METHOD FOR MANUFACTURING A BERYLLIUM-BASED ARTICLE
Methods for manufacturing a beryllium-based article object comprising beryllium by depositing layers of beryllium. An element is added to the beryllium that dissolved to form a secondary phase to limit columnar grain. Grain refinement allows the beryllium article to have beneficial properties in terms of strength and durability.
1 . A method of manufacturing a beryllium-based article, the method comprising:
adding an element to beryllium powder;
depositing a layer comprising the beryllium powder on a surface;
applying energy to at least a portion of the layer to form molten beryllium, wherein at least a portion of the element is dissolved in the molten beryllium;
solidifying the molten beryllium to form a secondary phase from the dissolved element; and
repeating the depositing/applying/solidifying steps for successive layers to form the beryllium-based article.
2 . The method of claim 1 , wherein the element comprises aluminum, silicon or silver.
3 . The method of claim 1 , wherein the element is totally dissolved in the molten beryllium.
4 . The method of claim 1 , wherein the secondary phase is dispersed between grains of beryllium.
5 . The method of claim 4 , wherein the grains of beryllium has an average grain size from 1 to 80 microns.
6 . The method of claim 1 , wherein the element is added to the beryllium powder by blending, atomization, mechanical alloying, or resonant mixing.
7 . The method of claim 1 , wherein 0.1 to 25% by weight of the element is added to beryllium.
8 . The method of claim 1 , wherein 0.1 to 10% by weight of the element is added to beryllium.
9 . The method of claim 1 , wherein an electron beam or laser is used to apply energy to at least a portion of the layer.
10 . The method of claim 1 , further comprising depositing the layer in a reducing atmosphere.
11 . The method of claim 10 , wherein the reducing atmosphere has a volume concentration of 10% by volume or less of oxygen or other oxidizing agents.
12 . The method of claim 1 , wherein the beryllium powder have a D50 average size from 10 to 50 microns.
13 . A method of manufacturing a beryllium-based article, the method comprising:
adding an element and a nucleant to beryllium powder;
depositing a layer comprising the beryllium powder on a surface;
applying energy to at least a portion of the layer to form molten beryllium, wherein at least a portion of the element is dissolved in the molten beryllium;
solidifying the molten beryllium, wherein the beryllium has an average grain size from 1 to 80 microns; and
repeating the depositing/applying/solidifying steps for successive layers to form the beryllium-based article.
14 . The method of claim 13 , wherein the nucleant comprises beryllium titanium, beryllium chromium, iron beryllium, beryllium zirconium, tantalum beryllide, beryllium molybdenum, niobium beryllium, beryllium tungsten, beryllium strontium, and/or beryllium hafnium.
15 . The method of claim 13 , wherein the beryllium powder comprises from 0 to 40% by weight of the nucleants.
16 . The method of claim 13 , wherein the element comprises aluminum, silicon or silver.
17 . The method of claim 13 , wherein the element is totally dissolved in the molten beryllium.
18 . The method of claim 13 , wherein the secondary phase is dispersed between grains of beryllium.
19 . The method of claim 13 , wherein 0.1 to 25% by weight of the element is added to beryllium.
20 . The method of claim 13 , wherein 0.1 to 10% by weight of the element is added to beryllium.