R-T-B MAGNET AND PREPARATION METHOD THEREFOR

Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US None
App. No.
18/548,206
Abstract

Disclosed are an R-T-B magnet and a preparation method therefor. The R-T-B magnet comprises the following components: R≥29 wt. %, R being a rare earth element and containing Nd, wherein Nd is ≥22 wt. %; 0.2-0.75 wt. % of Ti+Nb; 0.05-0.45 wt. % of Cu; 0.955-1.15 wt. % of B; and 58-69 wt. % of Fe, wherein wt. % is the ratio of the mass of each component to the total mass of the components; and the mass ratio of Ti to Nb is (1-5):1. According to the present invention, the matching relationship among the added elements in the R-T-B magnet is further optimized, and an R-T-B magnet with better magnetic properties such as relatively high residual magnetization, coercivity, and squareness can be prepared by using the formula.

Claims (88)

1 . A R-T-B magnet, characterized by comprising the following components of:

≥29 wt % of R, said R is a rare earth element comprising Nd, wherein the content of Nd in all components is ≥22 wt %;

0.2-0.75 wt % of Ti+Nb;

0.05-0.45 wt % of Cu;

0.955-1.15 wt % of B; and

58-69 wt % of Fe, wherein

wt % is a ratio of the mass of respective component to the total mass of all components;

and the mass ratio of said Ti to said Nb is (1-5):1.

2 . The R-T-B magnet according to claim 1 , characterized in that:

the content of R is 30-32 wt %, such as 30 wt %, 30.6 wt %, 30.7 wt % or 31.2 wt %; and/or

the content of Nd is 25-31 wt %, such as 28.5 wt %, 28.7 wt %, 29.1 wt %, 29.2 wt %, 29.3 wt %, 29.5 wt %, 29.7 wt % or 30.4 wt %; and/or

the R comprises Pr and/or RH, wherein the RH is a heavy rare earth element;

wherein, the content of the Pr is preferably 0.3 wt % or less, such as 0.2 wt %, wherein wt % is the mass percentage of Pr in the total mass of all components;

wherein, the content of RH is preferably 2.5 wt % or less, such as 0.5 wt %, 0.8 wt %, 1 wt %, 1.1 wt %, 1.4 wt %, 2 wt %, 2.2 wt %, wherein wt % is the mass percentage of RH in the total mass of all components;

wherein, the RH preferably comprises Tb and/or Dy;

when the RH comprises Tb, the content of Tb is preferably 0.5-1.4 wt %, such as 0.5 wt %, 0.6 wt %, 0.8 wt %, 1 wt %, 1.1 wt % or 1.4 wt %, wherein wt % is the mass percentage of Tb in the total mass of all components;

when the RH comprises Dy, the content of Dy is preferably 0.5-2 wt %, such as 0.5 wt %, 1 wt %, 1.6 wt % or 2 wt %, wherein wt % is the mass percentage of Dy in the total mass of all components;

wherein the ratio of the atomic percentage of the RH to the atomic percentage of the R is 0.1 or less, such as 0.02, 0.04 or 0.06.

3 . The R-T-B magnet according to claim 1 , characterized in that:

the content of Ti+Nb is 0.22-0.7 wt %, such as 0.22 wt %, 0.28 wt %, 0.35 wt %, 0.38 wt %, 0.45 wt %, 0.58 wt %, 0.59 wt % or 0.7 wt %, preferably 0.25-0.55 wt %; and/or

the mass ratio of Ti to Nb is (1.2-4.8): 1, such as 1.2:1, 1.8:1, 2.5:1, 3.5:1, 3.8:1, 4:1 or 4.8:1, more preferably Ground is (1.5-3.5): 1; and/or

the content of Ti is 0.12-0.56 wt %, such as 0.12 wt %, 0.18 wt %, 0.25 wt %, 0.3 wt %, 0.35 wt %, 0.48 wt % or 0.56 wt %; and/or

the content of Nb is 0.08-0.14 wt %, such as 0.08 wt %, 0.1 wt %, 0.11 wt % or 0.14 wt %.

4 . The R-T-B magnet according to claim 1 , characterized in that:

the content of Cu is 0.06-0.39 wt %, such as 0.06 wt %, 0.15 wt %, 0.31 wt %, 0.34 wt %, 0.35 wt %, 0.36 wt %, 0.38 wt % or 0.39 wt %; and/or

the content of B is 0.98-1.1 wt %, such as 0.99 wt %; and/or

the ratio of the atomic percentage of B to the atomic percentage of R in the R-T-B magnet is 0.38 or more, such as 0.4, 0.41, 0.42, 0.43 or 0.44; and/or

the content of Fe is 65-69 wt %, such as 66.64 wt %, 67.14 wt %, 67.25 wt %, 67.33 wt %, 67.42 wt %, 67.47 wt %, 67.55 wt %, 67.62 wt %, 67.64 wt %, 67.68 wt %, 67.7 wt %, 67.74 wt %, 67.88 wt %, 67.97 wt % or 68.34 wt %; and/or

the R-T-B magnet further comprises Co;

wherein, the content of Co is preferably 1.2 wt % or less, such as 0.5 wt % or 1 wt %, wherein wt % is the mass percentage of Co in the total mass of all components.

