POSITIVE ELECTRODE MATERIAL, PREPARATION METHOD THEREOF, AND SECONDARY BATTERY INCLUDING SAME
A positive electrode material, including a core and a shell layer are provided. In some embodiments, a molecular formula of the core is Li 1+a Ni x Co y Mn 1-x-y M1 z O 2 , 0.8≤x<1.0, 0<y<0.2, 0<a<0.1, 0≤z<0.1, and M1 is selected from at least one of Al, Ta, and B; and a molecular formula of the shell layer is Li 1+b Co m A1 n Nb 1-m-n M2 c O 2 , 0.85≤m<1.0, 0<n<0.15, 0<b<0.1, 0.001≤1-m-n≤0.02, 0≤c<0.05, and M2 is selected from at least one of W, Mo, Ti, Zr, Y, and Yb.
1 . A positive electrode material, comprising:
a core; and
a shell layer;
wherein a molecular formula of the core is Li 1+a Ni x Co y Mn 1-x-y M1 z O 2 , 0.8≤x<1.0, 0<y<0.2, 0<a<0.1, 0≤z<0.1, and M1 is selected from at least one of Al, Ta, and B;
and a molecular formula of the shell layer is Li 1+b Co m Al n Nb 1-m- n M2 c O 2 , 0.85≤m<1.0, 0<n<0.15, 0<b<0.1, 0.001≤1-m-n≤0.02, 0≤c<0.05, and M2 is selected from at least one of W, Mo, Ti, Zr, Y, or Yb.
2 . The positive electrode material according to claim 1 , wherein
an average length-to-width ratio of primary particles of the positive electrode material is 2-11.
3 . The positive electrode material according to claim 1 , wherein
the average length-to-width ratio of primary particles of the positive electrode material is 5-8.
4 . The positive electrode material according to claim 1 , wherein
an average diameter of the core is 2 µm to 10 µm, and an average thickness of the shell layer is 0.5 µm-3 µm.
5 . The positive electrode material according to claim 1 , wherein
a median particle size by volume Dv50 of the positive electrode material is 3 µm-16 µm.
6 . The positive electrode material according to claim 5 , wherein
the median particle size by volume Dv50 of the positive electrode material is 5 µm-11 µm.
7 . The positive electrode material according to claim 1 , wherein
a particle size distribution of the positive electrode material satisfies 1.35≤(Dv90-Dv10)/Dv50≤1.50.
8 . The positive electrode material according to claim 1 , wherein
a specific surface area of the positive electrode material is 0.2 m 2 /g-1m 2 /g.
9 . The positive electrode material according to claim 8 , wherein
the specific surface area of the positive electrode material is 0.3 m 2 /g-0.7 m 2 /g.
10 . The positive electrode material according to claim 1 , wherein
a tap density (TD) of the positive electrode material is 1.8 g/cm 3 -2.5 g/cm 3 .
11 . The positive electrode material according to claim 10 , wherein
The TD of the positive electrode material is 1.9 g/cm 3 -2.3 g/cm 3 .
12 . A preparation method of positive electrode material,
comprising the following:
preparing a first mixed solution containing a soluble nickel salt, a first cobalt salt, and a manganese salt, preparing a second mixed solution containing a second cobalt salt and an aluminum salt, and preparing an alkali solution, an ammonia solution, and a niobium salt solution;
adding pure water into a reactor as a solvent, adding the ammonia solution and the alkali solution in the reactor to adjust a pH value and an amino value of the solvent, stirring the resulting product, maintaining a stable reaction temperature, adding the first mixed solution, the alkali solution, and the ammonia solution concurrently into the reactor, maintaining the pH value and the amino value unchanged, and introducing an inert gas for protection, to synthesize a first precursor slurry;
adding the second mixed solution, the niobium salt solution, the alkali solution, and the ammonia solution concurrently into the reactor, and maintaining the pH value and the amino value unchanged, to synthesize a second precursor slurry; and
mixing the synthesized second precursor slurry and lithium salt based on a specified proportion for sintering to obtain a positive electrode material, wherein the positive electrode material comprises a core and a shell layer; and
a molecular formula of the core is Li 1+a Ni x Co y Mn 1-x-y M1 z O 2 , 0.8≤x<1.0, 0<y<0.2, 0<a<0.1, 0≤z<0.1, and M1 is selected from at least one of Al, Ta, and B;
and a molecular formula of the shell layer is Li 1+b Co m Al n Nb 1-m -n M2 c O 2 , 0.85≤m<1.0, 0<n<0.15, 0<b<0.1, 0.001≤1-m-n≤0.02, 0≤c<0.05, and M2 is selected from at least one of W, Mo, Ti, Zr, Y, or Yb.
13 . The preparation method of positive electrode material according to claim 12 , wherein
the soluble nickel salt contains one or more of nickel sulfate, nickel nitrate, and nickel acetate;
the first cobalt salt and the second cobalt salt contain one or more of cobalt sulfate, cobalt oxalate, cobalt nitrate, and cobalt acetate; and/or
the manganese salt contains one or more of manganese sulfate, manganese nitrate, and manganese acetate;
the aluminum salt contains one or more of aluminum sulfate, aluminum nitrate, aluminum chloride, aluminum acetate, and aluminum sulfite;
the niobium salt contains one or more of niobium oxalate, sodium niobate, niobium nitrate, and niobium chloride; and/or
the alkali contains one or more of an alkali hydroxide, an alkaline earth hydroxide, and alkali metal carbonate.
14 . The preparation method of positive electrode material according to claim 12 , wherein
a concentration of all metal ions in the first mixed solution is 1 mol/L-5 mol/L; and/or
a concentration of all metal ions in the second mixed solution is 1 mol/L-5 mol/L;
a concentration of alkali in the alkali solution is 1 mol/L-10 mol/L;
a concentration of ammonia in the ammonia solution is 5 mol/L-10 mol/L; and/or
a concentration of niobium salt in the niobium salt solution is 0.5 mol/L-2 mol/L.
15 . The preparation method of positive electrode material according to claim 12 , wherein
the reaction pH value is 11.0-12.0, and preferably 11.2-11.6;
the reaction amino value is 0.1 mol/L-0.6 mol/L, and preferably 0.2 mol/L-0.5 mol/L;
the reaction temperature is 50° C.-70° C.; and/or
a stirring velocity is 200 rpm-600 rpm.
16 . The preparation method of positive electrode material according to claim 12 , wherein
a molar ratio of the lithium salt to metal in the second precursor slurry, Li/Me, is 0.9-1.1, Me is a total mole number of nickel, cobalt, and manganese;
a sintering temperature is 700° C.-900° C.;
a sintering time is 10 h-20 h; and/or
a sintering atmosphere is air atmosphere or oxygen-containing atmosphere.
17 . A secondary battery, wherein
the secondary battery comprises the positive electrode material according to claim 1 or the positive electrode material prepared by using the preparation method according to claim 12 .
18 . A battery module, wherein
the battery module comprises the secondary battery according to claim 17 .
19 . A battery pack, wherein
the battery pack comprises the battery module according to claim 18 .
20 . An electric apparatus, wherein
the electric apparatus comprises at least one of the secondary battery according to claim 17 , the battery module according to claim 18 , and the battery pack according to claim 19 .