BIO-BASED SEALING COMPOSITION, WOOD PRODUCT COMPRISING THE SAME AND APPLICATIONS THEREOF
The present disclosure provides a bio-based sealing composition for imparting waterproof performance to a wood substrate, a wood product comprising the composition, and the applications thereof. The sealing composition comprises a paraffin wax, bio-based wax, penetration aid, structural modifier, and optionally a functional additive. As compared with commercial sealing wax compositions, the bio-based sealing composition of the present disclosure shows better waterproof, reduced substrate surface friction, lower volume shrinkage, and superior durability.
1 . A sealing composition, comprising following components based on a total weight of the sealing composition:
15%-55% of one or more paraffin waxes selected from a group consisting of a crude paraffin, semi-refined paraffin, all-refined paraffin, and mixtures thereof;
5%-50% of one or more bio-waxes selected from a group consisting of soy wax, beeswax, candelilla wax, rice bran wax, carnauba wax, and mixtures thereof;
10%-50% of one or more penetration aids selected from a group consisting of paraffin oil, isoparaffin, soybean oil, oleic acid, soft wax, and mixtures thereof; and
0-40% of one or more structural modifiers selected from a group consisting of a microcrystalline wax, petroleum resin, terpene resin, and mixtures thereof.
2 . The composition according to claim 1 , comprising the following components based on the total weight of the sealing composition:
30%-45% of the one or more paraffin waxes selected from the group consisting of the crude paraffin, the semi-refined paraffin, the all-refined paraffin, and the mixtures thereof;
15%-25% of the one or more bio-waxes selected from the group consisting of the soy wax, the beeswax, the candelilla wax, the rice bran wax, the carnauba wax, and the mixtures thereof; and
10%-40% of the one or more penetration aids selected from the group consisting of the paraffin oil, the isoparaffin, the soybean oil, the oleic acid, the soft wax, and the mixtures thereof; and
10%-25% of the one or more structural modifiers selected from the group consisting of the microcrystalline wax, the petroleum resin, the terpene resin, and the mixtures thereof.
3 . The composition according to claim 1 , comprising the following components based on the total weight of the sealing composition:
40%-45% of the one or more paraffin waxes selected from the group consisting of the crude paraffin, the semi-refined paraffin, the all-refined paraffin, and the mixtures thereof;
15%-20% of the one or more bio-waxes selected from the group consisting of the soy wax, the beeswax, the candelilla wax, the rice bran wax, the carnauba wax, and the mixtures thereof; and
25%-30% of the one or more penetration aids selected from the group consisting of the paraffin oil, the isoparaffin, the soybean oil, the oleic acid, the soft wax, and the mixtures thereof; and
10%-15% of the one or more structural modifiers selected from the group consisting of the microcrystalline wax, the petroleum resin, the terpene resin, and the mixtures thereof.
4 . The composition according to claim 1 , wherein the paraffin wax has a melting point from 50° C. to 65° C., and the bio-wax has a melting point from 55° C. to 85° C.
5 . The composition according to claim 1 , wherein the bio-wax is the soy wax and/or the beeswax.
6 . The composition according to claim 1 , wherein the penetration aid has a viscosity from 5 cSt to 10000 cSt and a boiling point of over 100° C.
7 . The composition according to claim 1 , wherein the structural modifier has a melting point from 50° C. to 105° C.
8 . The composition according to claim 1 , wherein, the structural modifier is a mixture of the microcrystalline wax and the terpene resin, or a mixture of the microcrystalline wax and the petroleum resin.
9 . The composition according to claim 1 , further comprising one or more functional additives.
10 . The composition according to claim 1 , wherein the sealing composition is in a solid state at room temperature, and has a melting point from 40° C. to 80° C.
11 . The composition according to claim 1 , wherein the sealing composition is prepared by melting the paraffin, the bio-wax, the penetration aid, the structural modifier, and optionally the functional additives at a temperature from 60° C. to 150° C. to a liquid state.
12 . A wood product comprising a wood substrate and a wax layer formed from the sealing composition according to claim 1 on at least a part of a surface of the wood substrate.
13 . The wood product of claim 12 , wherein the wax layer is formed on an edge surface of the wood substrate.
14 . The wood product of claim 12 , wherein the wax layer is formed on a tongue-and-groove surface of the wood substrate.
15 . The wood product of claim 12 , wherein the sealing composition further penetrates the wood substrate.
16 . The wood product of claim 12 , wherein the wood product is trim, furniture, subflooring, wall coverings or wood floor.
17 . A method for treating a wood substrate, comprising a step of applying the sealing composition according to claim 1 to at least a part of a surface of the wood substrate to form a wax layer.
18 . The method according to claim 17 , wherein the sealing composition is applied to an edge surface of the wood substrate to form the wax layer.
19 . The method according to claim 17 , wherein the sealing composition is applied to a tongue-and-groove surface of the wood substrate to form the wax layer.