The present disclosure provides poly(tetrafluoroethylene) (PTFE) microparticles with a Dv50 of about 20 μm to about 30 μm and a specific surface area (SSA) of at least about 3.0 m 2 /g when measured by a multipoint BET method of ISO 9277. Such PTFE microparticles can be obtained via a method including thermomechanically degrading scrap PTFE in the presence of air and/or oxygen and reducing the particle size of the resultant degraded PTFE.
1 . Microparticles comprising reprocessed poly(tetrafluoroethylene) (PTFE),
wherein the microparticles exhibit a Dv50 of about 20 μm to about 30 μm and an improved specific surface area (SSA) for particles of that size range of at least about 3.0 m 2 /g when measured by a multipoint BET method of ISO 9277.
2 . The microparticles of claim 1 , wherein the microparticles are prepared via thermomechanically degrading reprocessed PTFE in the presence of air and/or oxygen to give degraded PTFE and reducing particle size of the degraded PTFE.
3 . The microparticles of claim 1 , wherein the microparticles consist essentially of the reprocessed poly(tetrafluoroethylene) and modified poly(tetrafluoroethylene) species.
4 . The microparticles of claim 3 , wherein the modified poly(tetrafluoroethylene) species comprise poly(tetrafluoroethylene) modified by one or more of oxygen atoms, additional carbon atoms, and/or additional hydrogen atoms.
5 . The microparticles of claim 1 , wherein the microparticles are prepared via a method that does not comprise irradiation.
6 . The microparticles of claim 2 , wherein the thermomechanical degrading comprises passing the reprocessed PTFE multiple times through equipment designed for thermomechanical degradation.
7 . The microparticles of claim 2 , wherein the reducing particle size comprises passing the degraded PTFE multiple times through equipment designed for particle size reduction.
8 . The microparticles of claim 2 , wherein the thermomechanical degrading is conducted in an extruder.
9 . The microparticles of claim 2 , wherein the thermomechanical degrading is conducted in an internal mixer.
10 . The microparticles of claim 1 , wherein the reprocessed PTFE is in sintered form.
11 . The microparticles of claim 1 , wherein the reprocessed PTFE is in unsintered form.
12 . A product selected from the group consisting of lubricants and pigments, comprising the microparticles of claim 1 .
13 . A method for providing microparticles comprising PTFE, comprising:
providing reprocessed PTFE;
degrading the reprocessed PTFE thermally and mechanically in the presence of air and/or oxygen to give degraded PTFE; and
reducing the particle size of the degraded PTFE by grinding or milling to give the microparticles,
wherein the microparticles exhibit a Dv50 of about 20 μm to about 30 μm and an improved specific surface area (SSA) for particles of that size range of at least about 3.0 m 2 /g when measured by a multipoint BET method of ISO 9277, and
wherein the method does not comprise irradiation.
14 . The method of claim 13 , wherein the microparticles form a line on a plot of SSA versus Dv50 with a slope of at least around −0.05 m 2 /g·μm and a y-intercept of at least around 4.0 m 2 /g.
15 . The method of claim 13 , wherein the reprocessed PTFE is in sintered form.
16 . The method of claim 13 , wherein the reprocessed PTFE is in unsintered form.
17 . The method of claim 13 , wherein the degrading is conducted in an extruder or an internal mixer.
18 . The method of claim 13 , wherein the degrading is conducted in an environment comprising an oxygen: nitrogen ratio of about 0.4 or greater.
19 . The method of claim 13 , further comprising repeating the degrading step two or more times.
20 . The method of claim 13 , further comprising repeating the reducing step two or more times.
21 . The method of claim 13 , further comprising separating a micropowder obtained after the reducing step into fractions according to particle size.
22 . The method of claim 21 , wherein the separating comprises sieving or processing with an air classifier to give the microparticles.
23 . Microparticles obtained by the process of claim 13 .