A METHOD OF MAKING A CATALYTIC COMPOSITION
The present invention relates to a method for making a catalytic composition and, in particular, to a composition for treating a NOx-containing exhaust gas. The composition comprises a small-pore zeolite having a SAR of 9-30 and one or more rare earth metals. The method achieves the introduction of higher levels of rare earth (RE) metals into a zeolite than can be achieved with conventional wash-coating approaches.
1 . A method of making a catalytic composition for treating a NOx-containing exhaust gas, wherein the composition comprises a small-pore zeolite having a SAR of 9-30 and one or more rare earth metals, the method comprising:
i) providing a large-pore precursor zeolite;
ii) introducing one or more rare earth metals into the precursor zeolite by ion exchange and calcination to form a rare earth metal-substituted precursor zeolite;
iii) converting the rare earth metal-substituted precursor zeolite into a small pore zeolite in the presence of a structure directing agent.
2 . The method according to claim 1 , wherein step (iii) comprises forming a synthesis gel comprising the rare earth metal-substituted precursor zeolite and the structure directing agent and then heating the synthesis gel to form the small-pore zeolite.
3 . The method according to claim 1 , wherein the small pore zeolite comprises the one or more rare earth metals in a total amount of 0.05 to 3.5 wt %, preferably 0.05 to 2 wt %.
4 . The method according to claim 1 , wherein the small pore zeolite further comprises Cu and/or Fe, preferably in a total amount of 0.1 to 6 wt %, more preferably in a total amount of 1 to 3 wt %.
5 . The method according to claim 1 , wherein the large-pore precursor zeolite has a USY framework structure type.
6 . The method according to claim 1 , wherein the small-pore zeolite has a CHA or AEI framework structure type.
7 . The method according to claim 1 , wherein the structure directing agent is N,N,N, trimethyladamantylammonium hydroxide or a salt thereof.
8 . The method according to claim 1 , wherein the rare earth metals are selected from Y and Ce and mixtures thereof.
9 . A catalytic composition for treating a NOx-containing exhaust gas, wherein the catalytic composition is produced according to the method of claim 1 , wherein the small pore zeolite of the catalytic composition has a SAR of 9-30 and one or more rare earth metals.
10 . Use of the A method comprising contacting a NOx-containing exhaust gas with the catalytic composition according to claim 9 .