BREATHABLE AND MICROPOROUS THIN THERMOPLASTIC FILM
Breathable, thermoplastic films, laminates, and methods of making films having a basis weight less than or equal to 15 gsm and a water vapor transmission rate of at least about 500 grams H 2 O/24-hour/m 2 , wherein the film has a ratio of the MD load at break to the CD load at break of less than about 10, and at least one of a machine-direction notched Elmendorf tear strength of at least about 5 g or a machine-direction notched trapezoidal tear strength of at least about 15 g.
1 . A method of making a thermoplastic film product is provided, comprising
extruding a molten web comprising a thermoplastic polymer from an extruder onto a first chill roller, said first chill roller operating at a peripheral velocity V1 and at a temperature T1, which is below the melting point of the thermoplastic polymer and which cools said molten web to form a film;
advancing the film to a first stretching roller which operates at a peripheral velocity V2 which is greater than the peripheral velocity V1, and at a temperature T2;
advancing the film to a first machine direction orientation section comprising at least one heated roller having a temperature T3 and a second stretching roller; and
stretching the film in the first machine direction orientation section in the machine direction to produce a film having limited machine direction orientation and a ratio of the MD load at break to a CD load at break of less than about 10.