Manufacturing of polyethylene thin films for high-altitude balloons
Aspects of the disclosure relate to manufacturing a balloon envelope for use in a stratospheric balloon system. For instance, a stream of polyethylene mixture is extruded through an extruder in order to orient molecules of polymer chains of polyethylene and to provide an oriented film. The oriented film is passed through an electron beam and thereby crosslinking the polymer chains to provide a cross-linked film. The cross-linked film is heat sealed to form the balloon envelope.
1 . A balloon envelope for use in a stratospheric balloon, the balloon envelope comprising:
a plurality of gores included in the balloon envelope;
a plurality of tendon arranged at a centerline of one or more of the plurality of gores;
the balloon envelope including a cross-linked film comprising an extruded polyethylene mixture having oriented molecules and crosslinked polymer chains, wherein the balloon envelope is formed by a process of:
heat bonding the cross-linked film to form the plurality of gores; and
bonding each of the plurality of tendons to each of a respective one or more of the plurality of gores,
wherein crystallinity of the balloon envelope is greater than 50% after the process, and,
wherein TD tensile strain is less than 2 mm/mm for a tensile stress of 150 MPa at −60° C. with a 50 mm/min pull rate.
2 . The balloon envelope of claim 1 wherein the process of forming the balloon envelope includes reheating the cross-linked film into molten state.
3 . The balloon envelope of claim 1 wherein a MD tensile strain is less than 2 mm/mm for a tensile stress of 150 MPa at −60° C. with a 50 mm/min pull rate.
4 . The balloon envelope of claim 1 , wherein optical clarity of the balloon envelope is 95% or greater.
5 . The balloon envelope of claim 1 , wherein MD tensile strain is less than 2 mm/mm for a tensile stress of 100 MPa at 23° C. with a 50 mm/min pull rate.
6 . The balloon envelope of claim 1 , wherein ID tensile strain is less than 2 mm/mm for a tensile stress of 140 MPa at −40 C with a 50 mm/min pull rate.
7 . The balloon envelope of claim 1 , wherein MD tensile strain is less than 2 mm/mm for a tensile stress of 140 MPa at −40° C. with a 50 mm/min pull rate.
8 . The balloon envelope of claim 1 , wherein high-rate elongation at −80° C. for TD is greater than 20%.
9 . The balloon envelope of claim 1 , wherein thermal emissivity is less than 0.03 at 193K.
10 . The balloon envelope of claim 1 , wherein thermal emissivity is less than 0.04 at 233K.
11 . The balloon envelope of claim 1 , wherein a thickness of the cross-linked film of the balloon envelope less than 1.5 mil and a strength to weight ratio of the balloon envelope is greater than 1 MPa/(dt*g/cm3).
12 . A balloon envelope for use in a stratospheric balloon, the balloon envelope comprising:
a plurality of gores; and
a plurality of tendons, each tendon of the plurality of tendons arranged at a respective one or more of the plurality of gores;
wherein crystallinity of the balloon envelope is greater than 50%;
and wherein a thickness of the balloon envelope less than 1.5 mil and a strength to weight ratio of the balloon envelope is greater than 1 MPa/(dt*g/cm3).
13 . The balloon envelope of claim 12 , wherein TD tensile strain is less than 2 mm/mm for a tensile stress of 100 MPa at 23 C with a 50 mm/min pull rate.
14 . The balloon envelope of claim 12 , wherein MD tensile strain is less than 2 mm/mm for a tensile stress of 100 MPa at 23 C with a 50 mm/min pull rate.
15 . A method of manufacturing a balloon envelope for use in a stratospheric balloon, the method comprising:
extruding a stream of polyethylene mixture through to orient molecules of polymer chains of polyethylene and provide an oriented film;
crosslinking the polymer chains by passing the oriented film through an electron beam to produce an oriented cross-linked film;
heat bonding the cross-linked film to form a plurality of gores,
wherein crystallinity of the balloon envelope is greater than 50%, and
wherein a thickness of the cross-linked film of the balloon envelope less than 1.5 mil and a strength to weight ratio of the balloon envelope is greater than 1 MPa/(dt*g/cm3).
16 . The balloon envelope of claim 15 including bonding each of a plurality of tendons to each of a respective one or more of the plurality of gores.