BLOW MOLDING COMPOSITIONS BASED ON BRANCHED POLYAMIDES AND USES THEREOF
The present invention relates to a composition for blow-molding or extrusion, in particular blow-molding, comprising by weight: a) from 88 to 99.95%, more particularly from 89 to 99.9%, in particular from 93 to 99.9%, of at least one semicrystalline aliphatic polyamide having a carbon number per nitrogen atom of greater than or equal to 7, more particularly greater than or equal to 8, b) from 0.05% to 10%, more particularly from 0.1% to 9%, in particular from 0.1% to 5% by weight of at least one branching agent chosen from polyepoxides, polyanhydrides, more particularly polymaleic anhydrides and polyepoxides, c) from 0 to 2% of at least one additive, more particularly from 0.1 to 2%, the composition having, after compounding, a melt viscosity of from 10 000 to 300 000 Pa·s, preferably from 15 000 to 220 000 Pa·s, as measured in plane-plane geometry according to standard 6721-10:2015 at a temperature of 250° C., a frequency of 0.292 rad/s and a deformation of 2%, the sum of the constituents a)+b)+c) making 100% by weight.
1 . A composition for blow-molding or extrusion comprising by weight:
a) from 88 to 99.95% of at least one semicrystalline aliphatic polyamide having a carbon number per nitrogen atom of greater than or equal to 7,
b) from 0.05% to 10% by weight of at least one branching agent chosen from polyepoxides, polyanhydrides and polyisocyanates,
c) from 0 to 2% of at least one additive, the composition having, after compounding, a melt viscosity of from 10,000 to 300,000 Pa·s, as measured in plane-plane geometry according to ISO standard 6721-10:2015 at a temperature of 250° C., a frequency of 0.292 rad/s and a deformation of 2%,
the sum of the constituents a)+b)+c) making 100% by weight.
2 . The composition for blow-molding or extrusion as claimed in claim 1 , wherein said compounding is carried out at a temperature of the molten polymer of greater than 280° C., with an average residence time of from 20 seconds to 10 minutes.
3 . The composition for blow-molding or extrusion as claimed in claim 1 , wherein the impact modifiers are excluded from said composition.
4 . The composition for blow-molding or extrusion as claimed in claim 1 , wherein the ratio of the viscosities as measured in plane-plane geometry in the melt state at 0.292 rad·s −1 /292 rad·s −1 is from 10 to 200.
5 . The composition for blow-molding or extrusion as claimed in one claim 1 , wherein said branching agent has an average functionality in terms of epoxy, anhydride or isocyanate functions of from 1.8 to 200.
6 . The composition for blow-molding or extrusion as claimed in one claim 1 , wherein said branching agent has an average equivalent weight in terms of epoxy, anhydride or isocyanate functions of from 100 to 10,000 g/mol.
7 . The composition for blow-molding as claimed in claim 1 , wherein the Rheotens force of the composition after compounding is from 22 mN to 200 mN.
8 . The composition for blow-molding or extrusion as claimed in claim 1 , wherein said semicrystalline aliphatic polyamide is chosen from PA610, PA612, PA 614, PA 10, PA11 and PA12.
9 . A monolayer or multilayer tubular structure configured for the transport, distribution or storage of gasoline, comprising at least one sealing layer comprising a composition as defined in claim 1 .
10 . The monolayer or multilayer tubular structure as claimed in claim 9 , wherein said sealing layer, on first storage of gasoline, has at most 1 g/m2 of insoluble extract and also at most 15 g/m2 of soluble extract being removed by washing of the single-layer or multilayer tubular structure as an overall system, determined for a 20×4×4 cm3 tank having a wall thickness of 2 mm.
11 . The monolayer or multilayer tubular structure as claimed in claim 9 , wherein said structure is a monolayer structure.
12 . The monolayer or multilayer tubular structure as claimed in claim 9 , wherein said structure is a multilayer structure and comprises a barrier layer.
13 . The monolayer or multilayer tubular structure as claimed in claim 12 , wherein said barrier layer is made of EVOH.
14 . A method of using 0.05% to 10% by weight of at least one branching agent chosen from polyepoxides, polyanhydrides, with 88% to 99.95% of at least one semicrystalline aliphatic polyamide having a carbon number per nitrogen atom of greater than or equal to 7, and optionally an additive for the constitution of a composition for blow-molding, as defined in claim 1 , the melt viscosity of which after compounding is from 10,000 to 300,000 Pa·s, as measured in plane-plane geometry at a temperature of 250° C., a frequency of 0.292 rad/s and a deformation of 2%.
15 . A process for preparing a composition for blow-molding or extrusion as defined in claim 1 , comprising a step of compounding said composition.
16 . A process for preparing a monolayer or multilayer tubular structure as defined in claim 9 , comprising a step of blow-molding or extrusion of the composition.
17 . A process for preparing a monolayer or multilayer tubular structure as claimed in claim 16 , comprising a preliminary step of compounding the composition.