5 . The R-T-B magnet according to claim 1 , characterized in that:

the R-T-B magnet comprises a Ti x Nb 1 phase, wherein the X is 3-5; the Ti x Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti x Nb 1 phase to the total area of the main phase particles is 1-2%;

wherein, the ratio of the area of the Ti x Nb 1 phase to the total area of the main phase particles is, for example, 1.3%, 1.4%, 1.5%, 1.6% or 1.7%.

6 . The R-T-B magnet according to claim 1 , characterized in that:

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.39 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.64 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.40%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.38 wt % of Cu, 0.3 wt % of Ti, 0.08 wt % of Nb, 0.99 wt % of B and 67.55 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 4 Nb 1 phase; the Ti 4 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 4 Nb 1 phase to the total area of the main phase particles is 1.40%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.39 wt % of Cu, 0.48 wt % of Ti, 0.11 wt % of Nb, 0.99 wt % of B and 67.33 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 5 Nb 1 phase; the Ti 5 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 5 Nb phase to the total area of the main phase particles is 1.70%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.36 wt % of Cu, 0.56 wt % of Ti, 0.14 wt % of Nb, 0.99 wt % of B and 67.25 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 5 Nb 1 phase; the Ti 5 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 5 Nb 1 phase to the total area of the main phase particles is 1.80%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.39 wt % of Cu, 0.12 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.7 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.3%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.34 wt % of Cu, 0.25 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.62 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.5%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.39 wt % of Cu, 0.35 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.47 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 4 Nb 1 phase; the Ti 4 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 4 Nb 1 phase to the total area of the main phase particles is 1.6%; or

the R-T-B magnet comprises the following components of: Nd 29.3 wt %, Tb 1.4 wt %, Cu 0.31 wt %, Ti 0.48 wt %, Nb 0.1 wt %, B 0.99 wt % and Fe 67.42 wt %, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 5 Nb 1 phase; the Ti 5 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 5 Nb 1 phase to the total area of the main phase particles is 1.5%; or

the R-T-B magnet comprises the following components of: 29.5 wt % of Nd, 1.1 wt % of Tb, 0.39 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.74 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.4%; or

the R-T-B magnet comprises the following components of: 30.4 wt % of Nd, 0.8 wt % of Tb, 0.39 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.14 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.5%; or

the R-T-B magnet comprises the following components of: 29.5 wt % of Nd, 0.5 wt % of Tb, 0.39 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 68.34 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.3%; or

the R-T-B magnet comprises the following components of: 28.7 wt % of Nd, 2 wt % of Dy, 0.39 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.64 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.4%; or

the R-T-B magnet comprises the following components of: 28.5 wt % of Nd, 0.6 wt % of Tb, 1.6 wt % of Dy, 0.39 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.64 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.5%; or

the R-T-B magnet comprises the following components of: 29.7 wt % of Nd, 1 wt % of Dy, 0.39 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.64 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.4%; or

the R-T-B magnet comprises the following components of: 29.2 wt % of Nd, 1 wt % of Tb, 0.5 wt % of Dy, 0.39 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.64 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.4%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.39 wt % of Cu, 0.5 wt %, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.14 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.5%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.39 wt % of Cu, 1 wt %, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 66.64 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.5%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.35 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.68 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.5%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.15 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.88 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.5%; or

the R-T-B magnet comprises the following components of: 29.3 wt % of Nd, 1.4 wt % of Tb, 0.06 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.97 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.3%; or

the R-T-B magnet comprises the following components of: 29.1 wt % of Nd, 0.2 wt % of Pr, 1.4 wt % of Tb, 0.39 wt % of Cu, 0.18 wt % of Ti, 0.1 wt % of Nb, 0.99 wt % of B and 67.64 wt % of Fe, wherein wt % is the ratio of the mass of respective component to the total mass of all components; the R-T-B magnet comprises a Ti 3 Nb 1 phase; the Ti 3 Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti 3 Nb 1 phase to the total area of the main phase particles is 1.5%.

7 . A preparation method of a R-T-B magnet, characterized by comprising the steps of subjecting a raw mixture comprising the respective components for the R-T-B magnet according to claim 1 to an aging treatment and then a cooling treatment, wherein:

the aging treatment comprises a primary aging treatment and a secondary aging treatment; and

the cooling treatment has a rate of 20° C./min or more.

