MODIFIED POSITIVE ELECTRODE MATERIAL AND PREPARATION METHOD THEREOF, POSITIVE ELECTRODE PLATE, SECONDARY BATTERY, BATTERY MODULE, BATTERY PACK AND ELECTRICAL APPARATUS
A modified positive electrode material includes an inner core and a cladding layer. The inner core is a positive electrode material, and the cladding layer includes a polymer electrolyte body and a ferroelectric ceramic material dispersed in the polymer electrolyte body.
1 . A modified positive electrode material, comprising:
an inner core; and
a cladding layer;
wherein the inner core is a positive electrode material, and the cladding layer includes a polymer electrolyte body and a ferroelectric ceramic material dispersed in the polymer electrolyte body.
2 . The modified positive electrode material according to claim 1 , wherein a mass of the cladding layer is 0.5 wt %-5 wt % of a mass of the modified positive electrode material.
3 . The modified positive electrode material according to claim 1 , wherein an ionic diffusion coefficient of the modified positive electrode material is 10 −11 -10 −10 S/cm 2 .
4 . The modified positive electrode material according to claim 1 , wherein the polymer electrolyte body is one or more selected from the group consisting of polyethylene oxide, polyethylene glycol, polymethyl methacrylate, polyacrylonitrile, polyvinylidene fluoride, vinylidene fluoride-trifluoroethylene copolymer, vinylidene fluoride-hexafluoropropylene copolymer, and vinylidene fluoride-chlorotrifluoroethylene copolymer.
5 . The modified positive electrode material according to claim 1 , wherein a weight average molecular weight of the polymer electrolyte body is 1500 to 800000.
6 . The modified positive electrode material according to claim 1 , wherein the ferroelectric ceramic material has the general formula: XYO 3 , where X is one or more selected from the group consisting of Li + , Na + , K + , Mg 2+ , Sr 2+ , Pb 2+ , Ba 2+ and La 2+ , Y is one or more selected from the group consisting of Ti 4+ , Zr 4+ , V 5+ , Nb 5+ and Ta 2+ .
7 . The modified positive electrode material according to claim 1 , wherein a D V50 particle size of the ferroelectric ceramic material is 5 nm to 100 nm.
8 . The modified positive electrode material according to claim 1 , wherein a thickness of the cladding layer is 2 nm to 40 nm.
9 . The modified positive electrode material according to claim 1 , wherein the positive electrode material is any one or more selected from the group consisting of layered positive electrode materials, lithium-rich manganese-based positive electrode materials, spinel lithium manganese nickel oxide positive electrode materials, and conversion positive electrode materials.
10 . A preparation method of the modified positive electrode material according to claim 1 , comprising:
preparing a solution of a polymer electrolyte;
mixing a ferroelectric ceramic material with a positive electrode material to obtain the positive electrode material cladded with the ferroelectric ceramic material; and
mixing and drying the solution of the polymer electrolyte and the positive electrode material coated with the ferroelectric ceramic material to obtain the modified positive electrode material.
11 . The preparation method according to claim 10 , wherein a mass sum W1 of the polymer electrolyte, the positive electrode material, and the ferroelectric ceramic material and a mass W2 of the polymer electrolyte satisfy that W2/W1 is between 0.5 wt % and 5 wt %.
12 . The preparation method according to claim 10 , wherein a mass W2 of the polymer electrolyte and a mass W3 of the ferroelectric ceramic material satisfy that W3/(W2+W3) is between 2% and 10%.
13 . The preparation method according to claim 10 , wherein a mass content of the polymer electrolyte in the polymer electrolyte solution is 0.5%-10%.
14 . The preparation method according to claim 10 , wherein a solvent used in the polymer electrolyte solution is one or more selected from the group consisting of absolute ethanol, N-methylpyrrolidone (NMP), and N,N-dimethylformamide (DMF).
15 . The preparation method according to claim 10 , wherein the drying includes spray drying.
16 . A positive electrode plate, comprising:
a positive electrode current collector; and
a positive electrode film layer disposed on at least one surface of the positive electrode current collector, wherein the positive electrode film layer comprises a positive electrode active material, the positive electrode active material includes the modified positive electrode material according to claim 1 .
17 . A secondary battery, comprising the modified positive electrode material according to claim 1 .
18 . A battery module comprising the secondary battery according to claim 17 .
19 . A battery pack comprising the battery module according to claim 18 .
20 . An electrical apparatus comprising the secondary battery according to claim 17 .