ABSORBENT ARTICLE BARRIER LAYER
An absorbent article comprising a liquid permeable cover layer, an impervious barrier layer and an absorbent core between the cover layer and the barrier layer, wherein the barrier layer is impervious and biodegradable and comprises a kraft paper layer and a continuous resin coating; wherein the continuous resin coating is on the surface of the barrier layer disposed toward the absorbent core, and the continuous resin coating weight is from 10 to 18 g/m 2 , and the continuous resin coating is an acrylic copolymer.
1 . Absorbent article comprising a liquid permeable cover layer, an impervious barrier layer and an absorbent core between the cover layer and the barrier layer, wherein the barrier layer is impervious and biodegradable and comprises a kraft paper layer and a continuous resin coating,
wherein the continuous resin coating is on the surface of the barrier layer disposed toward the absorbent core, and
the continuous resin coating weight is from 10 to 18 g/m 2 , preferably 12 to 15 g/m 2 , and the continuous resin coating is an acrylic copolymer.
2 . Absorbent article according to claim 1 , wherein the kraft paper layer comprises 80% to 50% of cellulosic fibers having an average length greater than about 2 mm.
3 . Absorbent article according to claim 1 , wherein the kraft paper layer has a basis weight from 28 to 32 g/m 2 .
4 . Absorbent article according to claim 1 , wherein the kraft paper layer has a thickness from 45 to 60 μm.
5 . Absorbent article according to claim 1 , wherein the kraft paper layer has a transversal tear resistance greater than 25 gf.
6 . Absorbent article according to claim 1 , wherein the kraft paper layer does not comprises a polyethylene coating layer, a polylactic acid coating layer or a plant-based protein coating layer.
7 . Absorbent article according to claim 1 , wherein the kraft paper layer is unbleached.
8 . Absorbent article according to claim 1 , wherein there is no construction adhesive between the absorbent core and the continuous resin coating of the barrier layer.
9 . Absorbent article according to claim 1 , wherein a transfer layer is present between the cover layer and the absorbent core.
10 . Absorbent article according to claim 1 , wherein the liquid permeable cover layer is manufactured from at least 70% of biodegradable fibers or compostable fibers, such as natural fibers.
11 . Absorbent article according to claim 1 , wherein there is no positioning adhesive on the face of the kraft paper layer opposite to the continuous resin coating.
12 . Liquid impervious barrier layer comprising a kraft paper layer and a continuous resin coating; wherein the continuous resin coating weight is from 10 to 18 g/m 2 , preferably 12 to 15 g/m 2 , and the continuous resin coating is an acrylic copolymer, wherein the thickness of the barrier layer ranges from 40 μm to 80 μm.
13 . Process for the construction of an absorbent article comprising the following steps:
Applying a continuous resin coating on a kraft paper layer, to obtain a resin coated kraft paper,
Drying the resin coated kraft paper in an oven to obtain a barrier layer,
Assembling the barrier layer with at least a liquid permeable cover layer and optionally an absorbent core between the barrier layer and the cover layer to obtain an absorbent article,
wherein the continuous resin coating weight is from 10 to 18 g/m 2 , preferably 12 to 15 g/m 2 , and the continuous resin coating is an acrylic copolymer.
14 . Process for the construction of an absorbent article according to claim 13 , wherein the application step of the continuous resin coating on the kraft paper layer is done in at least two distinct steps.
15 . Use of a liquid impervious barrier layer comprising a kraft paper layer and a continuous resin coating, for the construction of an absorbent article such as a feminine hygiene product, for example a napkin, a panty liner;
wherein the continuous resin coating weight is from 10 to 18 g/m 2 , preferably 12 to 15 g/m 2 , and the continuous resin coating is an acrylic copolymer, wherein the thickness of the barrier layer ranges from about 40 μm to about 80 μm.