8 . The preparation method of the R-T-B magnet according to claim 7 , characterized in that:

the temperature for the primary aging treatment is 860-920° C., such as 900° C.; and/or

the time for the primary aging treatment is 2.5-4 h, such as 3 h; and/or

the temperature for the secondary aging treatment is 460-530° C., such as 510° C.; and/or

the time for the secondary aging treatment is 2.5-4 h, such as 3 h; and/or

the cooling treatment has a rate of 20-40° C./min.

9 . The preparation method of the R-T-B magnet according to claim 7 , characterized in that the preparation method further comprises the steps of smelting, casting, hydrogen decrepitation, pulverization, magnetic field shaping and sintering treatment before the aging treatment,

wherein, the vacuum degree for the smelting is, for example, 5×10 −2 Pa;

wherein, the temperature for the melting is, for example, 1550° C. or less;

wherein, the temperature for the casting is preferably 1390-1460° C., such as 1450° C.;

wherein, the alloy sheet obtained after the casting has a thickness of preferably 0.25-0.40 mm, such as 0.29 mm;

wherein, the process of the hydrogen decrepitation preferably comprises hydrogen absorption, dehydrogenation, and a cooling treatment in turn, wherein the hydrogen absorption is preferably carried out under a condition of a hydrogen pressure of 0.085 MPa; the dehydrogenation is preferably carried out under the condition of raising the temperature while evacuating, and the temperature for the dehydrogenation is preferably 480-520° C., For example, 500° C.;

wherein, the pulverization is preferably jet mill pulverization;

wherein, the magnetic field shaping is preferably carried out under the protection of a nitrogen atmosphere with a magnetic field strength of 1.8 T or more, such as 1.8-2.5 T;

wherein, the temperature for the sintering treatment is preferably 1000-1100° C., such as 1080° C.;

wherein, the time for the sintering treatment is preferably 4-8 h, such as 6 h; and/or

wherein, when the R-T-B magnet comprises a heavy rare earth element, the preparation method further comprises a grain boundary diffusion treatment after the cooling treatment;

wherein, the temperature for the grain boundary diffusion treatment is preferably 800-900° C., such as 850° C.;

wherein, the time for the grain boundary diffusion is preferably 5-10 h, such as 8 h;

wherein, the method of adding heavy rare earth elements in the R-T-B magnet preferably comprises the steps of adding 0-80% of heavy rare earth elements during the smelting and adding the remaining heavy rare earth elements during the grain boundary diffusion; for example, when the heavy rare earth elements in the R-T-B magnet are Tb with a content of greater than 0.5 wt %, 25-50% of Tb is added during the smelting, and the rest is added during the grain boundary diffusion; or, for example, when the heavy rare earth elements in the R-T-B magnet are Tb and Dy, the Tb is added during smelting, and the Dy is added during the grain boundary diffusion; or for example, when the heavy rare earth elements in the R-T-B magnet are Tb with a content of less than or equal to 0.5 wt %, or when the heavy rare earth elements in the R-T-B magnet are Dy, the heavy rare earth elements in the R-T-B magnet are added during the grain boundary diffusion.

10 . A R-T-B magnet prepared by the preparation method of the R-T-B magnet according to claim 7 .

11 . The R-T-B magnet according to claim 2 , characterized in that:

the R-T-B magnet comprises a Ti x Nb 1 phase, wherein the X is 3-5; the Ti x Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti x Nb 1 phase to the total area of the main phase particles is 1-2%;

wherein, the ratio of the area of the Ti x Nb 1 phase to the total area of the main phase particles is, for example, 1.3%, 1.4%, 1.5%, 1.6% or 1.7%.

12 . The R-T-B magnet according to claim 3 , characterized in that:

the R-T-B magnet comprises a Ti x Nb 1 phase, wherein the X is 3-5; the Ti x Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti x Nb 1 phase to the total area of the main phase particles is 1-2%;

wherein, the ratio of the area of the Ti x Nb 1 phase to the total area of the main phase particles is, for example, 1.3%, 1.4%, 1.5%, 1.6% or 1.7%.

13 . The R-T-B magnet according to claim 4 , characterized in that:

the R-T-B magnet comprises a Ti x Nb 1 phase, wherein the X is 3-5; the Ti x Nb 1 phase is located between a Nd-rich phase and main phase particles; and the ratio of the area of the Ti x Nb 1 phase to the total area of the main phase particles is 1-2%;

wherein, the ratio of the area of the Ti x Nb 1 phase to the total area of the main phase particles is, for example, 1.3%, 1.4%, 1.5%, 1.6% or 1.7%.

Assignments (2)
CHANGE OF NAME Recorded Dec 20, 2023
From: FUJIAN CHANGTING GOLDEN DRAGON RARE-EARTH CO., LTD.
To: FUJIAN GOLDEN DRAGON RARE-EARTH CO., LTD.
Reel/Frame 066124/0473 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Sep 13, 2023
From: MOU, WEIGUO; HUANG, JIAYING
To: FUJIAN CHANGTING GOLDEN DRAGON RARE-EARTH CO., LTD
Reel/Frame 064889/0246 →