POLYMER REINFORCED GLASS MAT WITH ENHANCED NAIL SHANK SHEAR RESISTANCE, SHINGLES INCLUDING THE SAME, AND METHODS OF MANUFACTURING THE SAME
Some embodiments of the present disclosure relate to an article comprising a reinforced glass mat. In some embodiments, the reinforced glass mat includes a glass mat and a reinforcement material. In some embodiments, the glass mat includes a web of glass fibers. In some embodiments, the reinforcement material is embedded into the web of glass fibers of the glass mat. In some embodiments, the reinforced glass mat includes a sufficient amount of the reinforcement material, so as to result in a nail shank shear resistance of 13 lbs to 17 lbs, when the article is tested according to ASTM 1761 at 140° F. Methods of making the article, specific embodiments of the reinforcement material in the form of a polymeric binder, and methods of forming a roofing shingle from the article are also disclosed.
1 .- 19 . (canceled)
20 . A roofing material, comprising:
a polymer reinforced glass mat,
wherein the polymer reinforced glass mat comprises:
a glass mat,
wherein the glass mat comprises a web of glass fibers,
wherein the glass mat comprises interstitial voids, and
a polymeric binder,
wherein the polymeric binder is embedded into the web of glass fibers,
wherein a weight of the polymeric binder embedded in the web of glass fibers is 0.5 to 2.5 lbs per square inch.
21 . The roofing material of claim 20 , further comprising an asphalt coating, wherein the asphalt coating surrounds the polymer reinforced glass mat.
22 . The roofing material of claim 21 , further comprising a plurality of granules, wherein the plurality of granules is embedded in the asphalt coating.
23 . The roofing material of claim 20 , wherein the roofing material is a roofing shingle.
24 . The roofing material of claim 20 , wherein the polymeric binder comprises atactic polypropylene (APP).
25 . The roofing material of claim 20 , wherein the polymeric binder comprises at least one polymer having a melting temperature of 120° C. to 200° C.
26 . The roofing material of claim 20 , wherein the polymeric binder comprises at least one polymer having a melt flow index of 20 to 60 measured according to ASTM D1238.
27 . The roofing material of claim 20 , wherein the polymeric binder comprises at least one polymer having a vicat softening temperature of 50° C. to 90° C. measured according to ASTM D1525.
28 . A roofing material, comprising:
a polymer reinforced glass mat,
wherein the polymer reinforced glass mat comprises:
a glass mat,
wherein the glass mat comprises a web of glass fibers,
wherein the glass mat comprises interstitial voids, and
a polymeric binder,
wherein the polymeric binder is embedded into the web of glass fibers,
wherein a weight of the polymeric binder embedded in the web of glass fibers is 0.5 to 2.5 lbs per square inch; and
an asphalt coating on the polymer reinforced glass mat.
29 . The roofing material of claim 28 , further comprising a plurality of granules, wherein the plurality of granules is embedded in the asphalt coating.
30 . The roofing material of claim 28 , wherein the roofing material is a roofing shingle.
31 . The roofing material of claim 28 , wherein the polymeric binder comprises atactic polypropylene (APP).
32 . The roofing material of claim 28 , wherein the polymeric binder comprises at least one polymer having a melting temperature of 120° C. to 200° C.
33 . The roofing material of claim 28 , wherein the polymeric binder comprises at least one polymer having a melt flow index of 20 to 60 measured according to ASTM D1238.
34 . A method, comprising:
obtaining a glass mat,
wherein the glass mat comprises a web of glass fibers;
wherein the glass mat comprises interstitial voids;
obtaining a polymeric binder;
embedding the polymeric binder into the web of glass fibers, thereby to form a polymer reinforced glass mat,
wherein a weight of the polymeric binder embedded in the web of glass fibers is 0.5 to 2.5 lbs per square inch.
35 . The method of claim 34 , further comprising:
obtaining an asphalt coating; and
surrounding the polymer reinforced glass mat with the asphalt coating.
36 . The method of claim 35 , further comprising:
obtaining a plurality of granules; and
embedding the plurality of granules in the asphalt coating.
37 . The method of claim 34 , wherein the polymeric binder comprises atactic polypropylene (APP).
38 . The method of claim 34 , wherein the polymeric binder comprises at least one polymer having a melting temperature of 120° C. to 200° C.
39 . The method of claim 35 , wherein the polymeric binder comprises at least one polymer having a vicat softening temperature of 50° C. to 90° C. measured according to ASTM D1525.