COATINGS AND SURFACE MODIFICATIONS TO MITIGATE SiC CLADDING DURING OPERATION IN LIGHT WATER REACTORS
The invention relates to SiC ceramic matrix composite (CMC) claddings with metallic, ceramic and/or multilayer coatings applied on the outer surface for improved corrosion resistance and hermeticity protection. The coating includes one or more materials selected from FeCrAl, Y, Zr and Al—Cr alloys, Cr 2 O 3 , ZrO 2 and other oxides, chromium carbides, CrN, Zr- and Y-silicates and silicides. The coatings are applied employing a variety of known surface treatment technologies including cold spray, thermal spray process, physical vapor deposition process (PVD), and slurry coating.
1 . (canceled)
2 . A composite silicon carbide cladding for use in a light water nuclear reactor, the composite silicon carbide cladding comprising:
an innermost a silicon carbide ceramic matrix composite (CMC) layer, wherein the silicon carbide CMC layer comprises a silicon matrix and silicon fibers; and
a coating applied to an outer surface of the silicon carbide CMC layer, wherein the coating comprises:
a first CrN layer applied to the outer surface of the silicon carbide CMC layer, a first chromium layer applied to the first CrN layer, a second CrN layer applied to the first chromium layer, and a second chromium layer applied to the second CrN layer;
a YSi 2 layer applied to the outer surface of the silicon carbide CMC layer;
a Y 2 Si 2 O 7 layer applied to the outer surface of the silicon carbide CMC layer;
a ZrSi 2 layer applied to the outer surface of the silicon carbide CMC layer; or
a ZrSiO 4 layer applied to the outer surface of the silicon carbide CMC layer.
3 . (canceled)
4 . A method of preparing a composite silicon carbide cladding for use in a light water nuclear reactor, comprising:
providing a silicon carbide ceramic matrix composite (CMC) substrate, wherein the silicon carbide CMC substrate comprises a silicon matrix and silicon fibers; and
depositing a coating on an outer surface of the silicon carbide CMC substrate, wherein depositing the coating, comprises:
depositing a first CrN layer on the outer surface of the silicon carbide CMC substrate, depositing a first chromium layer on the CrN layer, depositing a second CrN layer on the first chromium layer, and depositing a second chromium layer on the second CrN layer;
depositing a YSi 2 layer on the outer surface of the silicon carbide CMC substrate; or
depositing a ZrSi 2 layer on the outer surface of the silicon carbide CMC substrate.
5 . (canceled)
6 . (canceled)
7 . The method of claim 4 , wherein depositing the coating comprises depositing the YSi 2 layer on the outer surface of the silicon carbide CMC substrate, the method further comprising heat treating the coating forming a Y 2 Si 2 O 7 layer applied to the outer surface of the silicon carbide CMC substrate.
8 . The method of claim 4 , wherein depositing the coating comprises depositing the ZrSi 2 layer on the outer surface of the silicon carbide CMC substrate, the method further comprising heat treating the coating forming a ZrSiO 4 layer applied to the outer surface of the silicon carbide CMC substrate.
9 . (canceled)
10 . The method of claim 4 , wherein depositing the coating comprises a process selected from the group consisting of thermal spray, physical vapor deposition, and DC reactive sputtering.
11 . (canceled)
12 . The composite silicon carbide cladding of claim 2 , wherein the coating comprises the first CrN layer applied to the outer surface of the silicon carbide CMC layer, the first chromium layer applied to the first CrN layer, the second CrN layer applied to the first chromium layer, and the second chromium layer applied to the second CrN layer.
13 . The composite silicon carbide cladding of claim 2 , wherein the coating comprises the YSi 2 layer applied to the outer surface of the silicon carbide CMC layer.
14 . The composite silicon carbide cladding of claim 2 , wherein the coating comprises the Y 2 Si 2 O 7 layer applied to the outer surface of the silicon carbide CMC layer.
15 . The composite silicon carbide cladding of claim 2 , wherein the coating comprises the ZrSi 2 layer applied to the outer surface of the silicon carbide CMC layer.
16 . The composite silicon carbide cladding of claim 2 , wherein the coating comprises the ZrSiO 4 layer applied to the outer surface of the silicon carbide CMC layer.