in terms of a molar ratio relative to the content of niobium (Nb), and
the lower alcohol accounts for 70% by mass or more of a contained component (referred to as “remaining portion”) other than a component derived from the polyoxo niobate compound, a component derived from the amine compound solvent, and water.
2 . The polyoxo niobate compound dispersion according to claim 1 ,
comprising 0.1% by mass to 40% by mass of niobium in terms of Nb 2 O 5 .
3 . The polyoxo niobate compound dispersion according to claim 1 , having a light transmittance at a wavelength of 400 nm of 65% or more.
4 . A method for producing a polyoxo niobate compound dispersion comprising mixing a polyoxo niobate compound (referred to as “precursor”) that is a compound containing polyoxo niobate and ammonium ions, a lower alcohol and/or water, and a primary amine, a secondary amine, a tertiary amine, a quaternary ammonium compound, or two or more of them (also referred to as “amine compound solvent”).
5 . The method for producing a polyoxo niobate compound dispersion according to claim 4 , wherein the precursor has a molar ratio of the content of ammonium ions to the content of Nb (NH 4 + /Nb) of 0.50 or more.
6 . The polyoxo niobate compound dispersion according to claim 1 , being evaluated as pass in the following adhesion evaluation,
wherein the polyoxo niobate compound dispersion is coated once on a soda glass substrate using a spin coater, the soda glass substrate provided with the coated film is calcined at 200° C. for 3 hours and cooled to 25° C., a cellophane adhesive tape having a size of 24 mm×15 m, according to Japanese Industrial Standards (JIS) Z1522: 2009, is attached to the surface of the coated film, within 1 minute after rubbing the surface of the adhesive tape three times with fingertips, the edge of the adhesive tape is grasped and the adhesive tape is peeled off at an angle of 60°±10° and at a speed of 0.5 to 1.0 second, and the polyoxo niobate compound dispersion is evaluated as “pass” when the surface of the coated film is smooth and there is no peeling at all.