Polyketone powder for laser sintering
A semicrystalline poly ketone powder useful for additive manufacturing may be made by dissolving a polyketone having differential scanning calorimetry (DSC) monomodal melt peak, at a temperature above 50° C. to below the melt temperature of the polyketone, precipitating the dissolved polyketone by cooling, addition of a nonsolvent or combination thereof. The method may be used to form polyketones having a DSC melt peak with an enthalpy greater than the starting polyketone.
1. A composition comprising a semicrystalline aliphatic polyketone powder that has a melt peak having a melt peak enthalpy of at least 50 joules/gram as determined by differential scanning calorimetry (DSC) using a heating rate of 10° C./min, wherein the semicrystalline aliphatic polyketone is represented by:
where A is the residue of an alkene monomer converted to a saturated hydrocarbon group, m is from about 1 to 6 and n is at least about 2 to 10,000.
2. The composition of claim 1 , wherein the composition has a D 90 particle size of at most 300 micrometers and average particle size of 1 micrometer to 150 micrometers equivalent spherical diameter.
3. The composition of claim 1 , wherein at least 80% by number of the particles of the semicrystalline polyketone powder has a circularity of at least about 0.8.
4. The composition of claim 3 , wherein the semicrystalline aliphatic polyketone powder is a copolymer of ethylene, carbon monoxide and at least one other alkene monomer.
5. The composition of claim 4 , wherein the other alkene monomer is propylene.
6. The composition of claim 1 , wherein the melt peak and recrystallization peak fail to overlap.
7. The composition of claim 6 , wherein the melt peak has an onset melt peak temperature and a recrystallization peak onset temperature that are at least separated by 10° C.
8. The composition of claim 1 , wherein the semicrystalline aliphatic polyketone powder has a crystallinity of at least about 15% by volume.
9. The composition of claim 2 , wherein semicrystalline aliphatic polyketone powder has: (i) a D90 particle size of less than about 150 μm, (ii) a D10 of at least 10 μm and (iii) an average particle size of about 20 μm to about 150 μm.
10. The composition of claim 1 , wherein the melt peak has a melt enthalpy of at least 75 joules/gram.
11. A method for forming an aliphatic polyketone powder useful for making an additive manufactured article comprising;
(i) dissolving an initial aliphatic polyketone having an onset melt temperature in a solvent above 50° C. to below the onset melt temperature of the initial aliphatic polyketone to form a solution comprised of a dissolved aliphatic polyketone,
(ii) precipitating the dissolved aliphatic polyketone by cooling the solution, adding a non-solvent to the solution or combination thereof to form the semicrystalline aliphatic polyketone powder, and
(iii) separating the semicrystalline aliphatic polyketone powder from the solvent, wherein the semicrystalline aliphatic polyketone is represented by:
where A is the residue of an alkene monomer converted to a saturated hydrocarbon group, m is from about 1 to 6 and n is at least about 2 to 10,000 and has a melt peak and recrystallization peak that fail to overlap.
12. The method of claim 11 , further comprising comminuting the semicrystalline aliphatic polyketone powder to form a semicrystalline aliphatic comminuted polyketone powder.
13. The method of claim 11 further comprising heating the semicrystalline aliphatic polyketone powder of step (iii) to a temperature within 20% of the onset melt temperature of the semicrystalline aliphatic polyketone to form a heat-treated semicrystalline aliphatic polyketone.
14. The method of claim 13 , wherein the semicrystalline aliphatic polyketone has a melt peak enthalpy of at least 75 joules/gram.
15. The method of claim 14 , wherein the conditions to increase the crystallinity is comprised of heat treating any one of the said semicrystalline aliphatic polyketone powders to a temperature from 50° C. to below the melt peak temperature as determined by DSC for a time to increase the crystallinity forming an increased crystallinity semicrystalline aliphatic polyketone.
16. The method of claim 11 , wherein the dissolving is at a temperature from 100° C. to 150° C.
17. The method of claim 11 , wherein the precipitating is performed by adding a nonsolvent comprised of water.
18. The method of claim 17 , wherein the precipitating is performed at a temperature from 75° C. to 130° C.
19. The method of claim 11 , wherein the initial semicrystalline aliphatic polyketone has a monomodal melt peak and crystallization peak each having an onset temperature that fail to overlap.
20. The method of any one of claim 17 , wherein the solvent is a polar aprotic solvent.