Methods for producing highly thermoformable acrylic solid surface
Articles may be formed from a thermoformable composition, the thermoformable composition including: a) about 35 wt % to about 95 wt % of an acrylic pre-polymerized syrup; b) about 0 wt % to about 10 wt % of a comonomer; and c) about 5 wt % to about 65 wt % of a filler having an average particle size (d50) in a range of about 0.1 μm to about 50 μm; wherein the article has a surface having a gloss measurement at a 60° measurement angle within a range of about 0 Gloss Units to about 20 Gloss Units, and a roughness Ra within a range of about 1 microinch to about 100 microinches. Methods may include producing a thermoformed article by the steps of: i) preparing a thermoformable composition; ii) casting the thermoformable composition into a sheet; and iii) thermoforming the cast sheet against a mold to produce a thermoformed article.
1. An article formed from a thermoformable composition, the thermoformable composition comprising:
a) about 35 wt % to about 95 wt % of an acrylic pre-polymerized syrup;
b) about 0 wt % to about 10 wt % of a comonomer; and
c) about 5 wt % to about 65 wt % of a filler having an average particle size (d50) in a range of about 0.1 μm to about 50 μm, wherein the filler comprises one or more selected from a group consisting of aluminum trihydrate, aluminum monohydrate, magnesium hydroxide, calcium carbonate, magnesium silicate, talc, silica, calcium carbonate, calcium metasilicate, Wollastonite, Dolomite, Perlite, hollow glass spheres, and kaolin;
wherein the article has a surface having a gloss measurement at a 60° measurement angle within a range of about 0 Gloss Units to about 20 Gloss Units, and a roughness Ra within a range of about 1 microinch to about 100 microinches.
2. The article of claim 1 , wherein a ratio of filler to acrylic pre-polymerized syrup is in a range of about 0.05 to about 1.9.
3. The article of claim 1 , wherein the filler has a d50 particle size in a range of about 2 μm to about 20 μm and a Brunauer-Emmett-Teller (BET) surface area of greater than about 1 m 2 /g.
4. The article of claim 1 , wherein the filler has a Brunauer-Emmett-Teller (BET) surface area of greater than about 3 m 2 /g.
5. The article of claim 1 , wherein the acrylic pre-polymerized syrup has a percent by weight of solids (wt %) ranging from 5 wt % to 40 wt %.
6. The article of claim 1 , wherein the comonomer is butyl acrylate.
7. The article of claim 1 , wherein the article has a Q value ranging from 5 to 25.
8. The article of claim 1 , wherein the thermoformable composition comprises:
a) about 35 wt % to about 95 wt % of an acrylic pre-polymerized syrup;
b) about 0 wt % to about 10 wt % of a comonomer;
c) about 5 wt % to about 65 wt % of a filler, wherein the filler has an average particle size (d50) in a range of 0.1 μm to 50 μm;
d) about 0.0 wt % to about 1.0 wt % of a coupling agent; and
e) about 0.1 to about 1.0 wt % of a crosslinking agent.
9. The article of claim 1 , wherein the filler comprises less than about 1.0 wt % of moisture.
10. The article of claim 1 , wherein the thermoformable composition further comprises one or more selected from a group consisting of wetting/dispersing agent, anti-flocculating agent, pigment, release agent, air release agent, suspension agent, and initiator.
11. The article of claim 1 , wherein the article has a density of greater than about 1.3 g/cm 3 .
12. A method for producing a thermoformed article comprising the steps of:
i) preparing a thermoformable composition comprising:
a) about 35 wt % to about 95 wt % of an acrylic pre-polymerized syrup;
b) about 0-10 wt % of a comonomer; and
c) about 5-65 wt % of a filler, wherein the filler has an average particle size (d50) in a range of 0.1 μm to 50 μm, and wherein the filler comprises one or more selected from a group consisting of aluminum trihydrate, aluminum monohydrate, magnesium hydroxide, calcium carbonate, magnesium silicate, talc, silica, calcium carbonate, calcium metasilicate, Wollastonite, Dolomite, Perlite, hollow glass spheres, and kaolin;
ii) casting the thermoformable composition into a sheet; and
iii) thermoforming the cast sheet against a mold to produce a thermoformed article, wherein the article has a surface having a gloss measurement at a 60° measurement angle within a range of about 0 Gloss Units to about 20 Gloss Units, and a roughness Ra within a range of about 1 microinch to about 100 microinches.
13. The method of claim 12 , further comprising modifying the surface of the thermoformed article by one or more of sanding, media blasting, embossing a pattern on the article, cell casting between plates, casting on a matte film, and acid-etching.
14. The method of claim 12 , wherein a ratio of filler to acrylic pre-polymerized syrup is in a range of 0.05 to 1.9.
15. The method of claim 12 , wherein the acrylic pre-polymerized syrup has a percent by weight of solids (wt %) ranging from 5 wt % to 40 wt %.
16. The method of claim 12 , wherein the thermoformed article has a Q value ranging from 5 to 25 following thermoforming.
17. The method of claim 12 , wherein the filler has a d50 particle size in a range of about 2 μm to about 20 μm and a BET surface area of greater than about 1 m 2 /g.
18. The article of claim 1 , wherein the thermoformable composition comprises about 0.05 wt % to about 1.0 wt % of a coupling agent.