A METHOD OF SYNTHESIZING A LOW SAR CHABAZITE ZEOLITE AND THE ZEOLITE OBTAINED THEREBY
A low SAR chabazite zeolite, its synthesis, and its use for the treatment of an exhaust gas, are disclosed. The chabazite (CHA) zeolite having an SAR of from 7 to 15, and at least one following features: (a) a mesoporous surface area of less than 35 m 2 (b) a BET surface area of 500-800 m 2 /g; and/or (c) a micropore volume of 0.2-0.3 cm 2 /g.
1 . A chabazite (CHA) zeolite having an SAR of from 7 to 15, and at least one following features: (a) a mesoporous surface area of less than 35 m 2 /g; (b) a BET surface area of 500-800 m 2 /g; and/or (c) a micropore volume of 0.2-0.3 cm 2 /g.
2 . The CHA zeolite according to claim 1 , wherein the SAR is from 7 to 13, preferably 8 to 12.
3 . The CHA zeolite according to claim 1 , wherein the zeolite has a crystallinity of greater than 95%.
4 . The CHA zeolite according to claim 1 , having a granular particle comprising cubic crystals.
5 . The CHA zeolite according to claim 1 , having a mean longest edge crystal size of no greater than 6 microns.
6 . A method for the manufacture of a chabazite (CHA) zeolite having an SAR of from 7 to 15, the method comprising:
(i) forming a reaction gel comprising a structure directing agent (SDA), sodium and/or potassium hydroxide, a silica source and an alumina source, and
(ii) heating the gel to a temperature and for a duration suitable for the growth of the CHA zeolite,
wherein, relative to a molar amount of Al 2 O 3 equivalent, the gel comprises from 0.1 to 2 moles of the SDA, and wherein the SDA cation is N,N,N-trimethyladamantylammonium.
7 . The method according to claim 6 , wherein, relative to the molar amount of Al 2 O 3 equivalent, the gel comprises from 0.5 to 1.8 moles of the SDA.
8 . The method according to claim 6 , wherein, relative to the molar amount of Al 2 O 3 equivalent, the gel comprises water and the water is present in an amount of 750 to 1200 moles.
9 . The method according to claim 6 , wherein, relative to the molar amount of Al 2 O 3 equivalent, the gel comprises an amount of SiO 2 equivalent of 20 to 50 moles.
10 . The method according to claim 6 , wherein, relative to the molar amount of Al 2 O 3 equivalent, the gel comprises a total amount of Na 2 O and K 2 O equivalent of 3 to 15 moles.
11 . The method according to claim 6 , wherein the reaction gel does not comprise CHA seed crystals.
12 . The method according to claim 6 , wherein the gel consists of the structure directing agent (SDA), sodium and/or potassium hydroxide, the silica source, the alumina source and water.
13 . The method according to claim 6 , wherein the temperature is from 110° C. to 190° C.
14 . The method according to claim 6 , wherein the duration is 20 to 60 hours.
15 . The method according to claim 6 wherein the alumina source is selected from FAU zeolite, USY zeolite, Al(OH) 3 , and Al 2 (SO 4 ) 3 .
16 . The method according to claim 6 , wherein the method further comprises adding iron and/or copper to the zeolite by ion exchange.
17 . (canceled)
18 . A catalyst article for the treatment of an exhaust gas, the catalyst article comprising the CHA zeolite according to claim 1 .
19 . A method for the treatment of an exhaust gas, the method comprising contacting an exhaust gas with the catalyst article according to claim 18 .
20 . A catalyst article for the treatment of an exhaust gas, the catalyst article comprising the CHA zeolite prepared by the method according to claim 6 .
21 . A method for the treatment of an exhaust gas, the method comprising contacting an exhaust gas with the catalyst article according to claim 20 .