The present disclosure provides extruded PTFE composite tubes with a reduced coefficient of friction (COF). In some embodiments, such extruded PTFE composite tubes may exhibit a reduced change in coefficient of friction between about 20° C. and about 40° C. with the inclusion of secondary polymeric particles with small particle sizes (<100 μm) at loading percentages of less than about 50 weight %.
1 .- 22 . (canceled)
23 . A PTFE composite tube comprising PTFE and a second polymer,
wherein the second polymer is present in a concentration of less than about 50% by weight of the PTFE composite tube, and
wherein the PTFE composite tube exhibits a smaller change in coefficient of friction from about 23° C. to about 40° C. as compared to a comparable PTFE tube, the comparable PTFE tube not comprising the second polymer.
24 . The PTFE composite tube of claim 23 , wherein the concentration of the second polymer is less than 10% by weight of the PTFE composite tube.
25 . The PTFE composite tube of claim 23 , wherein the PTFE composite tube exhibits a coefficient of friction of about 0.07 or less at 23° C. and an increase in coefficient of friction of about 0.02 or less from about 23° C. to about 40° C.
26 . The PTFE composite tube of claim 23 , wherein the PTFE composite tube exhibits a lower storage modulus as compared to a comparable PTFE tube, the comparable PTFE tube not comprising the second polymer, at temperatures from 0° C. to about 100° C. and a reduced change in storage modulus from about 20° C. to about 40° C. as compared to the comparable PTFE tube.
27 . The PTFE composite tube of claim 23 , wherein the PTFE composite tube exhibits a storage modulus of about 15×10 8 Pa or less at temperatures from about 15° C. to about 100° C. and a decrease in storage modulus of about 7.5×10 8 Pa or less from about 20° C. to about 40° C.
28 . The PTFE composite tube of claim 23 , wherein the second polymer is a polyolefin or modified polyolefin.
29 . The PTFE composite tube of claim 23 , wherein the second polymer is a fluoropolymer or a modified fluoropolymer.
30 . The PTFE composite tube of claim 23 , wherein the second polymer is a polyarylketone (PAEK), a polyetheretherketone (PEEK), or a modified PAEK or PEEK.
31 . The PTFE composite tube of claim 23 , wherein the second polymer is a polyester or modified polyester.
32 . The PTFE composite tube of claim 23 , wherein the second polymer is a polyurethane or modified polyurethane.
33 . The PTFE composite tube of claim 23 , wherein the second polymer is a polyimide, polyamide, polyamine, or a copolymer thereof.
34 . The PTFE composite tube of claim 23 , wherein the second polymer is in the form of a plurality of polymeric particles having an average particle size of less than about 100 microns.
35 . The PTFE composite tube of claim 23 , wherein the second polymer is a second, different PTFE selected from the group consisting of sintered PTFE, reground PTFE, PTFE of a different grade, chemically modified PTFE, and combinations thereof.
36 . The PTFE composite tube of claim 23 , wherein the second polymer is selected from the group consisting of polyaryletherketone (PAEK), modified polyaryletherketone (modified PAEK), polyetheretherketone (PEEK), modified polyetheretherketone (modified PEEK), polyimide (PI), ultra high molecular weight polyethylene (UHMWPE), fluorinated ethylene propylene (FEP), perfluoroalkoxy alkane (PFA), and combinations or copolymers of any two or more thereof.
37 . The PTFE composite tube of claim 23 , wherein the PTFE composite tube has a wall thickness of less than about 0.1 mm.
38 . The PTFE composite tube of claim 23 , wherein the comparable PTFE tube is an unfilled PTFE tube.
39 . The PTFE composite tube of claim 23 , wherein the comparable PTFE tube is a virgin PTFE tube.
40 . A medical device comprising the PTFE composite tube of claim 22 .
41 . The medical device of claim 40 , wherein the medical device is a catheter.
42 . A PTFE composite tube comprising PTFE and a second polymer,
wherein the second polymer is present in a concentration of less than about 50% by weight of the PTFE composite tube, and
wherein the PTFE composite tube exhibits one or both of:
a lower storage modulus as compared to a comparable PTFE tube at temperatures from 0° C. to about 100° C., the comparable PTFE tube not comprising the second polymer; and
a reduced change in storage modulus from about 20° C. to about 40° C. as compared to the comparable PTFE tube.
43 . The PTFE composite tube of claim 42 , wherein the PTFE composite tube exhibits a storage modulus of about 15×10 8 Pa or less at temperatures from about 15° C. to about 100° C. and a decrease in storage modulus of about 7.5×10 8 Pa or less from about 20° C. to about 40° C.
44 . A medical device comprising:
a PTFE composite tube, the PTFE composite tube comprising:
PTFE and a second polymer, the second polymer concentration being less than about 50% by weight of the PTFE composite tube, the PTFE composite tube exhibiting one or both of:
a lower storage modulus as compared to a comparable PTFE tube at temperatures from 0° C. to about 100° C., the comparable PTFE tube not comprising the second polymer; and
a reduced change in storage modulus from about 20° C. to about 40° C. as compared to a comparable PTFE tube, the comparable PTFE tube not comprising the second polymer.