Microwave assisted synthesis of greenly synthesized magnetic hydrochar nanocomposite obtained from desert date seeds
A method for forming a magnetic hydrochar nanocomposite includes the step of adding basically treated desert date seeds into a vessel containing phosphoric acid and mixing the basically treated desert date seeds with the phosphoric acid to form a mixture. The mixture is transferred to a microwave and heated to 150° C. The mixture is held at this temperature for one hour to form a hydrochar. The magnetic hydrochar nanocomposite is further formed by dissolving ferrous sulphate and ferric chloride to form magnetic nanoparticles. The magnetic nanoparticles are mixed with the hydrochar, then date fruit extract is mixed with the magnetic nanoparticles and hydrochar mixture to form a resultant mixture. The pH of the resultant mixture is raised to 9-11 by adding sodium hydroxide to form a basic resultant mixture. The basic resultant mixture is heated in a microwave to 150° C. for 30 minutes to form the magnetic hydrochar nanocomposite.
1. A method for forming a magnetic hydrochar nanocomposite comprising:
adding basically treated desert date seeds into a vessel containing phosphoric acid and mixing the basically treated desert date seeds with the phosphoric acid to form a mixture;
transferring the mixture to a microwave and heating the mixture to about 150° C. at a rate of about 10° C./minute;
holding the temperature of the mixture at about 150° C. for about one hour to form a hydrochar;
dissolving ferrous sulphate and ferric chloride in an about 1:2 weight ratio in deionized water to form magnetic nanoparticles;
mixing the magnetic nanoparticles with the hydrochar to form a magnetic nanoparticles and hydrochar mixture;
mixing date fruit extract with the magnetic nanoparticles and hydrochar mixture to form a resultant mixture;
raising a pH of the resultant mixture to about 9 to about 11 by adding 1M sodium hydroxide to form a basic resultant mixture; and
heating the basic resultant mixture in a microwave to about 150° C. for about 30 minutes to form the magnetic hydrochar nanocomposite.
2. The method of forming the magnetic hydrochar nanocomposite according to claim 1 , wherein the magnetic hydrochar is further purified by washing with distilled water, applying an external magnetic field, and drying at about 40° C.
3. The method of forming the magnetic hydrochar nanocomposite according to claim 1 , wherein the basically treated desert date seeds are formed by a method comprising the steps of:
harvesting the desert date seeds;
washing the harvested desert date seeds to form washed desert date seeds;
drying the washed desert date seeds at about 40° C. to form dried desert date seeds;
crushing the dried desert date seeds to form crushed desert date seeds;
passing the crushed desert date seeds through a sieve to obtain homogeneous desert date seeds;
mixing the homogeneous desert date seeds with 0.1 M potassium hydroxide and heating at about 70° C. for about three hours to form the basically treated desert date seeds.
4. The method of forming the magnetic hydrochar nanocomposite according to claim 1 , wherein the phosphoric acid is about 50% by weight phosphoric acid.
5. A magnetic hydrochar nanocomposite formed by the method according to claim 1 .