ARTIFICIAL GRAPHITE AND PREPARATION METHOD THEREOF, SECONDARY BATTERY CONTAINING SUCH ARTIFICIAL GRAPHITE, AND ELECTRIC APPARATUS
An artificial graphite and a preparation method thereof, a secondary battery containing the artificial graphite, and an electric apparatus are provided. The artificial graphite includes secondary particles and satisfies A≥0.5, where A is a ratio of a powder compacted density of the artificial graphite at 2 t pressure to a particle size by volume D v 1 of the artificial graphite. The secondary battery provided in this application can have low cyclic volume swelling while maintaining high energy density.
1 . An artificial graphite, wherein the artificial graphite comprises secondary particles and satisfies A≥0.5;
wherein A is a ratio of a powder compacted density (measured in g/cm 3 ) of the artificial graphite at 2 t pressure to a particle size by volume D v 1 (measured in μm) of the artificial graphite.
2 . The artificial graphite according to claim 1 , wherein the secondary particles satisfies 0.50≤A≤1.40.
3 . The artificial graphite according to claim 1 , wherein the secondary particles satisfies 0.70≤A≤1.30.
4 . The artificial graphite according to claim 1 , wherein the artificial graphite is secondary particles.
5 . The artificial graphite according to claim 1 , wherein the powder compacted density of the artificial graphite at 2 t pressure is 1.60 g/cm 3 -1.95 g/cm 3 .
6 . The artificial graphite according to claim 5 , wherein the powder compacted density of the artificial graphite at 2 t pressure is 1.70 g/cm 3 -1.90 g/cm 3 .
7 . The artificial graphite according to claim 1 , wherein the particle size by volume D v 1 of the artificial graphite is 1.5 μm-3.5 μm.
8 . The artificial graphite according to claim 7 , wherein the particle size by volume D v 1 of the artificial graphite is 1.8 μm-3.2 μm.
9 . The artificial graphite according to claim 7 , wherein the particle size by volume D v 1 of the artificial graphite is 2 μm-3.2 μm.
10 . The artificial graphite according to claim 1 , wherein a particle size by volume D v 50 of the artificial graphite is 10.0 μm-20.0 μm.
11 . The artificial graphite according to claim 10 , wherein a particle size by volume D v 50 of the artificial graphite is 12.0 μm-20.0 μm
12 . The artificial graphite according to claim 1 , wherein a gram capacity of the artificial graphite is 350 mAh/g or more.
13 . The artificial graphite according to claim 1 , wherein the gram capacity of the artificial graphite is 352 mAh/g or more.
14 . A preparation method of artificial graphite, comprising the following steps:
S1: performing crushing, grading, and shaping treatment on a raw material to obtain a precursor;
S2: performing granulation treatment on the precursor obtained in step S1 to obtain an intermediate 1;
S3: performing graphitization treatment on the intermediate 1 obtained in step S2 at a temperature of 2700° C.-3200° C. to obtain an intermediate 2; and
S4: performing mechanical treatment on the intermediate 2 obtained in step S3 in a mechanical fusion machine to obtain artificial graphite;
wherein the artificial graphite comprises secondary particles and satisfies A≥0.5, and A is a ratio of a powder compacted density of the artificial graphite at 2 t pressure to a particle size by volume D v 1 of the artificial graphite.
15 . The preparation method according to claim 14 , wherein in the mechanical treatment, a rotating speed of the mechanical fusion machine is 600 rpm-1400 rpm.
16 . The preparation method according to claim 14 , wherein a treatment time of the mechanical treatment is 5 min to 30 min.
17 . The preparation method according to claim 14 , wherein a binder is added in the granulation treatment, and an amount of the binder added is 5%-15% of a weight of the precursor used for the granulation in step S2.
18 . The preparation method according to claim 14 , wherein the binder comprises one or more of coal tar, pitch, epoxy resin, and phenolic resin.
19 . The preparation method according to claim 14 , wherein the raw material comprises one or more of green petroleum coke, calcined petroleum coke, needle green coke, calcined needle coke, pitch coke, and metallurgical coke.
20 . A secondary battery, comprising a negative electrode plate, wherein the negative electrode plate comprises a negative electrode active material, and the negative electrode active material comprises the artificial graphite according to claim 1 .